Glass fiber reinforced polycarbonate composite material and its preparation method and application

A polycarbonate and composite material technology, used in the preparation of notebook shells, glass fiber reinforced polycarbonate composite materials and the field of preparation thereof, can solve the problem of not maximizing the comprehensive balance of composite materials and no glass fiber retention length , composite materials heat resistance and poor coating performance, etc., to achieve the effect of rich color selection characteristics, enhanced coating performance, mechanical strength and heat resistance retention

Active Publication Date: 2018-04-10
CGN JUNER NEW MATERIALS +1
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the thickness and width of the flat glass fiber used in this patent document do not have a reserved length for the glass fiber, and the comprehensive balance between the strength and warpage performance of the composite material has not been realized to the greatest extent, and its mechanical properties are yet to be determined. At the same time, the heat resistance and coating performance of the composite material are not good enough

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glass fiber reinforced polycarbonate composite material and its preparation method and application
  • Glass fiber reinforced polycarbonate composite material and its preparation method and application
  • Glass fiber reinforced polycarbonate composite material and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～10

[0035] Examples 1 to 10 relate to glass fiber reinforced polycarbonate composite materials. The content of each component of the composite material is shown in Table 1. Among them, the PC resin selects LG-DOW PC201-10 resin (at 300 ℃, 1.2Kg conditions The lower melt flow rate is 8~15g / 10min, and the weight average molecular weight is 2.5~40,000 resin); the shaped glass fiber is selected from Taishan Fiberglass Company’s alkali-free flat chopped glass fiber, and its glass fiber width is 30~40μm , The thickness is 2~5μm; the antioxidant is a combination of Iraanox1076 and Iraanox168 from Ciba, and the weight ratio is 1:1.

[0036] Table 1 formula components and parts by weight

[0037]

[0038]

[0039] *The compatibilizer 1 is ethylene-octene-glycidyl methacrylate copolymer, the compatibilizer 2 is hydrogenated styrene-butadiene-styrene grafted maleic anhydride copolymer; the lubricant 1 is stearic acid Calcium, Lubricant 2 is ethylene bisstearic acid amide, Lubricant 3 is silicone...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
widthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a glass fiber reinforced polycarbonate composite material, its preparation method and its application in the preparation of notebook casings. The composite material is made of the following raw materials in parts by weight: polycarbonate 40-65 parts; special-shaped glass fiber 30-50 parts; flame retardant 2-8 parts; anti-dripping agent 0.1-1 part; compatibilizer 2-8 parts; antioxidant 0.2-3 parts; lubricant 0.2- 3 parts; the special-shaped glass fiber is an alkali-free flat chopped glass fiber, the width of the special-shaped glass fiber is 30-40 μm, the thickness is 2-5 μm, and the length is 350-450 μm. The material of the invention has the characteristics of ultra-high modulus, low warpage, high flame retardancy, high impact performance, and good coating performance, and at the same time, the injection molding process is simple and the cost is low, and it is very suitable for preparing the notebook shell.

Description

Technical field [0001] The invention relates to the technical field of polycarbonate composite materials, in particular to a glass fiber reinforced polycarbonate composite material, a preparation method thereof, and application in the preparation of a notebook casing. Background technique [0002] With the rapid development of China's economy and the popularization of the Internet, people have higher and higher requirements for the use of electronic devices such as thinness, beauty, and ease of carrying. Since its inception, notebook computers have been rapidly developed with the advantages of small size and portability. At present, with the rapid development of mobile phones, tablet computers, etc., this convenient experience of notebook computers has encountered huge challenges. Therefore, how to make notebook computers have the characteristics of lighter and thinner, diversified appearance, three-dimensional structure, rich color selection, and excellent surface texture exper...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L69/00C08L23/08C08L51/00C08K13/04C08K7/14C08K5/42
Inventor 王浩方万漂黄瑞杰周国剑肖红伟姜小龙黄志杰
Owner CGN JUNER NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap