A Homogenization Heat Treatment Process for Reducing Anisotropy of Wide Rolled Aluminum Sheet

A homogeneous heat treatment and anisotropic technology, applied in the field of aluminum alloy processing, to reduce the work hardening rate, increase the driving force, and reduce the effect of solid solution strengthening

Inactive Publication Date: 2016-08-17
CHONGQING UNIV
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of the above-mentioned deficiencies in the prior art, the purpose of the present invention is to provide a homogenized heat treatment process for reducing the anisotropy of wide-width rolled aluminum sheets, and to solve the problem of uniformity of structure and deformation of alloy sheets in all directions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A Homogenization Heat Treatment Process for Reducing Anisotropy of Wide Rolled Aluminum Sheet

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Example 1 ： A homogenization heat treatment process for reducing the anisotropy of wide-width rolled aluminum plates, comprising the steps of:

[0019] The ingot of 5052 alloy added with 0.3 wt% Er was used, and then the alloy was subjected to two-stage homogenization heat treatment.

[0020] First, carry out homogenization and heat preservation at 560°C for 30 h (first-level homogenization);

[0021] Subsequently, it was cooled to 300 °C and kept for 10 h (secondary homogenization), and then it was taken out of the furnace and air-cooled to room temperature.

[0022] The ingot that has undergone the above-mentioned two-stage homogenization treatment is hot-rolled at a rolling temperature of 470°C. Before rolling, the rolled billet is preheated at 470°C for 1 h, and the total rolling reduction is 73%. The obtained plate was tested for tensile mechanical properties at room temperature along the rolling direction, vertical rolling direction and 45° direction, and the...

Embodiment 2

[0023] Example 2 ： A homogenization heat treatment process for reducing the anisotropy of wide-width rolled aluminum plates, comprising the steps of:

[0024] Add 0.2 wt% (or 0.3 wt% or 0.4wt%) rare earth element Er to the 5052 alloy, and then perform three-stage homogenization heat treatment:

[0025] First, the 5052 alloy ingot added with rare earth element Er was subjected to homogenization and heat preservation at 560 °C for 30 h, that is, first-level homogenization;

[0026] Subsequently, cool to 150°C and hold for 10 h, that is, secondary homogenization;

[0027] Then, the temperature was raised to 300°C, and the temperature was continued for 10 h, that is, three-stage homogenization;

[0028] Finally, take it out of the oven and let it cool to room temperature.

[0029] The ingot that has undergone the above-mentioned three-stage homogenization treatment is hot-rolled at a rolling temperature of 470°C. Before rolling, the rolled billet is preheated at 470°C for 1 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a homogenization heat treatment process for reducing the anisotropy of wide-width rolled aluminum plates, adding 0.1-0.5 wt% of rare earth element Er to 5052 alloy; and then performing two-stage or three-stage homogenization heat treatment; The two-stage homogenization heat treatment is performed at 530-560°C for 20-30 hours of homogenization and heat preservation, then cooled to 150-300°C for 8-12 hours, and then air-cooled to room temperature; 530-560°C for 20-30 hours of homogenization and heat preservation, then cooled to 150-180°C and heat preservation for 8-12 hours, further raised to 300-320°C and continued heat preservation for 8-12 hours, and then air-cooled to room temperature. The method can effectively control the solid solution and precipitation of the second phase, effectively spheroidize the undissolved non-equilibrium compounds in the alloy, significantly improve the plasticity of the alloy, and reduce the anisotropy of the structure and deformation of the rolled plate.

Description

technical field [0001] The invention belongs to the technical field of aluminum alloy processing, and in particular relates to a homogenization heat treatment process for reducing the anisotropy of wide-width rolled aluminum plates. Background technique [0002] Energy and environmental issues continue to promote the application of lightweight materials in transportation and aerospace. Due to the advantages of light weight, high specific strength, corrosion resistance and easy forming and processing, aluminum alloy is widely used in more and more fields. In recent years, with the rapid development of my country's economy, the rise of manufacturing industry and the improvement of national consumption level, the demand for high-grade wide aluminum sheet and strip represented by transportation, packaging and printing has increased rapidly. Especially for aluminum containers, refrigerated trucks, coal trucks and other transportation aluminum strips, the required width is not le...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22F1/047
CPCC22F1/047
Inventor 张静杨亮左汝林
Owner CHONGQING UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com