Hot-melt copper slag modification process and its device

A hot-melting slag and modification technology, which is applied in hot-melting copper slag modification device and hot-melting copper slag modification technology field, can solve the problem of unsatisfactory iron concentrate grade and recovery rate indicators, difficulty in selling iron concentrate, and inability to Achieving problems such as separation of iron and silicon

Active Publication Date: 2017-05-31
YANGGU XIANGGUANG COPPER
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Copper smelting slag is the recovery of copper from the slag produced in the copper smelting process with a copper content of more than 0.5%, and it also contains Fe, Zn, Pb, Co and other metals. At present, the focus of copper smelting slag treatment in the world is on In terms of copper recovery, pyrolysis and beneficiation depletion processes are mainly used. In the beneficiation and depletion process, the vast majority of copper metal is recovered; for the tailings after copper beneficiation, a few enterprises use magnetic separation process to treat iron ore. However, since the iron minerals are mainly fayalite, which is a compound of ferrous oxide and silicon dioxide, magnetic separation cannot realize the separation of iron and silicon, resulting in unsatisfactory indicators of iron concentrate grade and recovery rate. Difficulty selling concentrates

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hot-melt copper slag modification process and its device
  • Hot-melt copper slag modification process and its device
  • Hot-melt copper slag modification process and its device

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0030] The core of the invention is to provide a hot-melt copper slag modification process to improve the refining precision of iron. Another core of the present invention is to provide a hot-melt copper slag modification device for performing the above-mentioned hot-melt copper slag modification process.

[0031] In order to enable those skilled in the art to better understand the technical solutions of the present invention, the present invention will be further described in detail below in conjunction with the accompanying drawings and embodiments.

[0032] Please refer to Figure 1 to Figure 7 , in a specific embodiment, the hot melt copper slag modification process provided by the present invention includes the steps of: carrying out oxidation treatment on the slag at the discharge port of the liquid hot molten slag by inputting oxygen; The slag is slowly cooled.

[0033] It can be seen from the above description that in the hot-melt copper slag modification process pro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a modification process for hot molten copper slag. The modification process comprises the steps of inputting oxygen into the slag at a discharging port of the liquid hot molten slag to perform oxidation treatment; and performing slow cooling on the hot molten slag after oxidation treatment. According to the modification process for the hot molten copper slag, the following reaction that 6(2FeO.SiO2) +2O2=4Fe3O4+6SiO2 is performed, so that silicon and iron are separated, and the iron extracting accuracy is further improved. The invention further discloses a modification device for the hot molten copper slag.

Description

technical field [0001] The invention relates to the technical field of copper smelting slag, in particular to a modification process of hot-melt copper slag. The present invention also relates to a hot-melt copper slag modification device for performing the above-mentioned hot-melt copper slag modification process. Background technique [0002] Copper smelting slag is the recovery of copper from the slag produced in the copper smelting process with a copper content of more than 0.5%, and it also contains Fe, Zn, Pb, Co and other metals. At present, the focus of copper smelting slag treatment in the world is on In terms of copper recovery, pyrolysis and beneficiation depletion processes are mainly used. In the beneficiation and depletion process, the vast majority of copper metal is recovered; for the tailings after copper beneficiation, a few enterprises use magnetic separation process to treat iron ore. However, since the iron minerals are mainly fayalite, which is a compo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C21B3/06C21B3/08C22B7/04
CPCY02P10/20Y02W30/50
Inventor 耿联胜
Owner YANGGU XIANGGUANG COPPER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap