Preparation method and application of Au/PILs (Polymeric Ionic Liquids)/PPyNTs (Polypyrrole Natotubes) composite material

A composite material and polymerized ionic liquid technology, which is applied in the field of preparation of gold nanoparticle/polymeric ionic liquid/polypyrrole nanotube composite material, can solve the problems of technicians requiring relatively high operation steps, expensive equipment and complicated equipment, etc. Effects of electron transport rate, state modulation convenience, and light weight

Active Publication Date: 2016-02-03
LIAONING UNIVERSITY
View PDF3 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although these methods have good accuracy, the instruments and equipment are expensive, the requirements for technicians are high, and the operation steps are complex and time-consuming

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method and application of Au/PILs (Polymeric Ionic Liquids)/PPyNTs (Polypyrrole Natotubes) composite material
  • Preparation method and application of Au/PILs (Polymeric Ionic Liquids)/PPyNTs (Polypyrrole Natotubes) composite material
  • Preparation method and application of Au/PILs (Polymeric Ionic Liquids)/PPyNTs (Polypyrrole Natotubes) composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1A

[0046] The preparation of embodiment 1Au / PILs / PPyNTs composite material

[0047] (1) Preparation method

[0048] Synthetic route such as Figure 8 shown.

[0049] 1. Synthesis of ionic liquid modified polypyrrole nanotubes (ILs / PPyNTs)

[0050] 1.1) Synthesis of PPyNTs

[0051] Polypyrrole nanotubes were synthesized by self-degradation template method. The methyl orange (MO) that takes 0.05g is added in the conical flask that contains 30mL water, after fully dissolving, then add 0.249g iron trichloride, after stirring for 5 minutes, add 0.113g pyrrole monomer again, in After stirring at room temperature for 24 hours, wash with distilled water and ethanol until neutral, and dry in vacuum at 50°C for 24 hours to obtain PPyNTs.

[0052] 1.2) PPyNTs-(CH 2 ) 4 -Synthesis of Br

[0053] Weigh 0.031g of PPyNTs and 0.055g of potassium hydroxide into a single-necked round-bottomed flask, then add 0.156g of 1,4-dibromobutane, disperse in 25mL of DMF, ultrasonically disperse for ...

Embodiment 2A

[0066] Application of Example 2 Au / PILs / PPyNTs composite material to the electrocatalytic performance of epinephrine (EP)

[0067] (1) The method is as follows:

[0068] 1) Take 1 mg of dried Au / PILs / PPyNTs nanocomposite, add it to 1 mL of ethanol, and ultrasonically disperse for 20 minutes to obtain a uniformly dispersed black suspension.

[0069] 2) Al for glassy carbon electrode 2 o 3 After polishing, they were ultrasonically cleaned in water and ethanol respectively, and after drying in the air, pipette 3 μL of the above dispersed black suspension of Au / PILs / PPyNTs onto a clean glassy carbon electrode ( GCE) surface, placed in the air, you can get a glassy carbon electrode (Au / PILs / PPyNTs / GCE) modified with Au / PILs / PPyNTs, dry it for later use.

[0070] At the same time, PILs / PPyNTs nanotube-modified glassy carbon electrodes (PILs / PPyNTs / GCE) were prepared by the same method for comparison.

[0071] 3) Put Au / PILs / PPyNTs / GCE in a phosphate buffer solution containing ep...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method and application of an Au / PILs (Polymeric Ionic Liquids) / PPyNTs (Polypyrrole Natotubes) composite material. The adopted technical scheme is that the preparation method comprises the following steps of firstly, synthesizing ionic liquid-modified polypyrrole nanotubes (ILs / PPyNTs); secondly, by taking 1-vinyl-3-ethylimidazole bromide salt as a monomer and taking 2,2-azobisisobutyronitrile as an initiator, initiating a polymerization reaction on the surfaces of the polypyrrole natotubes to obtain polymeric ionic liquid-modified polypyrrole nanotubes (PILs / PPyNTs); finally, uniformly mixing the PILs / PPyNT with an HAuCl4 solution; by taking sodium borohydride as a reducing agent, performing in-situ reduction of AuCl<4-> on the surfaces of the PILs / PPyNT to obtain Au / PILs / PPyNTs. According to the preparation method disclosed by the invention, the polymeric ionic liquids are used as connectors for combining conductive polymer polypyrrole with gold nanoparticles to obtain the Au / PILs / PPyNTs composite material which has better detectability for epinephrine.

Description

technical field [0001] The invention belongs to the field of chemical synthesis, and in particular relates to a preparation method and application of a gold nanoparticle / polymer ionic liquid / polypyrrole nanotube (Au / PILs / PPyNTs) composite material. Background technique [0002] Polypyrrole nanotubes (PPyNTs) have attracted attention due to their good electrical conductivity at room temperature, long-term environmental stability, redox performance, and ion exchange properties. However, polypyrrole is generally insoluble in water and most organic solvents and has poor dispersion, which may be due to the strong intramolecular and intermolecular interactions and the formation of crosslinked structures. Therefore, polypyrrole nanotube composite materials are developed to overcome the insolubility of polypyrrole nanotube composite materials, and improve the dispersion and electron transport rate of polypyrrole nanotube composite materials in water or solvents, so that polypyrrole ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J31/06C08F283/00C08F226/06G01N27/327G01N27/48
Inventor 茆卉张海凤姜威张国林宋溪明
Owner LIAONING UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com