Bamboo cane softener

A softener and bamboo strip technology, which is applied in wood treatment, wood processing equipment, impregnated wood, etc., can solve the problems of too simple, easy to bake and break bamboo strips, and affect the toughness and strength of bamboo strips, and achieve good and softening effects Good, enhanced strength and toughness effect

Inactive Publication Date: 2015-09-09
陈新棠
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The existing traditional bamboo strips are generally softened by the traditional method of roasting. After the bamboo strips are roasted, they can be bent and woven into various products. Toughness and Strength of Bamboo Strips

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0009] A kind of bamboo stick softening agent described in the present embodiment 1 is made up of the following raw material components: 20 parts of chloromethyl oxirane, 30 parts of ethyl acetate, 20 parts of n-octanol, 25 parts of isoamyl Alcohol, 20 parts of isobutanol, 8 parts of castor oil polyoxyethylene ether, 6 parts of sodium dodecylbenzene sulfonate, 8 parts of dodecyl dimethyl amine oxide, 6 parts of zinc stearate, 8 parts of hard Copper stearate, 8 parts aluminum stearate, 6 parts nickel stearate, 8 parts butyl butyrate, 10 parts methyl carbamate, 8 parts ethyl methacrylate, 6 parts petroleum ether, 10 parts chlorinated paraffin , 150 parts of deionized water.

Embodiment 2

[0011] A kind of bamboo stick softening agent described in the present embodiment 2 is made up of the raw material components of the following parts: 30 parts of chloromethyl oxirane, 40 parts of ethyl acetate, 25 parts of n-octanol, 30 parts of isoamyl Alcohol, 25 parts of isobutanol, 10 parts of castor oil polyoxyethylene ether, 8 parts of sodium dodecylbenzene sulfonate, 10 parts of dodecyl dimethyl amine oxide, 10 parts of zinc stearate, 10 parts of hard Copper stearate, 10 parts of aluminum stearate, 10 parts of nickel stearate, 10 parts of butyl butyrate, 12 parts of methyl carbamate, 10 parts of ethyl methacrylate, 10 parts of petroleum ether, 15 parts of chlorinated paraffin , 200 parts of deionized water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a bamboo cane softener. The bamboo cane softener comprises components of raw materials in parts as follows: 20-30 parts of epichlorohydrin, 30-40 parts of ethyl acetate, 20-25 parts of n-caprylic alcohol, 25-30 parts of isoamyl alcohol, 20-25 parts of isobutanol, 8-10 parts of castor oil polyoxyethylene ether, 6-8 parts of sodium dodecyl benzene sulfonate, 8-10 parts of dodecyl dimethyl amine oxide, 6-10 parts of zinc stearate, 8-10 parts of copper stearate, 8-10 parts of aluminum stearate, 6-10 parts of nickel stearate, 8-10 parts of butyl butyrate, 10-12 parts of methyl carbamate, 8-10 parts of ethyl methacrylate, 6-10 parts of petroleum ether, 10-15 parts of chlorinated paraffin and 150-200 parts of deionized water. The bamboo cane softener has a good softening effect, is non-corrosive and convenient to popularize and use and has a better effect on improvement of the strength and the toughness of a softened part.

Description

technical field [0001] The invention relates to the technical field of a softener, in particular to a bamboo strip softener. Background technique [0002] The existing traditional bamboo strips are generally softened by the traditional method of roasting. After the bamboo strips are roasted, they can be bent and woven into various products. Toughness and strength of bamboo strips. Contents of the invention [0003] The purpose of the present invention is to provide a kind of bamboo strip softener in order to overcome above existing shortcoming of the prior art, the softening effect of this bamboo strip softener is good, without corrosion, strengthens the strength and toughness of softening position, and effect is better, Easy to promote and use. [0004] The technical scheme that the present invention solves its technical problem is: a kind of bamboo strip softener, is made up of the raw material component of following parts: 20-30 parts of chloromethyl oxirane, 30-40 pa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B27K3/50B27K5/06
CPCB27K3/50B27K5/06B27K2240/00
Inventor 陈新棠
Owner 陈新棠
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com