Welding machine cable material adopting single covering layer and preparation method thereof

A covering layer, welding machine technology, applied in the direction of organic insulators, plastic/resin/wax insulators, rubber insulators, etc., to achieve the effect of competitive advantage in the large market

Inactive Publication Date: 2015-03-25
HEBEI HUATONG WIRES & CABLES GRP CO LTD
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The electric welding machine cable can choose double-layer covering or single-layer covering. The advantage of single-layer covering is that it saves the process, but there is a technical problem that the covering layer needs to take into account the dual characteristics of insulation and sheath. The single-layer covering layer can pass the voltage test when it meets the insulation and electrical properties. , wear-resistant, oil-resistant, soft, and flame-retardant, it is also necessary to consider whether there is a market competitive advantage in the price of materials. It is difficult to meet the above needs with the background technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] The present invention will be further described below through embodiment.

[0013] In the embodiment, the single-layer covering layer electric welding machine cable material, the weight parts of each raw material component are:

[0014] Chlorinated polyethylene rubber 100 parts

[0015] 25 parts of ethylene propylene rubber

[0016] 1 part of 2,2,4-trimethyl-1,2-dihydroquinoline polymer

[0017] Magnesium oxide 12 parts

[0018] Zinc oxide 1.5 parts

[0019] 1.5 parts of lead stearate

[0020] Tribasic lead sulfate 2.4 parts

[0021] Low molecular weight polyethylene wax 6 parts

[0022] 2.2 parts of antimony trioxide

[0023] Composite flame retardant 4 parts

[0024] Precipitated white carbon black 18 parts

[0025] 30 parts superfine talcum powder

[0026] OPE special clay 36 parts

[0027] 3 parts semi-refined paraffin wax

[0028] Chlorinated paraffin 36 parts

[0029] Dioctyl phthalate 13 parts

[0030] Dicumyl peroxide 3.5 parts

[0031] Triallyl i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a welding machine cable material adopting a single covering layer and a preparation method thereof, and belongs to the technical field of cables. The technical scheme is that the welding machine cable material comprises the following main components: 90-105 parts of chlorinated polyethylene rubber, 20-30 parts of ethylene propylene rubber, 0.5-1 part of poly(1,2-dihydro-2,2,4-trimethylquinoline), 5-8 parts of low-molecular polyethylene wax, 1-3 parts of antimony trioxide, 10-15 parts of dioctyl phthalate, 3-4 parts of dicumyl peroxide, 2-3 parts of triallyl isocyanurate and 0.5-1.5 parts of N,N'-1,3-metaphenylene bismaleimide. According to the welding machine cable material and the preparation method, the chlorinated polyethylene rubber and ethylene propylene rubber are taken as the base materials, double functions including insulation and sheathing are considered, the cable material has characteristics of the flame retardant level A, has good electric insulation property, passes the 1,000 V finished product voltage test, has wear-resisting, oil-resisting and soft characteristics and meets all requirements in the national standard GB / T5013.1 for SE3 and SE4 materials, the tensile strength is higher than 12 Mpa, the cost is about half of that of SE4 neoprene in the corresponding period or other equivalent synthetic elastomer mixture, so that the cable material has great competitive advantage in market.

Description

technical field [0001] The invention relates to a single-layer covering electric welding machine cable material and a preparation method thereof, belonging to the technical field of cables. Background technique [0002] With the rapid development of the economy, wires and cables have been widely used in various industries and fields. At the same time, with the increasing number of cable manufacturers and increasingly fierce competition, how to reduce the production cost of cables on the basis of ensuring quality has become an important issue for various cable manufacturers. Manufacturers are most concerned about research and development topics. The electric welding machine cable can choose double-layer covering or single-layer covering. The advantage of single-layer covering is that it saves the process, but there is a technical problem that the covering layer needs to take into account the dual characteristics of insulation and sheath. The single-layer covering layer can pa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/28C08L23/16C08L91/06C08K13/02C08K3/22C08K5/098C08K3/36C08K3/34C08K5/12H01B3/44
CPCC08L23/286C08L2201/02C08L2203/202C08L2205/035H01B3/28C08L23/16C08L23/06C08L91/06C08K13/02C08K2003/222C08K2003/2296C08K5/098C08K2003/3045C08K3/2279C08K3/36C08K3/34C08K3/346C08K5/12
Inventor 李君张书军张宝龙程伟崔金生杨启曾孙连发田志明吴健
Owner HEBEI HUATONG WIRES & CABLES GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products