A kind of soft and hard particle blended anti-reflection coating liquid and its preparation method and application

A technology of anti-reflection coating and particles, which is applied in the field of anti-reflection coating liquid and its preparation, can solve the problems of limited application, achieve the effect of stable anti-reflection deepening, simple and easy finishing process, and avoid slippery hand feeling

Active Publication Date: 2017-04-19
ZHEJIANG SCI-TECH UNIV
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, the extensive use of organic solvents in the literature limits their application in fabric finishing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of soft and hard particle blended anti-reflection coating liquid and its preparation method and application
  • A kind of soft and hard particle blended anti-reflection coating liquid and its preparation method and application
  • A kind of soft and hard particle blended anti-reflection coating liquid and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] (1) Take by weighing 0.16g sodium dodecylbenzene sulfonate and join in the water of 84.76g, after mechanical stirring and mixing, add 8g methyl methacrylate and 2g divinylbenzene in the solution, after mechanical stirring, Put into the water bath and pass N 2 15min, after heating up to 70°C, dissolve 0.08g of potassium persulfate in 5g of water and add it to the above reaction mixture, after reacting for 3h, raise the temperature to 85°C and keep it warm for 30min to obtain a hard latex particle solution with a cross-linked structure Product 1, 10% solids.

[0050] (2) Weigh 1g of sodium dodecylbenzenesulfonate and add it to 83.94g of water. After mechanically stirring and mixing, add 10g of methyl acrylate to the solution. After mechanically stirring, put it into a water bath to pass N 2 15min, after heating up to 70°C, dissolve 0.06g of potassium persulfate in 5g of water and add it to the above reaction mixture, after reacting for 2.5h, raise the temperature to 85°C...

Embodiment 2

[0056] (1) Weigh 0.16g of sodium lauryl sulfate and add it to 74.78g of water. After mechanical stirring and mixing, add 16g of methyl methacrylate and 4g of divinylbenzene to the solution. After mechanical stirring, put Water bath in the pass N 2 15min, after heating up to 75°C, dissolve 0.06g of potassium persulfate in 5g of water and add it to the above reaction mixture, after reacting for 3h, raise the temperature to 85°C and keep it warm for 30min to obtain a hard latex particle solution with a cross-linked structure Product 3, 20% solids.

[0057] (2) Weigh 2g of sodium lauryl sulfate and add it to 72.94g of water. After mechanical stirring and mixing, add a mixture of 10g of acrylonitrile and 10g of ethyl acrylate to the solution. After mechanical stirring, put it into a water bath ZTO N 2 15min, after heating up to 75°C, dissolve 0.06g of potassium persulfate in 5g of water and add it to the above reaction mixture, after reacting for 2.5h, raise the temperature to 85...

Embodiment 3

[0060] (1) Weigh 0.06g of sodium lauryl sulfate and 0.14g of isooctylphenyl glycoside and add it to 69.88g of water. After mixing evenly with mechanical stirring, add 20g of ethyl methacrylate and 5g of dimethacrylic acid to the solution Ethylene glycol ester, mechanically stirred evenly, put into the water bath and pass N 2 15min, after heating up to 80°C, dissolve 0.08g of potassium persulfate in 5g of water and add it to the above reaction mixture, after reacting for 3h, raise the temperature to 90°C and keep it warm for 30min to obtain a hard latex particle solution with a cross-linked structure Product 5, 25% solids.

[0061] (2) Weigh 0.2g of sodium lauryl sulfate and add it to 69.72g of water. After mechanical stirring and mixing, add 25g of butyl acrylate to the solution. After mechanical stirring, put it into a water bath and pass N 2 15min, after heating up to 80°C, dissolve 0.08g of ammonium persulfate in 5g of water and add it to the above reaction mixture. After ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a reflection-deducting coating liquid with blended soft and hard particles as well as a preparation method and application of the reflection-deducing coating liquid. The method comprises the following steps: (1) preparing hard emulsion particles, namely fully mixing an emulsifying agent with water, adding monomers for forming the hard emulsion particles and a cross-linking agent into an emulsifying agent aqueous solution, adding an initiator and residual water, reacting and performing heat preservation, thereby obtaining a hard emulsion particle aqueous dispersion; (2) preparing soft emulsion particles, namely fully mixing an emulsifying agent with a part of water, adding monomers for forming the soft emulsion particles into an emulsifying agent aqueous solution, adding an initiator and residual water, reacting and performing heat preservation, thereby obtaining a soft emulsion particle aqueous dispersion; and (3) mixing the hard emulsion particle aqueous dispersion with the soft emulsion particle aqueous dispersion, thereby obtaining the reflection-deducting coating liquid with the blended soft and hard particles. According to the coating liquid, the soft particles and the hard particles are blended to form a nano rough surface on the surface of a dacron fabric, so that reflection deduction and densification of dacron are realized and the coating liquid has extensive application prospect.

Description

technical field [0001] The invention relates to the field of textile additives and its preparation, in particular to an anti-reflection coating liquid blended with soft and hard particles, its preparation method and application. Background technique [0002] Due to polyester fiber (n f =1.73) and air (n 0 =1.0) The difference in refractive index is large, and the incident light is largely reflected by the fiber surface without being absorbed by the dye. Therefore, the color saturation of the cloth surface is poor, and it is difficult to present strong color effects such as dark green, navy blue, purple red, and black ink. And as the fiber fineness decreases, the specific surface area and reflective surface area of ​​the fabric increase, and the dyed fabric often presents a "white" visual effect. At present, the method of post-finishing is often used to achieve fabric darkening, and finishing agents are the hotspots of research. [0003] The early finishing agents were mos...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M15/263D06M15/31C08F220/14C08F212/36C08F120/14C08F220/44C08F220/18C08F222/14C08F120/18C08F2/26D06M101/32
Inventor 杨雷宋庆婷沈一峰
Owner ZHEJIANG SCI-TECH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com