Polyurethane rubber PTMEG-F composite material and preparation method thereof

A technology of polyurethane rubber and composite material, applied in the field of polyurethane rubber PTMEG-F composite material and its preparation, can solve the problems of high density, large amount of consumables, easy size change, etc., and achieve the effect of low density, material saving and dimensional stability

Inactive Publication Date: 2015-12-09
黄文鹏
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Existing rubber foam materials usually use chemical foaming agents such as azo (such as azoformamide), 4,4 bisbenzenesulfonyl hydrazide, and dinitrosopentamethylenetetramine as foaming agents. , by controlling the amount of foaming agent to control the foaming (expansion) ratio (that is, the size) of the foaming material, the disadvantage is that the size of the foaming material is difficult to control, and the shrinkage rate of the material after foaming is large, and the size is easy to change. And the calculation of mold ratio is difficult
If hard rubber (non-foaming rubber) is used, although the size is stable after molding, it has a high density and a large amount of consumables, resulting in a waste of resources.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyurethane rubber PTMEG-F composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A polyurethane rubber PTMEG-F composite material, including polyether polyol (PPG), isocyanate (MDI), crosslinking agent and foaming aids, wherein the foaming aids include catalysts, additives, water, surface active agent, triisocyanate, sulfur accelerator, foaming agent, internal lubricant, external lubricant, colorant.

[0023] The mass percentage of each component of the rubber composite material is: 50%-70% polyether polyol (PPG), 18%-50% isocyanate (MDI), 6%-9% crosslinking agent, 1-3% catalyst , 4-5% additives, 0.9-2% water, 1-10% surfactant, 1-4% triisocyanate, 1-3% sulfur accelerator, 2-4% foaming agent, 1-3% Internal lubricant, 2-3% external lubricant, 1-10% colorant.

[0024] The crosslinking agent adopts 1.4 butanediol or hexylene glycol.

[0025] The linking agent adopts HQEE (4-hydroxyethyloxyethyl-1-hydroxyethylphenylene ether)

[0026] The catalyst adopts metal stannous octoate, dibutyltin dilaurate and mercury acetate.

[0027] The catalyst uses non-...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the fields of composite material and preparation thereof, and particularly relates to a polyurethane rubber PTMEG-F rubber composite material including polyether polyol (PPG), isocyanate (MDI), a crosslinking agent and foaming auxiliary agents, wherein the foaming auxiliary agents include a catalyst, auxiliary agents, water, a surfactant, triisocyanate, a sulfur promoting agent, a foaming agent, an internal lubricant, an external lubricant and a colorant; with the use of the preparation method, the composite material has low density and stable size compared with traditional hard rubber, and can greatly save materials.

Description

technical field [0001] The invention relates to the field of composite materials and preparation thereof, in particular to a polyurethane rubber PTMEG-F composite material and a preparation method thereof. Background technique [0002] Existing rubber foam materials usually use chemical foaming agents such as azo (such as azoformamide), 4,4 bisbenzenesulfonyl hydrazide, and dinitrosopentamethylenetetramine as foaming agents. , by controlling the amount of foaming agent to control the foaming (expansion) ratio (that is, the size) of the foaming material, the disadvantage is that the size of the foaming material is difficult to control, and the shrinkage rate of the material after foaming is large, and the size is easy to change. And the calculation of mold magnification is difficult. If hard rubber (non-foaming rubber) is used, although the size is stable after molding, the density is high and the amount of consumables is large, resulting in a waste of resources. Conte...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L75/08C08J9/08C08J9/10C08J3/24
Inventor 黄文鹏
Owner 黄文鹏
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com