Thin film flocked-type high-elastic flame-retarding warm-keeping sheet material and preparation method thereof

A flake material, flocking technology, applied in the textile field, to achieve the effect of reducing the amount of use, smoothing the surface and improving warmth retention

Active Publication Date: 2015-11-11
WUHAN TEXTILE UNIV
View PDF7 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the current thermal insulation wadding products, thermal insulation wadding that can achieve high elasticity, bulkiness, warmth retention and flame retardancy is relatively scarce. Therefore, it is of practical significance to prepare a high-elasticity flame-retardant thermal insulation wadding

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thin film flocked-type high-elastic flame-retarding warm-keeping sheet material and preparation method thereof
  • Thin film flocked-type high-elastic flame-retarding warm-keeping sheet material and preparation method thereof
  • Thin film flocked-type high-elastic flame-retarding warm-keeping sheet material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0038] (3) Preparation of mixed powder: uniformly mix hot melt powder and flame retardant powder to prepare hot melt powder and flame retardant powder mixed powder 6, 6 ， ;

[0039] (4) Sprinkle powder: Sprinkle the mixed powder 6 of hot-melt powder and flame-retardant powder in the upper fiber net 1, and the lower fiber net 1 ， Sprinkle the mixed powder of hot melt powder and flame retardant powder inside 6 ， ;

[0040] (5) Drying: Mix powders 6 and 6 sprinkled with hot-melt powder and flame-retardant powder respectively. ， The upper fiber web 1, the lower fiber web 1 ， to dry;

[0041] (6) Hot-press lamination: coat the upper flocking film substrate 3 and the upper hot-melt film 2 on the upper fiber web 1, and make the upper hot-melt film 2 on the upper flocking film substrate 3 and the upper fiber web. Between the nets 1, the upper hot-melt film 2 is melted by hot pressing, and the upper flocking film substrate 3 is consolidated on the upper fiber web 1; the lower floc...

Embodiment 1

[0050] Strip-shaped film flocking type mechanically-laid high-elastic flame-retardant and warm-keeping sheet material and its preparation method:

[0051] see figure 1 , figure 2 , film-flocked high-elastic flame-retardant thermal sheet material, including upper fiber web 1, upper hot-melt film 2, upper flocking film substrate 3, upper adhesive film 4, fluff 5, lower adhesive film 4 ', the lower flocking film substrate 3', the lower hot-melt film 2', the lower fiber web 1 ， , Mixed powder of hot melt powder and flame retardant powder 6, 6 ， . The upper fiber web 1 and the lower fiber web 1' are three-dimensional crimped hollow polyester fibers with a fineness of 3D and a length of 51mm and low-melting fibers with a fineness of 3D and a length of 51mm and a melting point of 110°C. %: 20% is opened and mixed, and the fiber web prepared by mechanical carding of short fibers. A mixed powder 6 of hot-melt powder and flame-retardant powder is sprinkled inside the upper fiber w...

Embodiment 2

[0067] Lattice-shaped film flocking type mechanically-laid high-elastic flame-retardant and warm-keeping sheet material and its preparation method:

[0068] see figure 1 , image 3 , film-flocked high-elastic flame-retardant thermal sheet material, including upper fiber web 1, upper hot-melt film 2, upper flocking film substrate 3, upper adhesive film 4, fluff 5, lower adhesive film 4 ', the lower flocking film substrate 3', the lower hot-melt film 2', the lower fiber web 1 ， , Mixed powder of hot melt powder and flame retardant powder 6, 6 ， . The upper fiber web 1 and the lower fiber web 1' are three-dimensional crimped hollow polyester fibers with a fineness of 3D and a length of 51mm and low-melting fibers with a fineness of 3D and a length of 51mm and a melting point of 110°C. %: 20% is opened and mixed, and the fiber web prepared by mechanical carding of short fibers. A mixed powder 6 of hot-melt powder and flame-retardant powder is sprinkled inside the upper fiber ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to a thin film flocked-type high-elastic flame-retarding warm-keeping sheet material and a preparation method thereof and belongs to the technical field of textile. In the interiors of an upper fiber net layer and a lower fiber net layer of the sheet material, a mixed powder composed of a hot melting powder and a flame retarding powder is filled. An upper flocked thin film base material and a lower flocked thin film base material are fixedly combined respectively with the two opposite surfaces of the upper fiber net layer and the lower fiber net layer, wherein fluffs are fixed combined between the upper flocked thin film base material and the lower flocked thin film base material. The preparation method includes following steps: (1) preparation before flocking; (2) preparation of the fiber nets; (3) powder preparation; (4) powder filling; (5) drying; (6) hot-pressing film coverage; (7) glue coating; (8) electrostatic flocking; (9) drying; (10) fluff suction; (11) composition of the fiber nets; (12) drying; and (13) winding. Compared with a sheet material in the prior art, the warm-keeping sheet material is excellent in flame retarding function, is good in elasticity and is good in warm keeping performance.

Description

technical field [0001] The invention relates to a thin-film flocking type high-elastic flame-retardant heat-retaining sheet material and a manufacturing method thereof, belonging to the field of textiles. Background technique [0002] In the past, people used traditional thermal insulation materials made of cotton, hemp, silk, wool and ordinary polyester, nylon, acrylic fiber and man-made fibers as thermal insulation materials. Among these thermal insulation materials, silk and wool have better thermal insulation properties. However, the fiber is prone to bacteria and is not resistant to moths. Moreover, silk is expensive, wool fiber has peculiar smell and poor molding degree, and cashmere processed through multiple processes is more expensive, and its use has been limited for many years. With the development of living standards and science and technology, people began to develop new thermal insulation materials, and chemical fiber thermal insulation sheets mainly composed o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B5/24B32B5/30B32B7/12B32B37/12B32B38/16B32B38/00
CPCB32B5/028B32B2250/40B32B2255/02B32B2260/025B32B2264/0264B32B2264/0278B32B2307/304B32B2307/3065B32B2307/51B32B2307/724B32B2437/00
Inventor 张如全蒋吉众武继松张尚勇李建强王成国
Owner WUHAN TEXTILE UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More