Preparation process of insulating resin for completely sealed bus duct

A technology of insulating resin and preparation process, applied in the field of preparation technology of insulating resin for fully enclosed bus duct, can solve the problems of serious environmental pollution, short insulation life, falling off, etc., and achieves reduction of environmental pollution, excellent insulation performance, and improved insulation performance. Effect

Inactive Publication Date: 2015-08-19
KINGSHORE NEW RESOURCES ELECTRIC JIANGSU
View PDF7 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] When insulating coatings are applied to equipment related to power systems, their performance is not only insulation, but also high temperature resistance, corrosion resistance, and impact resistance. At present, traditional insulating coatings have some defects, such as insufficient coating adhesion. , Easy to layer, fall off, low solid content, thin film formation, serious environmental pollution, short insulation life, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The preparation process of an insulating resin for a fully enclosed bus duct provided in this embodiment includes the following specific steps:

[0028] Take 5-15 parts of acrylic resin in a container, add 15 parts of a mixed solvent, stir and disperse at a speed of 4500r / min for 30-40 minutes to obtain a primary emulsion;

[0029] Add 2 parts of zinc chromate, 5 parts of zinc chloride, 2 parts of mica powder, and 5 parts of pigment to the above-mentioned primary emulsion, stir and disperse at a speed of 3800r / min for 25 minutes to obtain a color slurry;

[0030] Mix epoxy powder and benzophenone tricarboxylic anhydride, then add 16 parts of mixed solvent, mix with the first inorganic filler, the second inorganic filler, the third inorganic filler and the above-mentioned color paste, at a speed of 1100r / min Stir to disperse for 15 minutes;

[0031] will step Add 6 parts of silicone polyether polyol, 3 parts of ethylene bis stearic acid amide, 6 parts of acryl...

Embodiment 2

[0037] The preparation process of the aforementioned insulating resin for fully enclosed bus duct provided in this embodiment includes the following specific steps:

[0038] Take 11 parts of acrylic resin in a container, add 16 parts of mixed solvent, stir and disperse at a speed of 5500r / min for 36 minutes to obtain a primary emulsion;

[0039] Add 6 parts of zinc chromate, 3 parts of zinc chloride, 4 parts of mica powder, and 6 parts of pigment into the above-mentioned primary emulsion, stir and disperse at a speed of 3800r / min for 25 minutes to obtain a color paste;

[0040] Mix epoxy powder and benzophenone tricarboxylic anhydride, then add 16 parts of mixed solvent, mix with the first inorganic filler, the second inorganic filler, the third inorganic filler and the above-mentioned color paste, at a speed of 950r / min Stir and disperse for 16 minutes;

[0041] will step Add 6 parts of silicone polyether polyol, 3 parts of ethylene bis stearic acid amide, 8 parts of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
relative permittivityaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation process of insulating resin for a completely sealed bus duct. The process comprises the following steps: (1) putting 5-15 parts of acrylic resin into a container, adding 10-20 parts of a mixed solvent, and stirring and dispersing for 30-40 minutes at the rotation speed of 4000-6000r / minute, thereby obtaining primary emulsion; (2) adding 2-8 parts of zinc chromate, 1-5 parts of zinc chloride, 2-6 parts of mica powder and 1-5 parts of pigment into the primary emulsion, and stirring and dispersing for 20-30 minutes at the rotation speed of 3600-4200r / minute, thereby obtaining a sizing agent; (3) mixing epoxy powder with benzophenone tricarboxylic acid anhydride, further adding 10-20 parts of the mixed solvent to mix with first inorganic packing, second inorganic packing, third inorganic packing and the sizing agent, and stirring and dispersing for 10-20 minutes at the rotation speed of 0-1200r / minute; and (4) adding 5-10 parts of organosilicone polyether polyol, 1-5 parts of ethylidene bioctadecanamide, 5-10 parts of crylic acid resin and 10-15 parts of polyamide resin into the mixed liquid, and stirring and dispersing for 10-20 minutes at the rotation speed of 600-1100r / minute, thereby obtaining the insulating resin for the completely sealed bus duct.

Description

technical field [0001] The invention relates to the field of manufacturing and processing of fully enclosed bus ducts, in particular to a preparation process of insulating resin for fully enclosed bus ducts. Background technique [0002] Insulating paint is a paint with excellent electrical insulation properties, which can be used as a protective coating for products or components in the electrical and electronic industry. With the development of the science and technology industry, we have higher and higher requirements for the performance of insulating coatings. We have developed H-class, C-class, outdoors with excellent performance, and can be used in high temperature, humidity, severe cold, large temperature difference, strong radiation, corrosive High-voltage insulating coatings for harsh environmental conditions such as oil, oil, and salt spray are a worldwide topic in the field of new electrical materials. [0003] When insulating coatings are applied to equipment re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L33/00C08L63/00C08L71/00C08L77/00C08K13/02C08K3/24C08K3/16C08K3/34C08K5/20C08K3/26C08K3/38C08K3/04
Inventor 朱冬宏钱纪明
Owner KINGSHORE NEW RESOURCES ELECTRIC JIANGSU
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products