High-strength semitransparent ceramic sheet and preparation method thereof

A ceramic thin plate, translucent technology, which is applied in the field of building decoration materials, can solve the problems of high maintenance cost and many damages, and achieve the effect of improving the destructive strength and reducing the water absorption rate

Inactive Publication Date: 2015-02-18
FOSHAN HECAI TECH SERVICE
View PDF5 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The use of ceramic thin plates requires high strength and high toughness, while semi-permeable ceramic thin plates have certain disadvantages in this index. In application, there are many damages, and the construction and later maintenance costs are high.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0022] A method for preparing a high-strength translucent ceramic thin plate, comprising the steps of:

[0023] Step 1) Preparation of powder: Weigh various raw materials according to the proportion, then mix them evenly, add water ball mill to make slurry, and then spray dry to make powder;

[0024] Step 2) stamping forming: stamping the powder prepared in step 1) into a slab;

[0025] Step 3) drying and firing: drying the slab produced in step 2) until the moisture content is lower than 0.5%, and firing in a kiln at a firing temperature of 1150°C to 1250°C, and a firing cycle of 90 to 100 minutes;

[0026] Step 4) Polishing processing: polishing and edging the fired product in step 3) to obtain a high-strength translucent ceramic sheet.

[0027] The various raw materials include 20-25% of sodium sand, 15-20% of potassium feldspar, 9-13% of high potassium sand, 20-25% of potassium albite feldspar, 1-3% of barium carbonate, and 12% of calcined kaolin according to the mass per...

Embodiment 1

[0029] A method for preparing a high-strength translucent ceramic thin plate, comprising the steps of:

[0030] Step 1) preparing powder: weighing various raw materials according to the proportioning described in claim 1, then mixing them uniformly, adding water ball mill to make slurry, and then spray drying to make powder;

[0031] Step 2) stamping forming: stamping the powder prepared in step 1) into a slab;

[0032] Step 3) drying and firing: drying the slab made in step 2) until the moisture content is lower than 0.5%, and firing in a kiln at a firing temperature of 1150°C and a firing cycle of 100 minutes;

[0033] Step 4) Polishing processing: polishing and edging the fired product in step 3) to obtain a high-strength translucent ceramic sheet.

[0034] The various raw materials include 20% sodium sand, 18% potassium feldspar, 9% high potassium sand, 22% potassium albite feldspar, 2% barium carbonate, 14% calcined kaolin, 12% bone meal and flaky alumina by mass percent...

Embodiment 2

[0047] A method for preparing a high-strength translucent ceramic thin plate, comprising the steps of:

[0048] Step 1) preparing powder: weighing various raw materials according to the proportioning described in claim 1, then mixing them uniformly, adding water ball mill to make slurry, and then spray drying to make powder;

[0049] Step 2) stamping forming: stamping the powder prepared in step 1) into a slab;

[0050] Step 3) drying and firing: drying the slab made in step 2) until the moisture content is lower than 0.5%, and firing in a kiln at a firing temperature of 1200°C and a firing cycle of 95 minutes;

[0051] Step 4) Polishing processing: polishing and edging the fired product in step 3) to obtain a high-strength translucent ceramic sheet.

[0052]The various raw materials include 25% sodium sand, 15% potassium feldspar, 11% high potassium sand, 20% potassium albite feldspar, 3% barium carbonate, 12% calcined kaolin, 11% bone meal and flaky alumina by mass percenta...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
breaking strengthaaaaaaaaaa
water absorptionaaaaaaaaaa
water absorptionaaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-strength semitransparent ceramic sheet and a preparation method for the high-strength semitransparent ceramic sheet. The high-strength semitransparent ceramic sheet is prepared by sintering the formula components: 20-25% of sodium sand, 15-20% of potassium feldspar, 9-13% of high potassium sand, 20-25% of potassium sodium feldspar, 1-3% of barium carbonate, 12-15% of calcined kaolin, 5-15% of bone meal, and 1-3% of sheet aluminum oxide in percentage by weight at high temperature. The preparation method comprises the following steps: (1) preparing powder; (2) forming by punching; (3) drying and sintering; (4) polishing to make the high-strength semitransparent ceramic sheet. Sheet aluminum oxide particles are added in an original semitransparent ceramic material, an inorganic peroxide crystal whisker is further added, the water absorption of the semitransparent ceramic material is reduced, the breaking strength is improved, and then the semitransparent ceramic material is applied in the ceramic sheet, so that the water absorption of the ceramic sheet is reduced, and the breaking strength of the ceramic sheet is improved.

Description

technical field [0001] The invention relates to the technical field of building decoration materials, in particular to a high-strength translucent ceramic thin plate and a preparation method thereof. Background technique [0002] In the modern building decoration industry, with the industrialization of housing and the improvement of people's living standards, the market share of high-quality, multi-functional green building material products will gradually expand, and the product development tends to be diversified, personalized, fashionable, environmentally friendly and healthy change. In order to meet the requirements of people in today's society, various new decoration materials have emerged as the times require, and the products have become more and more natural, elegant and individual elements from the gorgeous decoration effect in the early days to today. [0003] There are many varieties of ceramic products, rich designs and colors, good decorative effects, easy main...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/16C04B35/81C04B35/622
CPCC04B35/16C04B35/80C04B2235/3215C04B2235/3217C04B2235/3427C04B2235/3472C04B2235/349C04B2235/447C04B2235/5276C04B2235/9653
Inventor 周克芳陈海云朱丽萍黎娟刘江锋
Owner FOSHAN HECAI TECH SERVICE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com