Anti-bite cable protective covering

A technology of anti-tearing and outer sheath, which is applied in the field of polymer materials, can solve the problems of unfavorable commercial application and cost increase, and achieve excellent thermal and light stability, good mechanical strength, and good protection of the cable core.

Inactive Publication Date: 2016-01-20
ZHEJIANG COMMSPACE CABLE
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the complex structure will lead to a great increase in cost, so it is not conducive to commercial application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] Accurately weigh 90 parts of polyvinyl chloride resin according to the mass parts, 40 parts of calcium carbonate, 10 parts of dioctyl phthalate, 11 parts of chlorinated paraffin, 2 parts of composite stabilizer, 0.4 part of stearic acid, 0.8 part of carbon black, 2 parts of epoxy soybean oil, 0.1 part of polyethylene wax, 3 parts of anti-rat bite functional masterbatch 9074-FT-40, add to high-speed mixer, after mixing evenly, pass the mixture through twin-screw extruder, extrude to make particles , and then formed into pieces by an open mill, molded by a vulcanizing machine, and finally formed into a standard strip by a tensile machine, that is, the outer sheath of the anti-bite cable.

Embodiment 2

[0049] Accurately weigh 100 parts of polyvinyl chloride resin according to the number of parts by mass, 50 parts of calcium carbonate, 16 parts of dioctyl phthalate, 14 parts of chlorinated paraffin, 3 parts of composite stabilizer, 0.6 part of stearic acid, 1 part of carbon black, 3 parts of epoxy soybean oil, 0.2 parts of polyethylene wax, 4 parts of anti-rat bite functional masterbatch 9074-FT-40, add to a high-speed mixer, after mixing evenly, pass the mixture through a twin-screw extruder, extrude to make particles , and then formed into pieces by an open mill, molded by a vulcanizing machine, and finally formed into a standard strip by a tensile machine, that is, the outer sheath of the anti-bite cable.

Embodiment 3

[0051] Accurately weigh 95 parts of polyvinyl chloride resin according to the mass parts, 55 parts of calcium carbonate, 19 parts of dioctyl phthalate, 18 parts of chlorinated paraffin, 5 parts of composite stabilizer, 0.7 part of stearic acid, 1.1 part of carbon black, 5 parts of epoxy soybean oil, 0.3 parts of polyethylene wax, 4.5 parts of anti-rat bite functional masterbatch 9074-FT-40, add to a high-speed mixer, after mixing evenly, pass the mixture through a twin-screw extruder, extrude to make particles , and then formed into pieces by an open mill, molded by a vulcanizing machine, and finally formed into a standard strip by a tensile machine, that is, the outer sheath of the anti-bite cable.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an anti-bite cable protective covering. A shell of the anti-bite cable protective covering is prepared from, by mass, 90-110 parts of polyvinyl chloride resin, 40-60 parts of calcium carbonate, 10-20 parts of o-benzene dioctyl, 11-16 parts of chlorinated paraffin, 2-4 parts of compound stabilizer, 0.4-0.8 part of stearic acid and 3-5 parts of anti-mouse-bite master batch 9074-FT-40. The anti-bite cable protective covering is environmentally friendly and safe in formula, is free of toxin and harms to human bodies and the environment, meets the ecological requirements, and meanwhile well achieves a mouse bite prevention function; the prepared cable protective covering is firm and durable, resistant to aging and higher in flexibility and can better achieve a cable core protecting effect.

Description

technical field [0001] The invention belongs to the field of polymer materials and relates to an outer sheath of an anti-tearing cable. Background technique [0002] Rats are rodents that are widely distributed all over the world and have strong reproductive and vitality. Rats have the habit of biting objects to keep their teeth sharp. Cables laid in the field often break down due to the gnawing of rats. [0003] A common solution currently on the market is to use a complex double-layer structure or other protective structures to prevent rats from biting. However, the complex structure will lead to a great increase in cost, so it is not conducive to commercial application. Contents of the invention [0004] In order to solve the above problems, the present invention provides an anti-bite cable outer sheath, which achieves the goals of safety, environmental protection and effective prevention of rats from biting. [0005] In order to realize the above-mentioned purpose of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L91/06C08L91/00C08L23/06C08K13/02C08K3/26C08K5/12C08K5/09C08K3/04
Inventor 鲁培宇
Owner ZHEJIANG COMMSPACE CABLE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products