Super early-strength mortar

A technology of early-strength mortar and early-strength agent, which is applied in the field of super-early-strength mortar, can solve the problems that cannot meet the requirements of early strength, high strength, high fluidity, and slow strength growth, and achieve good fluidity, fast strength growth, and fast setting time. fast effect

Inactive Publication Date: 2015-03-25
苏州大乘环保新材有限公司
View PDF0 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Whether it is an expressway or an urban road, poor road surface will lead to driving safety and traffic accidents, and road surface repair is inevitable. The early-strength mortar used in road surface repair projects now has a maximum strength of about 20MPa in 2 hours, and the strength increases slowly, which cannot meet the early-strength mortar. Requirements for strong, high strength and high fluidity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Super early-strength mortar

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Embodiment one: take each raw material by weight respectively: sulfoaluminate cement 380kg, construction gypsum 80kg, P. 30-mesh aggregate, 188kg of 30-60-mesh aggregate, 47kg of 70-140-mesh aggregate), 0.5kg of tartaric acid, 0.5kg of citric acid, 0.7kg of calcium formate, and 1.6kg of polycarboxylic acid superplasticizer. 0.5kg of PP fibers with a length of 3mm. The above raw materials are added into a dry powder mixer and stirred evenly to obtain the product. Referring to "GBT 2419-2005 Method for Determination of Fluidity of Cement Mortar Sand", the measured initial fluidity of super early strength mortar is 315mm. The compressive strength is measured with reference to "GBT 17671-1999 Cement Mortar Strength Test", the measured compressive strength of super early strength mortar is 34.3MPa in 1h, 47MPa in 2h, 54.7MPa in 4h, and 1d compressive strength It is 65.1MPa, and the 28d compressive strength is 92.6MPa. Its strength increases rapidly. The existing ultra-ea...

Embodiment 2

[0020] Embodiment two: take each raw material by weight respectively: sulfoaluminate cement 300kg, construction gypsum 50kg, P. 0.2kg, calcium formate 1.2kg, naphthalene sulfonate superplasticizer 1.5kg. 0.7 kg of PP fiber with a length of 5 mm, the above raw materials are added into a dry powder mixer and stirred evenly to obtain the product. Referring to "GBT 2419-2005 Method for Determination of Fluidity of Cement Mortar Sand", the measured initial fluidity of super early strength mortar is 290mm. The compressive strength is measured with reference to "GBT 17671-1999 Cement Mortar Strength Test". The measured compressive strength of super early strength mortar is 29.6MPa in 1h, 43.1MPa in 2h, 51.9MPa in 4h, and 51.9MPa in 1d. The strength is 61.1MPa, and the 28d compressive strength is 83.7MPa. Its strength increases rapidly, and its strength is stable in the later stage, and the fluidity of the slurry is good.

[0021] Naphthalene sulfonate high-efficiency water reducer...

Embodiment 3

[0022] Embodiment three: take each raw material by weight respectively: sulfoaluminate cement 340kg, construction gypsum 75kg, P. Calcium formate 1kg, polycarboxylate superplasticizer 1.8 kg. 1 kg of PP fiber with a length of 3 mm, the above raw materials are added into a dry powder mixer and stirred evenly to obtain the product. Referring to "GBT 2419-2005 Method for Determination of Fluidity of Cement Mortar Sand", the measured initial fluidity of super early strength mortar is 330mm. The compressive strength is measured with reference to "GBT 17671-1999 Cement Mortar Strength Test". The measured compressive strength of ultra-early-strength mortar is 32.3MPa in 1h, 46.4MPa in 2h, 52.7MPa in 4h, and 52.7MPa in 1d. The strength is 62.8MPa, and the 28d compressive strength is 89MPa. Its strength increases rapidly. The existing ultra-early-strength mortar has a strength of about 20 MPa after 2 hours. The ultra-early-strength mortar of the present invention can reach a maximum...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses super early-strength mortar. The key point of the technical scheme is that the super early-strength mortar is prepared from the following components in percentage by weight: 40-50% of an inorganic bond material, 1-3% of an enhancer, 45-55% of aggregates, 0.3-1.5% of an early-strength agent, 0.05-0.4% of a retarder, 0.1-0.5% of a water reducer and 0.03-0.15% of anti-cracking fibers. The invention provides the super early-strength mortar which does not bleed or shrink and is high in liquidity; in addition, the 1h compressive strength can reach 30MPa and the long-term strength is not decreased.

Description

technical field [0001] The invention is a special mortar material developed for highway and urban pavement repair, with fast setting time and high strength. It can be used in emergency repair projects of airports, railways, highways, bridges, etc., as well as in projects such as ultra-fast anchoring of anchor bolts, water interception and leak plugging. Background technique [0002] At present, my country's expressways and urbanization are developing rapidly, and many early-built expressway pavements and urban pavements have appeared potholes. Whether it is an expressway or an urban road, poor road surface will lead to driving safety and traffic accidents, and road surface repair is inevitable. The early-strength mortar used in road surface repair projects now has a maximum strength of about 20MPa in 2 hours, and the strength increases slowly, which cannot meet the early-strength mortar. Strong, high-strength, high-mobility requirements. Contents of the invention [0003...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04
Inventor 杨彰堂单秀军邱峰
Owner 苏州大乘环保新材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com