Helical carbon fiber water-based antiseptic camouflage paint and preparation method thereof

A technology of spiral carbon fiber and stealth paint, applied in the field of paint, can solve the problems of low mechanical performance of paint film, poor comprehensive performance, large environmental pollution, etc., and achieve the effects of simple production process, low cost and high viscosity

Inactive Publication Date: 2015-07-22
JIANGSU UNIV OF TECH
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there are still many defects in the performance of anti-corrosion stealth coatings in my country. The overall performance is poor and cannot meet the needs of the society, such as low mechanical properties of the paint film, poor anti-corrosion, and large environmental pollution.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] The spiral carbon fiber water-based anti-corrosion stealth coating is composed of two components, A and B, in a mass ratio of 1:1. In terms of parts by mass, component A includes the following components and contents: 100 parts of water-based epoxy resin; 0.5 parts of defoamer; 10 parts of distilled water. In parts by mass, component B includes the following components and contents: 25 parts of water-based epoxy curing agent; 0.1 part of defoamer; 1.2 parts of dispersant; 25 parts of superfine talcum powder; 20 parts of zinc phosphate; 10 parts of iron red 20 parts; 20 parts of titanium dioxide; 20 parts of spiral carbon fiber chiral wave absorbing agent;

[0050] The preparation method of spiral carbon fiber water-based anticorrosion stealth paint, the steps include:

[0051] (1) Spiral carbon fiber chiral absorber is prepared by horizontal furnace substrate method, with acetylene as carbon source and nickel plate as catalyst, PCL 3 As a co-catalyst, helical chiral c...

Embodiment 2

[0057] The spiral carbon fiber water-based anti-corrosion stealth coating is composed of two components, A and B, in a mass ratio of 1:1. In terms of parts by mass, component A includes the following components and contents: 100 parts of water-based epoxy resin; 0.5 parts of defoamer; 10 parts of distilled water. In parts by mass, component B includes the following components and contents: 25 parts of water-based epoxy curing agent; 0.1 part of defoamer; 1.2 parts of dispersant; 25 parts of superfine talcum powder; 25 parts of zinc phosphate; 10 parts of iron red parts; 20 parts of titanium dioxide; 25 parts of spiral carbon fiber chiral wave absorbing agent.

[0058] The preparation method of spiral carbon fiber water-based anticorrosion stealth paint, the steps include:

[0059] (1) Spiral carbon fiber chiral wave absorbing agent is prepared by horizontal furnace substrate method, with acetylene as carbon source and nickel plate as catalyst, PCL 3 As a cocatalyst, helical ...

Embodiment 3

[0065] The spiral carbon fiber water-based anti-corrosion stealth coating is composed of two components, A and B, in a mass ratio of 1:1. In terms of parts by mass, component A includes the following components and contents: 100 parts of water-based epoxy resin; 0.5 parts of defoamer; 10 parts of distilled water. In parts by mass, component B includes the following components and contents: 25 parts of water-based epoxy curing agent; 0.1 part of defoamer; 1.2 parts of dispersant; 25 parts of superfine talcum powder; 30 parts of zinc phosphate; 10 parts of iron red parts; 20 parts of titanium dioxide; 30 parts of spiral carbon fiber chiral wave absorbing agent.

[0066] The preparation method of spiral carbon fiber water-based anticorrosion stealth paint, the steps include:

[0067] (1) Spiral carbon fiber chiral wave absorbing agent is prepared by horizontal furnace substrate method, with acetylene as carbon source and nickel plate as catalyst, PCL 3 As a cocatalyst, helical ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
reflectanceaaaaaaaaaa
reflectanceaaaaaaaaaa
reflectanceaaaaaaaaaa
Login to View More

Abstract

The invention discloses helical carbon fiber water-based antiseptic camouflage paint and a preparation method thereof. The helical carbon fiber water-based antiseptic camouflage paint is formed by blending a component A and a component B in mass ratio of 1:1, wherein the component A comprises the following components in parts by mass: 80-120 parts of water-borne epoxy resin, 0.2-0.8 part of a defoaming agent and 5-15 parts of distilled water; and the component B comprises the following components in parts by mass: 20-30 parts of a water-borne epoxy curing agent, 0.08-0.15 part of a defoaming agent, 1-1.5 parts of a dispersing agent, 20-30 parts of ultrafine talcum powder, 15-30 parts of zinc phosphate, 0-20 parts of iron oxide red, 15-30 parts of titanium dioxide and 15-30 parts of helical carbon fiber chiral wave absorbing agent. The invention also discloses a preparation method of the helical carbon fiber water-based antiseptic camouflage paint. The helical carbon fiber water-based antiseptic camouflage paint has the advantages that anti-corrosion property is strong, wave absorption property is good, impact strength is high, flexibility is good, the preparation method is simple, and service life is long when the helical carbon fiber water-based antiseptic camouflage paint is applied to marine equipment.

Description

technical field [0001] The invention relates to a coating technology, especially a spiral carbon fiber water-based anti-corrosion stealth coating and a preparation method thereof Background technique [0002] Anti-corrosion and stealth of marine military equipment and operating platforms is one of the key technologies of marine engineering. Corrosion of metal components in the marine environment will cause stress corrosion cracking, hydrogen embrittlement, corrosion fatigue, intergranular corrosion, etc., resulting in fractures and ecological disasters in the marine environment. In recent years, a lot of research has been done on the anti-corrosion and stealth of metal components in the marine environment at home and abroad, and various anti-corrosion and stealth technologies have made great progress, but they are still far from meeting the actual needs. [0003] Marine anti-corrosion stealth coating refers to the anti-corrosion stealth coating used in the marine environment...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D5/30C09D5/32C09D5/08
CPCC09D163/00C08K3/22C08K3/32C08K3/34C08K7/06C08K13/04C08K2003/2241C08K2003/2272C08K2003/328C09D5/08C09D5/30C09D5/32C09D7/61C09D7/70
Inventor 王泽董观秀徐修玲卢雅琳谈衡叶霞孙冬梅
Owner JIANGSU UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com