Oil-soluble polyether oil for screw-type air compressor

An air compressor oil and oil-soluble polyether technology, applied in the field of lubricating oil, can solve the problems of increased oil consumption, oil film damage, shortened service life of parts, etc., and achieve excellent anti-oxidation stability, excellent viscosity-temperature performance, good The effect of defoaming

Inactive Publication Date: 2014-11-05
张家港市胜宇石油化工制品有限公司
View PDF3 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Lubricating oil with too low viscosity is not easy to form a strong enough oil film, which will accelerate wear and shorten the service life of parts
On the contrary, if the viscosity of the lubricating oil is too high, it will increase the internal friction force, increase the specific power of the compressor, and increase the power consumption and oil consumption. Formation of sediment
Compressor oil is prone to emulsification during operation, resulting in unclear separation of oil and gas and increased oil consumption. At the same time, the oil is emulsified to damage the oil film, which will cause increased wear

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Oil-soluble polyether oil for screw-type air compressor
  • Oil-soluble polyether oil for screw-type air compressor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Take 40 parts of oil-soluble polyether (OSP) base oil and 55 parts of polyalphaolefin (PAO) into a stainless steel mixing kettle with agitator, keep the temperature of the kettle at 60 ° C, and continue stirring for 0.5 hours; sequentially add 0.5 parts Alkylated diphenylamine, 0.9 parts of boric acid ester anti-oxidant and anti-wear agent, 0.4 part of high-temperature ashless anti-wear agent; 0.5 part of sorbitol fatty acid ester; 0.05 part of benzotriazole derivatives; 0.01 part of acrylate and ether The copolymer was added into the blending kettle, and the temperature of the kettle was maintained at 65°C, and the mixture was continuously stirred for 1 hour until the mixture was completely dissolved and became uniform, and the refined oil was obtained.

Embodiment 2

[0025] Take 30 parts of oil-soluble polyether (OSP) base oil and 67.09 parts of polyalphaolefin (PAO) and add them into a stainless steel mixing tank with agitator for reaction, keep the temperature of the tank at 60 ° C, and continue stirring for 0.5 hours; Alkylated diphenylamine, 0.6 part of borate antioxidant, 0.6 part of high temperature ashless antiwear agent; 0.8 part of sorbitol fatty acid ester; 0.5 part of polyalphaolefin pour point depressant; 0.01 part of copolymerization of acrylate and ether Add the mixture into the blending kettle, keep the temperature of the kettle at 65°C, and stir continuously for 1 hour until the mixture is completely dissolved and becomes uniform, and the refined oil is obtained.

Embodiment 3

[0027] Take 39.8 parts of polyalphaolefin (PAO) with a viscosity of 46 centistokes (cSt), 26.65 parts of polyalphaolefin (PAO) with a viscosity of 68 centistokes (cSt), and 30 parts of polyether base oil into the belt stirring The stainless steel of the device adjusts the reaction in the kettle, maintains the temperature of the kettle at 60°C, and continuously stirs for 0.5 hours; sequentially add 0.5 parts of alkylated diphenylamine, 0.75 parts of borate antioxidant, 0.8 parts of high-temperature ashless anti-wear agent; 0.95 parts Sorbitol fatty acid ester; 0.5 part of polyalphaolefin pour point depressant; 0.01 part of copolymer of acrylate and ether is added to the blending kettle, and the temperature of the kettle is maintained at 60°C, and the stirring is continued for 1 hour until the mixture is completely dissolved and becomes uniform , to get refined oil.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses oil-soluble polyether oil for a screw-type air compressor. The oil-soluble polyether oil is prepared from 20-40 parts or 10-20 parts by mass of oil-soluble polyether base oil, 60-80 parts or 80-90 parts by mass of poly(alpha-olefin), 0.1-1.4 parts by mass of benzenamine, 0.8-2 parts by mass of a borate anti-oxidant, 1.2-2.2 parts by mass of a high-temperature ashless antiwear agent, 0.5-1.8 parts by mass of polyoxyethylene sorbitan fatty acid ester and 0.001-0.05 parts by mass of an acrylate-ether copolymer. The oil-soluble polyether oil for a screw-type air compressor is environmentally friendly, has the advantages of excellent antioxidation stability, emulsification resistance, corrosion and rusting resistance, very good defoaming performance and excellent viscosity-temperature performance, has performance indexes satisfying standards of air compressor oil 46 and can be used for mechanical equipment of an air compressor system.

Description

technical field [0001] The invention belongs to the technical field of lubricating oil, in particular to a screw air compressor oil which is compatible with mineral oil and synthetic hydrocarbon and has biodegradability. Background technique [0002] Air compressor oil is mainly used for the lubrication of the moving parts of the compressor cylinder and the exhaust valve, and plays the role of anti-rust, anti-corrosion, sealing and cooling. Since the compressor is always in an environment of high pressure, high temperature and condensed water (for air compressors), the air compressor oil should have excellent high temperature oxidation stability, low carbon deposition tendency, suitable viscosity and viscosity temperature Performance and good oil-water separation, anti-rust and anti-corrosion properties, etc. Lubricating oil with too low viscosity is not easy to form a strong enough oil film, which will accelerate wear and shorten the service life of parts. On the contrary...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10M169/04C10N30/12C10N30/18C10N30/10
Inventor 黄红袁卫华
Owner 张家港市胜宇石油化工制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com