High-permeability epoxy waterproof paint

A waterproof coating, high permeability technology, applied in epoxy resin coatings, coatings and other directions, can solve the problems of waterproof layer damage, easy aging, unstable epoxy resin permeability, etc., to achieve strong waterproof performance and strong permeability Effect

Inactive Publication Date: 2016-02-03
HEERON TECH (WUHAN) NEW MATERIALS CO LTD
View PDF3 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The penetration performance of epoxy resin using this series of curing agents is unstable, and the initial penetration is good during construction, but after the solvent evaporates, it is prone to defects such as low strength and easy delamination
At the same time, these curing agents themselves have poor toughness after curing with the epoxy resin, and the flexibility of the product can only be adjusted by adding a toughening agent. Once the performance of the toughening agent is shifted or the addition is uncomfortable, the product will be prone to aging and brittle rebound after curing. , resulting in damage to the waterproof layer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0058] A high-permeability modified epoxy waterproof coating. The waterproof coating is composed of liquid A and liquid B. The coating is formed by mixing liquid A and liquid B in proportion and stirring in a stirring tank at room temperature for 10 to 20 minutes.

[0059] in

[0060] A component: epoxy resin E5150 parts by mass

[0061] 15 parts by mass of dimethyl glycidyl ether

[0062] LD41020 parts by mass

[0063] 30 parts of xylene, 60 parts of n-butanol and C 9 20 parts by mass of a mixture of 10 parts

[0064] Component B: polyetheramine curing agent D200010 parts by mass

[0065]Polyetheramine curing agent D23015 parts by mass

[0066] 30 parts of xylene, 60 parts of n-butanol and C 9 20 parts by mass of a mixture of 10 parts

[0067] Accelerator K542 parts by mass

[0068] NP50 parts by mass.

Embodiment 2

[0070] A high-permeability modified epoxy waterproof coating. The waterproof coating is composed of liquid A and liquid B. The coating is formed by mixing liquid A and liquid B in proportion and stirring in a stirring tank at room temperature for 10 to 20 minutes.

[0071] in

[0072] A component: epoxy resin E5175 mass parts

[0073] 5 parts by mass of dimethyl glycidyl ether

[0074] LD41010 parts by mass

[0075] 30 parts of xylene, 60 parts of n-butanol and C 9 20 parts by mass of a mixture of 10 parts

[0076] B component: polyether amine curing agent D200020 parts by mass

[0077] Polyetheramine curing agent D23015 parts by mass

[0078] 30 parts of xylene, 60 parts of n-butanol and C 9 20 parts by mass of a mixture of 10 parts

[0079] Accelerator K545 parts by mass.

[0080] NP40 parts by mass

Embodiment 3

[0082] A high-permeability modified epoxy waterproof coating. The waterproof coating is composed of liquid A and liquid B. The coating is formed by mixing liquid A and liquid B in proportion and stirring in a stirring tank at room temperature for 10 to 20 minutes.

[0083] in

[0084] A component: epoxy resin E5160 mass parts

[0085] 10 parts by mass of dimethyl glycidyl ether

[0086] LD41015 parts by mass

[0087] 30 parts of xylene, 60 parts of n-butanol and C 9 10 parts of mixture 40 parts by mass

[0088] Component B: polyetheramine curing agent D200015 parts by mass

[0089] Polyetheramine curing agent D23015 parts by mass

[0090] 30 parts of xylene, 60 parts of n-butanol and C 9 30 parts by mass of a mixture of 10 parts

[0091] Accelerator K543 parts by mass

[0092] NP55 parts by mass.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to high-permeability epoxy waterproof paint. The high-permeability epoxy waterproof paint is prepared from modified epoxy resin and a part of high-permeability materials. The paint is prepared from a component A, and a component B. The component A is prepared from 50-75 parts of bisphenol A epoxy resin, 5-15 parts of reactive diluents, 10-20 parts of epoxy resin active flexibilizer and 20-40 parts of benzene diluents. The mixed diamine curing agent is prepared from 15-20 parts of polyether amine D 2000 and 10-15 parts of D 230. The component B is prepared from the mixed diamine curing agent, 50-70 parts of diluents, 2-5 parts of accelerant and 20-30 parts of benzene diluents. The solution A and a solution B are mixed to obtain the paint. The paint has high permeability and flexibility and can permeate and repair cracks and pores in surfaces of concrete, and a sealed whole waterproof structural layer is formed on the surfaces of concrete. Even when surface film forming matter is damaged, the surfaces of the concrete are closed by the paint to form the compact waterproof structure layers, and therefore the permanent waterproof effect is achieved.

Description

technical field [0001] The invention relates to a high-permeability epoxy resin waterproof coating, which belongs to the technical field of coating preparation. Background technique [0002] For concrete structure buildings and road bridges, concrete and steel bars are the most ideal combination. Although steel is a substance that is easily corroded, if the surrounding environment can remain stable and alkaline, steel will not be corroded. Once chloride ions, water, and acid ions penetrate into the concrete, the pH of the concrete will drop from 11 to below 7, and the steel bars in the concrete structure will begin to corrode. Waterproof performance is one of the most important factors affecting the life of concrete structures. [0003] Traditional waterproof materials, such as emulsified asphalt, polyurethane, etc., all form a waterproof film on the surface of the concrete structure, which can play a good waterproof role on the concrete surface. Due to stress, the waterp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D7/12
CPCC08K5/01C08K5/05C09D5/00C08G59/226C08G59/504C09D163/00C09D7/20
Inventor 严文郑四龙严木林徐立
Owner HEERON TECH (WUHAN) NEW MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products