Corrosion resistant composite electroplating liquid

A composite electroplating and corrosion-resistant technology, applied in electrolytic coatings, coatings, etc., can solve problems such as time-consuming, easy to rust, corrosion, etc., achieve low wear resistance, not easy to settle, and improve corrosion resistance

Inactive Publication Date: 2016-01-13
安徽恒源煤电股份有限公司
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there are many scaffolds made of steel pipe materials. Generally, construction projects take a long time, and the scaffolding is exposed outside. It is easy to rust and corrode in bad weather. In order to save resources and prolong the service life of scaffolding, the surface modification method of materials will be used to achieve wear resistance and corrosion resistance. , anti-rust performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] A corrosion-resistant composite electroplating solution, made of the following raw materials in parts by weight (kg): 500 nickel sulfamate, 25 cobalt sulfate, 25 nickel chloride, 20 boric acid, 0.6 sodium lauryl sulfate, undecane Sodium sulfonate 0.3, styrene 4, azobisisobutyronitrile 0.2, iron citrate 8, carbon nanotube 14, sodium fluoride 2, glass fiber 6, tripotassium phosphate 1, appropriate amount of deionized water.

[0015] Described a kind of corrosion-resistant composite electroplating solution is prepared by the following specific steps:

[0016] (1) Mix and stir carbon nanotubes, glass fibers, starch, and appropriate amount of deionized water, heat to form a paste, calcinate at 500°C for 1 hour, cool and pulverize naturally, and use 4% polyethylene glycol solution to sonicate Wash for 20 minutes, take it out and wash it with deionized water to make it neutral, then put it in a blast drying oven to dry, and set aside;

[0017] (2) Add a certain amount of etha...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses corrosion resistant composite electroplating liquid. The corrosion resistant composite electroplating liquid comprises, by weight, 500-550 parts of nickel aminosulfonate, 25-30 parts of cobaltous sulfate, 25-28 parts of nickel chloride, 20-25 parts of boric acid, 0.6-0.8 part of lauryl sodium sulfate, 0.3-0.6 part of sodium 1-undecanesulfonate, 4-6 parts of styrene, 0.2-0.3 part of azodiisobutyronitrile, 8-10 parts of ferric citrate, 14-16 parts of carbon nano tube, 2-3 parts of sodium fluoride, 6-8 parts of glass fiber, 1-2 parts of tripotassium phosphate and an appropriate amount of deionized water. A preparing method is simple, the material source is wide, the pollution to the environment is small, the waste liquid processing is convenient, the corrosion resistance, abrasion resistance and strength characteristic of a scaffold can be obviously improved, the service life is prolonged, and the corrosion resistant composite electroplating liquid is worthy of popularization.

Description

technical field [0001] The invention relates to the technical field of electroplating solutions, in particular to a corrosion-resistant composite electroplating solution. Background technique [0002] Scaffolding refers to the various supports set up on the construction site for workers to operate and solve vertical and horizontal transportation. A general term in the construction industry, which refers to the construction site used for exterior walls, interior decoration or places where direct construction is too high, mainly for construction workers to work up and down or peripheral safety net enclosures and high-altitude installation components, etc. Scaffolding materials usually include: bamboo, wood, steel pipe or synthetic materials. Some projects also use scaffolding as a template, and it is also widely used in advertising, municipal administration, traffic roads and bridges, mines and other departments. At present, there are many scaffolds made of steel pipe materi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C25D3/56C25D15/00
Inventor 不公告发明人
Owner 安徽恒源煤电股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com