Liquid crystal alignment agent, liquid crystal alignment film and liquid crystal display element

A technology of liquid crystal alignment agent and amine compound, which is applied in liquid crystal materials, instruments, optics, etc., and can solve problems such as poor printability for a long time

Inactive Publication Date: 2014-12-03
CHI MEI CORP
View PDF8 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] Therefore, one aspect of the present invention is to provide a liquid crystal alignment agent, which includes a polymer composition (A) and a solvent (B), and this liquid crystal alignment agent can improve the shortcoming of poor printability for a long time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Liquid crystal alignment agent, liquid crystal alignment film and liquid crystal display element
  • Liquid crystal alignment agent, liquid crystal alignment film and liquid crystal display element
  • Liquid crystal alignment agent, liquid crystal alignment film and liquid crystal display element

Examples

Experimental program
Comparison scheme
Effect test

Synthetic example A-1-1

[0143] A nitrogen inlet, a stirrer, a condenser, and a thermometer are arranged on a four-necked conical flask with a volume of 500 milliliters, and nitrogen is introduced. Then, add the diamine compound ( b-2-1), 4.05 grams (0.0375 moles) of p-phenylenediamine (b-3-1) and 80 grams of N-methyl-2-pyrrolidone (hereinafter referred to as NMP), and stirred at room temperature until dissolve. Next, 10.91 g (0.05 mol) of pyromellitic dianhydride (a-1) and 20 g of NMP were added, and reacted at room temperature for 2 hours. After the reaction, the reaction solution was poured into 1500 ml of water to precipitate the polymer, and the obtained polymer was filtered, and the steps of washing and filtering were repeated three times with methanol. Afterwards, the product was placed in a vacuum oven and dried at a temperature of 60° C. to obtain the polymer composition (A-1-1). Table 1 shows the results of evaluating the imidation rate of the obtained polymer composition (A-1-1) in the f...

Synthetic example A-2-1

[0147]A nitrogen inlet, a stirrer, a heater, a condenser tube and a thermometer are arranged on a four-neck conical flask with a capacity of 500 milliliters, and nitrogen is introduced. Then, add the diamine compound ( b-2-1), 4.05 g (0.0375 mol) of p-phenylenediamine (b-3-1) and 80 g of NMP, and stirred at room temperature until dissolved. Next, 10.91 g (0.05 mol) of pyromellitic dianhydride (a-1) and 20 g of NMP were added. After reacting at room temperature for 6 hours, 97 g of NMP, 2.55 g of acetic anhydride, and 19.75 g of pyridine were added, the temperature was raised to 60° C., and stirring was continued for 2 hours to carry out imidization reaction. After the reaction, the reaction solution was poured into 1500 ml of water to precipitate the polymer, and the obtained polymer was filtered, and the steps of washing and filtering were repeated three times with methanol. Afterwards, the product was placed in a vacuum oven and dried at a temperature of 60° C. to obtain t...

Embodiment 1

[0153] Add 100 parts by weight of polymer (A-1-1) to 1200 parts by weight of N-methyl-2-pyrrolidone (hereinafter referred to as B-1) and 600 parts by weight of ethylene glycol n-butyl ether (hereinafter referred to as In B-2), at room temperature, the liquid crystal alignment agent of Example 1 can be obtained by continuously stirring with a stirring device until dissolved. The obtained liquid crystal alignment agent was evaluated by the following evaluation methods, and the results are shown in Table 3, and the detection method of long-term printability will be described later.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to a liquid crystal alignment agent, a liquid crystal alignment film made by the liquid crystal alignment agent and a liquid crystal display element having the liquid crystal alignment film. The liquid crystal alignment agent includes a polymer composition (A) and a solvent (B). The polymer composition (A) is synthesized by reacting a mixture that includes a tetracarboxylic dianhydride component (a) and a diamine component (b). The aforementioned liquid crystal alignment agent has a better long-term printability.

Description

technical field [0001] The present invention relates to a liquid crystal alignment agent, a liquid crystal alignment film and a liquid crystal display element, in particular to provide a liquid crystal alignment agent with good long-term printability, a liquid crystal alignment film formed by using the liquid crystal alignment agent, and a liquid crystal alignment film with the liquid crystal alignment film liquid crystal display elements. Background technique [0002] In recent years, due to the increasing requirements of consumers on the wide viewing angle characteristics of liquid crystal displays year by year, the requirements on the electrical characteristics or display characteristics of wide viewing angle liquid crystal display elements have become more stringent than before. Among the liquid crystal display elements with a wide viewing angle, vertical alignment liquid crystal display elements are most commonly studied. Therefore, in order to have better electrical p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09K19/56G02F1/1337C08G73/10
CPCG02F1/133723G02F1/1393G02F1/133742
Inventor 蔡宗沛
Owner CHI MEI CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com