Manufacturing method of medical chitosan antibacterial fibers

The technology of chitosan fiber and antibacterial fiber is applied in the field of medical antibacterial sterilization and rope, which can solve the problems of poor antibacterial and sterilization effect of antibacterial fiber and complicated preparation process of antibacterial fiber, and achieve the effect of good effect and simple preparation process.

Inactive Publication Date: 2015-03-25
TAIAN ROPE NET PLASTIC
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the antibacterial and bactericidal effect of ordinary antibacterial fibers is poor, and the preparation process of antibacterial fibers is complicated

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method of medical chitosan antibacterial fibers

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0015] The preparation method of medical chitosan antibacterial fiber thread comprises the steps:

[0016] (1) Material selection: choose chitosan antibacterial fiber filament, its specification is 105D-210D, diameter is 0.1-0.5mm; the chitosan antibacterial fiber filament treatment process is: chitosan fiber is beaten and chopped Dispersing, using sodium dodecylbenzene sulfonate to wash and pretreat chitosan fibers, adding a dispersant to obtain chitosan antibacterial fiber filaments;

[0017] (2) Doubling: 2-5 treated chitosan antibacterial fiber filaments are used for doubling and 1 strand;

[0018] (3) Twisting: After paralleling, the chitosan antibacterial fiber filaments are twisted through a twisting machine, and the transmission belt of the twisting machine is tight and tight. Each filament must be controlled by a tension regulator, and its speed and twist are measured regularly , the twist is less than 20 twists / m;

[0019] (4) Heat setting: Heat the twisted chitosa...

Embodiment 1

[0022] The preparation method of medical chitosan antibacterial fiber thread comprises the steps:

[0023] (1) Material selection: choose chitosan antibacterial fiber filament, its specification is 105D, and the diameter is 0.1-0.5mm; Chitosan fiber is washed and pretreated by sodium dialkylbenzenesulfonate, and a dispersant is added to obtain chitosan antibacterial fiber filament;

[0024] (2) Paralleling: 2 chitosan antibacterial fiber filaments are used for paralleling to form 1 strand;

[0025] (3) Twisting: After paralleling, the chitosan antibacterial fiber filaments are twisted through a twisting machine, and the transmission belt of the twisting machine is tight and tight. Each filament must be controlled by a tension regulator, and its speed and twist are measured regularly , the twist is less than 20 twists / m;

[0026] (4) Heat setting: heat setting the twisted chitosan antibacterial fiber filament through a steam setting machine at a temperature of 60°C and a pres...

Embodiment 2

[0029] The preparation method of medical chitosan antibacterial fiber thread comprises the steps:

[0030] (1) Material selection: Chitosan antibacterial fiber filaments are selected, the specification is 160D, and the diameter is 0.1-0..5mm; the treatment process of chitosan antibacterial fiber filaments is: beating and chopping the chitosan fibers, Using sodium dodecylbenzene sulfonate to carry out washing pretreatment to chitosan fiber, add dispersant, obtain chitosan antibacterial fiber filament;

[0031] (2) Paralleling: 4 chitosan antibacterial fiber filaments are used in paralleling to form 1 strand;

[0032] (3) Twisting: After paralleling, the chitosan antibacterial fiber filaments are twisted through a twisting machine, and the transmission belt of the twisting machine is tight and tight. Each filament must be controlled by a tension regulator, and its speed and twist are measured regularly , the twist is less than 20 twists / m;

[0033] (4) Heat setting: heat setti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a manufacturing method of medical chitosan antibacterial fibers. The manufacturing method includes selecting chitosan antibacterial fiber filaments subjected to treatment, subjecting the fiber filaments to doubling, twisting and thermal shaping, and twisting a plurality of chitosan antibacterial fiber strands after thermal shaping into medical chitosan antibacterial fibers by a twister. The manufacturing method is simple in process and the medical chitosan antibacterial fibers are good in antibacterial and sterile effect.

Description

technical field [0001] The invention belongs to the technical field of ropes, and in particular relates to a preparation method of medical chitosan antibacterial fiber thread, which is suitable for the field of medical antibacterial and sterilization. Background technique [0002] Antibacterial fibers are fibers mixed with antibacterial agents or treated with antibacterial surfaces. They have antibacterial and sterilizing functions against methicillin-resistant Staphylococcus aureus, and can prevent infection and infection. The antibacterial fiber enables the antibacterial agent to dissolve slowly, forming an antibacterial zone on the surface of the fiber. Even if the surface antibacterial agent is washed off, new antibacterial agent will overflow to form a new antibacterial zone. However, common antibacterial fibers have poor antibacterial and bactericidal effects, and the preparation process of antibacterial fibers is complicated. Contents of the invention [0003] The ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D02G3/44D02G3/02D02G3/26D06C7/02D06M13/256D06M101/10
Inventor 沈明刘瑞强张功明田涛侯虎刘翠华
Owner TAIAN ROPE NET PLASTIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com