Pellets prepared from blast furnace slag iron concentrate powder and its preparation method and application

A technology of iron concentrate powder and blast furnace slag, which is applied in the field of pellets prepared from blast furnace slag iron concentrate powder and its preparation, can solve the problems of high energy consumption and complicated process, and achieve economic benefit improvement, good economic benefit and time saving Effect

Active Publication Date: 2017-07-28
PANZHIHUA HUANYE METALLURGICAL SLAG DEV CO LTD
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method needs to dehumidify the raw materials, and after the balls are formed, they need to enter the roasting system to go through the preheating, intermediate firing, and roasting processes. The energy consumption is high and the process is relatively complicated.
[0005] In the prior art, there is no technology related to preparing pellets from iron concentrate powder extracted from blast furnace slag by cold consolidation. Those skilled in the art need a method for preparing pellets from blast furnace slag iron concentrate powder with simple process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Pellets prepared from blast furnace slag iron concentrate powder and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0025] a, the blast furnace slag is crushed, sieved, ball milled, and magnetically separated to obtain fine iron powder, the iron content is 60-70%, and the particle size is 0.8mm-1.5mm, and the particle size of 25% of the iron fine powder in the obtained iron fine powder is 0.8mm-1mm;

[0026] b. Stir and mix the iron powder, water and binder with a multifunctional dough mixer, and stir for 2-3 minutes to mix evenly;

[0027] c. Use HYG367-80 high-pressure double-roller briquetting machine to press and form, the diameter of the briquette is 550mm, and place it at room temperature for 4 days to dry to obtain pellets;

[0028] The binding agent described in step b is the mixture of the Yilong brand cold-setting pellet binder and clay produced by Zibo Yilong Chemical Co., Ltd.; the Yilong brand cold-setting pellet produced by Zibo Yilong Chemical Co., Ltd. in the binder The added amount of the binder is 0.5-1% of the weight of the iron fine powder, the added amount of the clay ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of comprehensive utilization of solid waste resources and specifically relates to pellets prepared from blast furnace slag iron fine powder as well as a preparation method and application of the pellets. The invention aims at providing a method for preparing the pellets from the blast furnace slag iron fine powder, which is simple in process. The technical scheme adopted by the method provided by the invention comprises the following steps: a) performing crushing, screening, ball-milling and magnetic separation on blast furnace slag with the water content of not more than 10% to obtain iron fine powder, and controlling the particle size of the iron fine powder to be not more than 1.5mm, so that the iron fine powder with the particle size of less than 1mm accounts for above 20% of total weight of the iron fine powder and the iron content is not less than 60%; b) mixing the iron fine powder with a binding agent, adding water and uniformly mixing to obtain a mixture; and c) pressing the mixture for forming and air-drying to obtain the pellets. Compared with the conventional preparation of the pellets from steel slag, by adopting the method, the steps are saved, the production cost is reduced and the time is saved.

Description

technical field [0001] The invention belongs to the field of comprehensive utilization of solid waste resources, and in particular relates to pellets prepared from blast furnace slag iron concentrate powder, a preparation method and application thereof. Background technique [0002] Blast furnace slag is an inevitable product of blast furnace ironmaking production. Since Panzhihua Iron and Steel was put into production, it has accumulated more than 50 million tons, and an annual increase of 3.5 million tons has been added. The massive accumulation of blast furnace slag has seriously affected the production of Panzhihua Iron and Steel Co., Ltd., resulting in a waste of resources. At the same time, it also has a negative impact on the surrounding natural environment of the Jinsha River Basin in the upper reaches of the Yangtze River. [0003] Foreign iron and steel plants have been producing and using consolidated pellets for many years. For example, Nippon Steel’s Nagoya Iron...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22B1/243
CPCC22B1/243
Inventor 蓝静杨志远杨胜利苏辉杨青邓梅艳
Owner PANZHIHUA HUANYE METALLURGICAL SLAG DEV CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com