Dicing sheet with protective film forming layer and chip fabrication method

A manufacturing method and technology of protective film, which can be applied in the fields of film/sheet release liner, film/sheet adhesive, semiconductor/solid-state device manufacturing, etc., which can solve the problem of increased number of processes, increased product cost, and decreased yield and other problems to achieve the effect of preventing damage, inhibiting deformation or peeling

Active Publication Date: 2015-06-03
LINTEC CORP
View PDF5 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this method increases the number of steps, leading to an increase in product cost
In addition, since the thickness accuracy of the protective film formed as described above is not sufficient, the yield of the product may decrease.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Dicing sheet with protective film forming layer and chip fabrication method
  • Dicing sheet with protective film forming layer and chip fabrication method
  • Dicing sheet with protective film forming layer and chip fabrication method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～4 and comparative example 1～3

[0172] Using the compositions for protective film-forming layers containing the above-mentioned components in the compounding ratios shown in Table 1, slices with protective film-forming layers were produced, and various physical properties were evaluated. The results are shown in Table 2.

[0173] [Table 1]

[0174]

[0175] [Table 2]

[0176]

Example 1

Example 2

Example 3

Example 4

Comparative example 1

Comparative example 2

Comparative example 3

Tg(°C) of acrylic polymer

4

4

17

-28

4

4

4

Storage modulus (GPa)

0.7

2.5

0.6

0.7

0.5

0.4

3

punching workability

A

A

B

A

A

A

C

Distortion on Pickup

A

A

A

A

B

B

A

[0177] From the results in Table 2, when the storage modulus of the protective film forming layer is 0.6 to 2.5 GPa, both punchability and deformability are good. Slices with a storage...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
storage modulusaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
elastic modulusaaaaaaaaaa
Login to View More

Abstract

[Problem] To provide a dicing sheet with a protective film forming layer, provided with a precut and hardened protective film forming layer, wherein when the dicing sheet is fabricated, the protective film forming layer is not deformed even when subjected to die punch processing using a die cutter. [Solution] This dicing sheet with a protective film forming layer (10) is characterized in that a hardened protective film forming layer (4) is temporarily affixed, so as to be peelable, to the inner circumference of a support body (3) having an adhesive section on the outer circumference thereof, and the storage elasticity coefficient of the protective film forming layer at 23°C prior to hardening is 0.6-2.5 GPa.

Description

technical field [0001] The present invention relates to a slice with a protective film forming layer that is formed on the back of a chip and can also be used as a slice, and particularly relates to a slice with a protective film forming layer that is not damaged or deformed at the end of the protective film forming layer . Moreover, this invention relates to the manufacturing method of the chip|tip using the dicing with a protective film forming layer. Background technique [0002] In recent years, semiconductor devices have been manufactured using a mounting method called a so-called face down method. In the flip-chip method, a semiconductor chip (hereinafter also simply referred to as a "chip") having electrodes such as bumps on a circuit surface is used, and the electrodes are bonded to a substrate. Therefore, the surface (chip back surface) opposite to the circuit surface of the chip may be exposed. [0003] The exposed chip back surface may be protected with an orga...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01L21/301C09J7/02C09J133/00C09J7/40
CPCC09J7/40C09J133/02H01L21/6836H01L2221/68336H01L2221/68327C09J2433/005C09J2203/326
Inventor 高山佳篠田智则佐伯尚哉高野健
Owner LINTEC CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com