Environment-friendly rustproof powder coating and preparing method thereof

A powder coating, environmental protection technology, applied in the direction of powder coatings, anti-corrosion coatings, epoxy resin coatings, etc., can solve the problems of not meeting the requirements, traditional production and preparation methods of powder coatings, etc., to improve the purity and adhesion, and enhance the film-forming performance and adhesion, good film-forming effect

Inactive Publication Date: 2016-01-06
BENGBU KAIHENG ELECTRONICS CO LTD
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Organic polymer materials constitute the main part of today's coatings market. There are many types of paints, and the types of paints used in different fields are not the same. Powder coatings are a new type of solvent-free 100% solid powder coatings, but The powder coating process formula and powder coating production and preparation methods on the market are still relatively traditional and cannot meet the current market demand.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A preparation method of an environment-friendly antirust powder coating,

[0038] a. Select a reaction kettle with a large enough volume, and install a stirrer, a constant temperature heater, a reflux condenser, a thermometer, an air inlet pipe, and a decompression device on the reaction kettle for backup;

[0039] b. Add 200 parts of toluene solution to the reaction kettle prepared in a, turn on the constant temperature heater to heat the toluene solution at a constant temperature, and feed nitrogen into the inlet pipe for 25 minutes to get rid of the air in the reaction kettle;

[0040] c, adjust the constant temperature heater to ensure that the temperature in the reactor after step b is at 70°C, slowly add 55 parts of GMA type acrylic resin, 45 parts of epoxy resin, 18 parts of absolute ethanol, and 28 parts of flax in the reactor. Oil, 5 parts of titanium dioxide, 3 parts of degassing agent, 2 parts of flexibilizer, 1 part of leveling agent, and fully stirred, keep...

Embodiment 2

[0043] A preparation method of an environment-friendly antirust powder coating,

[0044] a. Select a reaction kettle with a large enough volume, and install a stirrer, a constant temperature heater, a reflux condenser, a thermometer, an air inlet pipe, and a decompression device on the reaction kettle for backup;

[0045] b. Add 400 parts of toluene solution to the reaction kettle prepared in a, turn on the constant temperature heater to heat the toluene solution at a constant temperature, and feed nitrogen into the inlet pipe for 20 minutes to get rid of the air in the reaction kettle;

[0046] c, adjust the constant temperature heater to ensure that the temperature in the reactor after step b is at 70°C, slowly add 105 parts of GMA type acrylic resin, 110 parts of epoxy resin, 68 parts of absolute ethanol, and 58 parts of flax in the reactor Oil, 10 parts of titanium dioxide, 10 parts of degassing agent, 8 parts of flexibility agent, 15 parts of leveling agent, and fully sti...

Embodiment 3

[0049] A preparation method of an environment-friendly antirust powder coating,

[0050] a. Select a reaction kettle with a large enough volume, and install a stirrer, a constant temperature heater, a reflux condenser, a thermometer, an air inlet pipe, and a decompression device on the reaction kettle for backup;

[0051] b. Add 280 parts of toluene solution to the reactor prepared in a, turn on the constant temperature heater to heat the toluene solution at a constant temperature, and feed nitrogen into the inlet pipe for 25 minutes to get rid of the air in the reactor;

[0052] c, adjust the constant temperature heater to ensure that the temperature in the reactor after step b is at 70°C, slowly add 77 parts of GMA type acrylic resin, 86 parts of epoxy resin, 47 parts of absolute ethanol, and 35 parts of flax in the reactor Oil, 8 parts of titanium dioxide, 5 parts of degassing agent, 5 parts of flexibility agent, 5 parts of leveling agent, and fully stirred, and kept warm f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an environment-friendly rustproof powder coating. The environment-friendly rustproof powder coating is prepared from, by weight, 55-105 parts of GMA type acrylic resin, 45-110 parts of epoxy resin, 18-68 parts of absolute ethyl alcohol, 28-58 parts of linseed oil, 200-400 parts of methylbenzene solutions, 5-10 parts of titanium dioxide, 3-10 parts of degassing agents, 2-8 parts of flexibilizer and 1-15 parts of flatting agents. The environment-friendly rustproof powder coating in the technical scheme is high in purity and large in adhesive force, both the powder coating and the coating production process are free of three-waste pollution, and therefore the environment-friendly effect is good; the powder coating can be recovered and coated for the second time and is resistant to acid, alkali and abrasion and waterproof, and a rustproof film is smooth, long in service life and good in rustproof capacity.

Description

technical field [0001] The invention belongs to the field of antirust materials for metal surfaces, and more specifically relates to a powder coating for antirust on metal surfaces and a preparation method of the coating. Background technique [0002] Coating is a kind of chemical mixture coating that can firmly cover the surface of objects and play the role of antirust, waterproof, anticorrosion, acid resistance, alkali resistance, etc. It is widely used in modern technology and industrial fields. Generally speaking, a coating is a material that can be coated on the surface of the object to be coated and can form a solidly attached continuous film. It can be either inorganic, such as electroplating copper, electroplating nickel, electrogalvanizing, etc., or organic, such as Most organic polymer materials. Organic polymer materials constitute the main part of today's coatings market. There are many types of paints, and the types of paints used in different fields are not th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D163/00C09D191/00C09D5/08C09D5/03C09D7/12
Inventor 常林法
Owner BENGBU KAIHENG ELECTRONICS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com