Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Manganese dioxide-ruthenium dioxide composite material and its preparation method and application

A composite material, the technology of ruthenium dioxide, applied in the directions of manganese oxide/manganese hydroxide, chemical instruments and methods, ruthenium/rhodium/palladium/osmium/iridium/platinum compounds, etc., can solve the complex preparation process, poor conductivity, problems such as poor dispersion, to achieve the effects of good dispersion, high specific capacity and low manufacturing cost

Active Publication Date: 2017-10-10
SHANGHAI INST OF CERAMIC CHEM & TECH CHINESE ACAD OF SCI
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to overcome the defects of existing electrode materials in the manufacture of supercapacitors and provide a novel electrode material: carbon dioxide A ruthenium dioxide composite material, and a method for preparing the composite material, to overcome the defects of low specific capacity, poor stability, poor dispersibility, poor conductivity, and complicated preparation process in the preparation of manganese dioxide electrode materials by current chemical methods. Exploring the use of this composite material to make supercapacitors

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manganese dioxide-ruthenium dioxide composite material and its preparation method and application
  • Manganese dioxide-ruthenium dioxide composite material and its preparation method and application
  • Manganese dioxide-ruthenium dioxide composite material and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] Prepare 0.1mol / L manganese chloride (MnCl 2 ) and ruthenium chloride (RuCl 3 ) aqueous solution of 200ml each; take 20ml of manganese chloride and ruthenium chloride aqueous solution, mix and stir for 5 minutes; add dropwise to the above solution until the pH value is 9; centrifuge filter, wash 3 times with water; dry at 80°C to obtain Ruthenium dioxide composite powder. The specific surface area of ​​the composite was determined by nitrogen adsorption-desorption to be 135m 2 / g.

[0051] Oxygenate Ruthenium dioxide composite material powder and polyvinylidene fluoride (PVDF) N-methylpyrrolidone (NMP) solution (PVDF concentration: 25mg / ml) were evenly mixed to obtain a viscous slurry, which was coated on graphite paper as a working electrode; During chemical testing, platinum wire is used as the counter electrode, silver / silver chloride is used as the reference electrode, and 1mol / L Na 2 SO 4 The aqueous solution is electrolyte; the test instrument is Shanghai C...

Embodiment 2

[0061] Prepare 1mol / L respectively, 0.8mol / L, each 200ml of 0.4mol / L manganese chloride, prepare 20ml of 0.1mol / L ruthenium chloride aqueous solution; An amorphous manganese oxide-ruthenium dioxide composite material.

[0062] The above-mentioned amorphous manganese oxide-ruthenium dioxide composite materials with ratios of manganese and ruthenium of 4:1, 8:1, and 10:1 have the highest specific capacitances of 289F / g and 263F / g respectively at a scan rate of 2mV / s. , 224F / g.

[0063] Example 2 is to adjust the concentration of manganese chloride so that the molar ratio of ruthenium chloride and manganese chloride is changed in the range of 1: (4-10). The measured specific capacitance is lower than the 1:1 molar ratio of CO2 - specific capacitance value of ruthenium dioxide. This is due to the poor conductivity of manganese oxide, increasing the amount of manganese oxide leads to the weakening of charge transport, which reduces the specific capacitance of the composite mate...

Embodiment 3

[0065] Using filter paper as a diaphragm and 1mol / L NaSO4 as an electrolyte, two electrode sheets obtained in Example 1 were placed on the front and back sides of the diaphragm to obtain a symmetrical supercapacitor (symmetrical cell). Active material area 1×1cm 2 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention relates to a manganese dioxide-ruthenium dioxide composite material, a preparation method of the composite material and an application of the composite material in the field of supercapacitors, wherein the manganese dioxide-ruthenium dioxide composite material is amorphous and porous particles, The particle size is 10-50nm; the composite material is produced by in-situ co-precipitation with manganese salt and ruthenium salt as raw materials; in 1mol / L Na2SO4 aqueous electrolyte, when the scan rate is 2mV / s, the The specific capacitance of the composite material can reach 347F / g; the molar ratio of the ruthenium element and the manganese element in the composite material is 1: (1-10).

Description

technical field [0001] The present invention relates to a manganese dioxide-ruthenium dioxide composite material, a preparation method of the composite material and the utilization of the composite material, in particular to an amorphous manganese dioxide-ruthenium dioxide composite material, co-precipitated by a precursor solution Preparation of the composite material and the application of the composite material in the field of supercapacitors. Background technique [0002] Supercapacitors have the advantages of high power density, fast response time, long life, and simple maintenance. They can be widely used in the fields of information, electronics, energy, environment, transportation, and military industry. Electrochemical capacitor electrode materials with excellent instantaneous charge and discharge performance and good cycle performance are imminent. [0003] According to the electrode materials used, supercapacitors can be divided into the following two categories:...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01G45/02C01G55/00H01G11/46
Inventor 黄富强支键尹浩
Owner SHANGHAI INST OF CERAMIC CHEM & TECH CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com