Energy-containing fluorescent material rare earth-glutamic acid-imidazole single crystal complex and preparation method thereof
A technology of fluorescent materials and glutamic acid, which is applied in the fields of luminescent materials, compounds containing Group 3/13 elements of the periodic table, chemical instruments and methods, etc., to achieve the effects of simple process, scientific ligand selection, and high energy density
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0028] Preparation of neodymium perchlorate solution: Weigh 10.00g of neodymium oxide, add 45mL of perchloric acid with a volume ratio of 1:1, filter out insoluble matter, set the volume to 250mL, and calibrate its concentration with a calibrated EDTA standard solution; The concentration of neodymium acid solution is 0.5M.
[0029] Preparation of the complex: react the above neodymium perchlorate solution at 60°C for 5h, then add glutamic acid at a molar ratio of neodymium:glutamic acid=1:4, adjust the pH value to 5 with alkaline solution, and then react at 60°C for 3h , and then add imidazole, the molar ratio of neodymium:imidazole=1:1, after reacting at 60°C for 3 hours, crystals were obtained after standing for a period of time.
[0030] Determination of the complex: Take the single crystal of the complex obtained above, and use the following method to determine its unit cell. The crystallographic data of the complex are collected with a BrukerSmart-1000CCD single crystal d...
Embodiment 2
[0034] Substitute samarium oxide for neodymium oxide, and other steps are the same as in Example 1. The crystallographic data of the complexes are shown in Table 1 and Table 2. Its crystal is monoclinic system, the space group is C 2 / c , the cell parameters are Z=4.
[0035] Fluorescence spectrum: as Figure 5 As shown, the crystal can produce relatively strong fluorescence at about 387nm.
Embodiment 3
[0037] Lanthanum oxide, cerium oxide, praseodymium oxide, holmium oxide, europium oxide, erbium oxide, and lutetium oxide were used instead of neodymium oxide, and other steps were the same as in Example 1 to obtain the corresponding rare earth amino acid imidazole single crystal complex. Its crystal is monoclinic system, the space group is C 2 / c , Z=4.
[0038] Example 3
[0039] First, react neodymium oxide with perchloric acid to prepare 1M neodymium perchlorate solution, add glutamic acid at 80°C for 1 hour, molar ratio neodymium:glutamic acid=1:8, adjust pH=8 with alkaline solution React at 80°C for 1 hour, then add imidazole, the molar ratio of neodymium:imidazole=1:4, react at 80°C for 1 hour, and let it stand for a period of time to obtain crystals. Other steps are the same as in Example 1.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com