Industrial latex gloves and preparation method thereof

A rubber gloves, industrial technology, applied in the field of composite materials, can solve the problems of easy skin damage, anti-virus, corrosion resistance and aging resistance, etc., and achieve excellent anti-virus effect.

Inactive Publication Date: 2016-01-20
SUZHOU COSMETIC MATERIALS
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003]Technical problem to be solved: Aiming at the shortcomings of existing industrial rubber gloves, which have poor anti-virus, corrosion resistance and aging resistance, and are easy to damage the skin, the present invention provides an industrial Rubber gloves and preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] An industrial rubber glove, containing the following components in parts by mass: 28 parts of neoprene latex, 0.1 part of zinc oxide, 0.1 part of N-isopropyl-N`-phenyl-p-phenylenediamine, 0.03 part of casein, potassium octanoate 0.05 parts, water glass 0.05 parts, triethylenediamine 0.2 parts, sulfur 0.2 parts, paraffin oil 0.3 parts, polylactic acid 0.08 parts, tricalcium phosphate 3 parts, carbon black 0.2 parts, vitamin E 0.2 parts.

[0017] A preparation method of industrial rubber gloves, the steps of the preparation method are as follows:

[0018] The first step: heat the neoprene latex at 60°C for 1 hour, and then cool it to 20°C;

[0019] Step 2: Add zinc oxide, N-isopropyl-N`-phenyl-p-phenylenediamine, casein, potassium octanoate, water glass, triethylenediamine, sulfur, paraffin oil, polylactic acid, tricalcium phosphate , carbon black, and vitamin E are mixed evenly to obtain a mixed material;

[0020] Step 3: Add the mixed material to a twin-screw extruder...

Embodiment 2

[0023] An industrial rubber glove, containing the following components in parts by mass: 40 parts of neoprene latex, 0.4 part of zinc oxide, 0.5 part of N-isopropyl-N`-phenyl-p-phenylenediamine, 0.08 part of casein, potassium octanoate 0.1 part, 0.1 part of water glass, 0.5 part of triethylenediamine, 0.6 part of sulfur, 0.7 part of paraffin oil, 0.16 part of polylactic acid, 9 parts of tricalcium phosphate, 0.6 part of carbon black, 0.5 part of vitamin E.

[0024] A preparation method of industrial rubber gloves, the steps of the preparation method are as follows:

[0025] The first step: heat the neoprene latex at a temperature of 70°C for 2 hours, and then cool it to 30°C;

[0026] Step 2: Add zinc oxide, N-isopropyl-N`-phenyl-p-phenylenediamine, casein, potassium octanoate, water glass, triethylenediamine, sulfur, paraffin oil, polylactic acid, tricalcium phosphate , carbon black, and vitamin E are mixed evenly to obtain a mixed material;

[0027] Step 3: Add the mixed m...

Embodiment 3

[0030] An industrial rubber glove, containing the following components in parts by mass: 38 parts of neoprene latex, 0.3 part of zinc oxide, 0.4 part of N-isopropyl-N`-phenyl-p-phenylenediamine, 0.07 part of casein, potassium octanoate 0.09 parts, water glass 0.09 parts, triethylenediamine 0.45 parts, sulfur 0.5 parts, paraffin oil 0.6 parts, polylactic acid 0.15 parts, tricalcium phosphate 7 parts, carbon black 0.5 parts, vitamin E 0.45 parts.

[0031] A preparation method of industrial rubber gloves, the steps of the preparation method are as follows:

[0032] The first step: heat the neoprene latex at 65°C for 1.5h, then cool to 25°C;

[0033] Step 2: Add zinc oxide, N-isopropyl-N`-phenyl-p-phenylenediamine, casein, potassium octanoate, water glass, triethylenediamine, sulfur, paraffin oil, polylactic acid, tricalcium phosphate , carbon black, and vitamin E are mixed evenly to obtain a mixed material;

[0034] Step 3: Add the mixed material to a twin-screw extruder for bl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a pair of industrial latex gloves and a preparation method thereof. The pair of industrial latex gloves comprises components in parts by mass as follows: 28-40 parts of neoprene latex, 0.1-0.4 parts of zinc oxide, 0.1-0.5 parts of N-isopropyl-N'-phenyl-p-phenylenediamine, 0.03-0.08 parts of casein, 0.05-0.1 parts of potassium octoate, 0.05-0.1 parts of water glass, 0.2-0.5 parts of triethylene diamine, 0.2-0.6 parts of sulfur, 0.3-0.7 parts of paraffin oil, 0.08-0.16 parts of polylactic acid, 3-9 parts of tricalcium phosphate, 0.2-0.6 parts of carbon black and 0.2-0.5 parts of vitamin E. According to the pair of industrial latex gloves and the preparation method thereof, the pair of industrial latex gloves has excellent performance such as anti-poison, corrosion resistance, oil resistance, aging resistance, tensile resistance and the like, and has a protective function on skin and does not harm hands.

Description

technical field [0001] The invention relates to the technical field of composite materials, in particular to an industrial rubber glove and a preparation method thereof. Background technique [0002] Rubber gloves are a type of gloves made of rubber sheets or films. According to the purpose, it can be divided into acid and alkali resistant gloves, electrical insulation gloves, radiation protection gloves, medical gloves, etc. According to rubber raw materials or manufacturing process, latex gloves and molded gloves are classified. Industrial rubber gloves are essential protective gear used to protect people's hands during industrial operations. They need to have properties such as acid and alkali resistance, anti-virus, stretch resistance, and aging resistance. However, the existing industrial rubber gloves on the market are poor in anti-virus, corrosion resistance and aging resistance, and do not have the effect of hand protection, and the gloves are easy to damage the sk...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L11/02C08L91/06C08L67/04C08K13/02C08K3/22C08K5/18C08K3/32C08K3/04C08K3/06C08K5/17
Inventor 金仲恩全春兰张帆
Owner SUZHOU COSMETIC MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com