A kind of graphene/titanium dioxide composite material with hollow microspheres and preparation method thereof

A graphene composite and composite material technology, applied in the preparation of microspheres, chemical instruments and methods, microcapsule preparations, etc., can solve the problems of cumbersome synthesis process, limited application scope, small specific surface area, etc., and achieves simple operation method and cost. Inexpensive, large surface area effect

Active Publication Date: 2017-10-17
哈尔滨悟山青环保科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, on the one hand, these reported graphene / titania composite materials often have a single structure, small specific surface area, and poor water dispersibility; greatly limited its scope of application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of graphene/titanium dioxide composite material with hollow microspheres and preparation method thereof
  • A kind of graphene/titanium dioxide composite material with hollow microspheres and preparation method thereof
  • A kind of graphene/titanium dioxide composite material with hollow microspheres and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Embodiment 1: The method provided by the invention is used to prepare graphene / titanium dioxide hollow composite microspheres

[0026] (1) Silica colloidal microspheres with an average particle size of 220 nm were prepared according to a slightly modified Stöber method [(a) Wang, W.; Gu, B.; Liang, L.; Hamilton, W. A. J. Phys. Chem. B 2003, 107 , 3400-3404. (b) Wang, W.; Gu, B.; Liang, L.; Hamilton, W. A. J. Phys. Chem. B 2003, 107 , 12113-12117.].

[0027] (2) The silica microspheres prepared in step (1) were coated with a layer of graphene oxide by an ultrasonic-assisted self-assembly method to obtain a silica / graphene oxide composite microsphere with an average particle size of 220 nm ( Xiao, W.; Zhang, Y.; Liu, B. ACS Appl. Mater. Interfaces 2015, 7 , 6041-6046.).

[0028] (3) Ultrasonic disperse 10 mg of the silica / graphene oxide composite microspheres in step (2) in 2 mL of water, then add it dropwise to 20 mL of absolute ethanol under ultrasonic conditio...

Embodiment 2

[0031] Embodiment 2: Graphene / titanium dioxide hollow composite microspheres prepared in the present invention are used for the photodegradation of methylene blue:

[0032] (1) Prepare a methylene blue aqueous solution with a concentration of 10 mg / L, take 48 mL of it and add it to the reaction tube, and then ultrasonically disperse 5 mg of the graphene / titanium dioxide hollow composite microsphere sample prepared in Example 1 in 2 mL with a concentration of 10 mg / L methylene blue aqueous solution, and then added dropwise to the above reaction tube under stirring conditions.

[0033] (2) Place the reaction tube in step (1) in a photochemical reaction apparatus (the brand model is Qiaoyue JOYN-GHX-A), use a high-pressure mercury lamp as the ultraviolet light source, set the power to 300 W, and stir vigorously The photocatalytic reaction was carried out under certain conditions, and then 4 mL of the dispersion liquid was pipetted from the reaction system every 5 min and placed i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a graphene / titanium dioxide composite material with a unique hollow microspherical structure and a simple and convenient preparation method thereof, and belongs to the technical field of synthesis and preparation of graphene-based micro-nano composite materials. First, an improved Stöber method is used to prepare silica microspheres, and then the surface is coated with a layer of graphene oxide through an ultrasound-assisted self-assembly method. Titanium tetrafluoride is then used as the precursor and a solvothermal method is used to make the silica microspheres. The deposition and crystallization of titanium dioxide on the surface of silica / graphene oxide composite microspheres, the dissolution and removal of the silica core, and the reduction of the coated graphene oxide components are achieved in one step, thereby preparing graphene / titanium dioxide hollow composite microspheres. . The hollow composite microspheres exhibit good water dispersibility and have efficient catalytic activity for the photodegradation of organic dyes, showing broad application prospects.

Description

technical field [0001] The invention belongs to the technical field of synthesis and preparation of graphene-based micro-nano composite materials, and in particular relates to a graphene / titanium dioxide composite material with hollow microspheres and a preparation method thereof. Background technique [0002] Since the discovery of graphene, its unique structural characteristics and excellent electronic properties have made the development and application of graphene-based composite materials a hot spot in the field of material science in recent years. In previous studies, people often loaded various functional nanoparticles (such as noble metals, metal oxides, metal sulfides, polymer nanoparticles, etc.) on the surface of graphene oxide sheets, and then reduced them to graphene components. Graphene-based composite materials have been obtained and widely used in catalysis, sensing, drug sustained release, and energy storage. However, adopting this strategy to synthesize is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J21/18B01J35/08B01J13/02C02F1/32C02F1/58
CPCB01J13/02C02F1/325C02F1/725B01J21/18C02F2101/308C02F2305/10B01J35/51
Inventor 肖巍张艳华周文杰
Owner 哈尔滨悟山青环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com