Scrub-resistant doodle-resistant powder paint and preparation method thereof

A powder coating and anti-graffiti technology, applied in the field of coatings, can solve the problems of cost, huge graffiti removal, affecting city appearance and landscape, etc., and achieves the effect of simple formula and excellent chemical resistance

Inactive Publication Date: 2014-11-19
ANHUI HUAHUI SUYE TECH SHARE CO LTD
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the loss caused by malicious graffiti has attracted more and more people's attention. It not only affects the city appearance and landscape, but also causes huge costs in removing graffiti

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Scrub-resistant doodle-resistant powder paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0029] A scrub-resistant, graffiti-resistant powder coating, which is made from the following raw materials in parts by weight:

[0030] Hydroxyl resin (hydroxyl value 100mg KOH / g) 50

[0031] Isocyanate 20

[0032] Barium sulfate 25

[0033] Acrylic leveling agent 1.0

[0034] Low surface tension additive 1.0

[0035] Benzoin 0.5

[0036] Antistatic agent 0.5

[0037] Pigment 2.0

[0038] The preparation method of above-mentioned scrub resistance, anti-graffiti powder coating, comprises the following steps:

[0039] (1) All materials are weighed according to the ratio, placed in a high-speed mixer, and mixed for 2 minutes;

[0040] (2) The twin-screw foundation is adopted, the screw arrangement is a standard arrangement, and the extrusion temperature is controlled at 90 o around C;

[0041] (3) The extruded tablet is crushed to 40um particles;

[0042] (4) Particles are sieved with 180 mesh and packed for later use.

example 2

[0044] A scrub-resistant, graffiti-resistant powder coating, which is made from the following raw materials in parts by weight:

[0045] Hydroxyl resin (hydroxyl value 300mg KOH / g) 35

[0046] Isocyanate 35

[0047] Titanium dioxide 1.0

[0048] Barium sulfate 25

[0049] Ether leveling agent 1.0

[0050] Low surface tension additive 1.2

[0051] Benzoin 0.5

[0052] Antistatic agent 0.8

[0053] Pigment 0.5.

[0054] The preparation method of above-mentioned scrub resistance, anti-graffiti powder coating, comprises the following steps:

[0055] (1) All materials are weighed according to the ratio, placed in a high-speed mixer, and mixed for 2 minutes;

[0056] (2) The twin-screw foundation is adopted, the screw arrangement is a standard arrangement, and the extrusion temperature is controlled at 85 o around C;

[0057] (3) The extruded tablet is crushed to 40um particles;

[0058] (4) Particles are sieved with 200 meshes and packaged for later use.

[0059] The po...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hydroxyl valueaaaaaaaaaa
Login to View More

Abstract

The invention discloses a scrub-resistant doodle-resistant powder paint which is prepared from the following raw materials in parts by weight: 35-60 parts of hydroxy resin, 20-50 parts of isocyanate, 20-40 parts of inorganic filler, 1-1.5 parts of leveling agent, 0.3-1 part of low-surface-tension assistant, 0.5-0.8 part of benzoin, 0.3-1.0 part of antistatic agent and 0.1-5 parts of pigment. The coated film formed by the paint is imporous and can prevent the paint from permeate into the coating. The product has the advantages of simple formula, excellent chemical resistance, scrub resistance, repeated doodle resistance and the like.

Description

technical field [0001] The invention relates to the field of coatings, in particular to a wipe-resistant and anti-graffiti powder coating and a preparation method thereof. Background technique [0002] At present, more and more people pay more and more attention to the loss caused by malicious graffiti. It not only affects the city appearance and landscape, but also causes huge costs in removing graffiti. It is relatively difficult to reduce the amount of graffiti, so it is of great significance to develop coatings with anti-graffiti properties. Among them, the anti-graffiti powder coating has the advantages of long-lasting wear resistance, easy cleaning of graffiti, cost saving, low pollution, and high product utilization rate, and the production and coating process can achieve zero VOC emissions. Therefore, it has a wide range of applications and industries. prospect. Contents of the invention [0003] The object of the present invention is to provide a kind of anti-sc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04C09D5/03C09D7/12
Inventor 刘荣兴丁运生费邦忠
Owner ANHUI HUAHUI SUYE TECH SHARE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com