An elastic coating and fire-resistant technology, applied in fire-resistant coatings, polyester coatings, coatings, etc., can solve the problems of poor fire-resistance of elastic coatings, and achieve the effects of good fire resistance, good flexibility and simple components
Inactive Publication Date: 2015-03-25
SUZHOU MINGXUAN FLOORING COATINGS
View PDF4 Cites 2 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] The technical problem mainly solved by the present invention is to provide a fire-resistant elastic coating, which solves the problem that the elastic coating has poor fire resistance
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0015] Embodiment 1 of the present invention comprises: a kind of refractory elastic paint, comprises the composition of following content ratio:
[0016] 2 parts polyester resin
[0017] 3.2 parts of methyl isobutyl ketone
[0018] Acrylic milk 2.5 parts
[0019] 3 parts propylene glycol
[0020] Elastic powder 5 parts
[0021] Quartz sand 8 parts
[0022] Bentonite 10 parts
[0023] Talcum powder 4 parts.
Embodiment 2
[0024] Embodiment 2 of the present invention comprises: a kind of refractory elastic paint, comprises the composition of following content ratio:
[0025] 3 parts polyester resin
[0026] 4.2 parts of methyl isobutyl ketone
[0027] Acrylic milk 2.8 parts
[0028] Propylene glycol 4 parts
[0029] Elastic powder 6 parts
[0030] Quartz sand 9 parts
[0031] Bentonite 11 parts
[0032] Talcum powder 5 parts.
Embodiment 3
[0033] Embodiment 3 of the present invention comprises: a kind of refractory elastic coating, comprises the composition of following content ratio:
[0034] 5 parts polyester resin
[0035] 6.2 parts of methyl isobutyl ketone
[0036] Acrylic milk 3.6 parts
[0037] Propylene glycol 5 parts
[0038] Elastic powder 8 parts
[0039] Quartz sand 10 parts
[0040] Bentonite 12 parts
[0041] Talcum powder 6 parts.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a fire-resistant elastic coating. The fire-resistant elastic coating comprises the following components in parts by weight: 2-5 parts of polyester resin, 3.2-6.2 parts of methyl isobutyl ketone, 2.5-3.6 parts of an acrylic emulsion, 3-5 parts of propylene glycol, 5-8 parts of elastic powder, 8-10 parts of quartz sand, 10-12 parts of bentonite and 4-6 parts of talc powder. In such a manner, the fire-resistant elastic coating disclosed by the invention has strong three-dimensional sense, good flexibility, simplicity in components and low cost as well as long flame-retardant time, high tensile viscosity and good fire resistance.
Description
technical field [0001] The invention relates to the field of architectural coatings, in particular to a fire-resistant elastic coating. Background technique [0002] Elastic architectural coatings are based on synthetic resin emulsion, formulated with pigments, fillers and additives. After applying a certain thickness (dry film thickness greater than or equal to 150μm), it has the ability to produce small cracks due to the expansion and contraction (movement) of the base material. flexible functional coatings. This type of coating has the characteristics of rich expressiveness, strong three-dimensional effect, good flexibility, strong plasticity, strong adhesion, scrubbing, acid and alkali resistance, no fading, no peeling, no cracking, easy maintenance and recoating, etc. However, ordinary elastic coatings have poor fire resistance and are easy to fall off under high temperature. Contents of the invention [0003] The main technical problem to be solved by the invention...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more