Wear-resistant sliding plate surface and processing method

A board surface and skateboard technology, applied in chemical instruments and methods, synthetic resin layered products, layered products, etc., can solve the problem that the bottom is not reinforced, and achieves reduction of gluing processes, high efficiency, and high mechanical strength. Effect

Active Publication Date: 2014-10-15
SHANGHAI GENIUS ADVANCED MATERIAL (GRP) CO LTD
View PDF9 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There are also some products that use the top-layer glass fiber reinforcement technology to greatly increase the toughness and strength of the board surface. However, in the design and lay-up process of the skateboard surface, since the top layer is laid with glass fiber, this design has no effect on the bottom of the board surface that is prone to fracture. Doing good enhancements is a design flaw

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wear-resistant sliding plate surface and processing method
  • Wear-resistant sliding plate surface and processing method
  • Wear-resistant sliding plate surface and processing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] The skateboard surface is composed of a prepreg layer and a polyurethane layer. The prepreg layer is formed by laying 100 parts of unidirectional prepreg tape of glass fiber reinforced thermoplastic resin composite material. The polyurethane layer is 5 parts of sheet thermoplastic polyurethane. Its preparation method comprises the following steps:

[0050] (1) Take glass fiber reinforced thermoplastic resin composite unidirectional prepreg tape, as shown in Figure 1, including 35 parts of polypropylene, 65 parts of glass fiber, and its density is 1.57g / cm 3 , the single layer thickness of the prepreg tape is 0.25mm;

[0051] Take 15 layers of fabrics for laying, of which 1, 3, 5, 7, 9, 11, 13, and 15 layers are all in the direction of 0 degrees, and 2, 4, 6, 8, 10, 12, and 14 layers are laid The direction is 90 degrees, and the total thickness is 3.75mm, as shown in Figure 2(a) and 2(b);

[0052] (2) Take polyurethane material film, its content is 5 parts, its shape i...

Embodiment 2

[0057] The skateboard surface is composed of a prepreg layer and a polyurethane layer. The prepreg layer is formed by laminating 100 parts of glass fiber reinforced thermoplastic resin composite material unidirectional prepreg tape. The polyurethane layer is 7 parts of sheet thermoplastic polyurethane. Its preparation method comprises the following steps:

[0058] (1) Take glass fiber reinforced thermoplastic resin composite unidirectional prepreg tape, as shown in Figure 1, including 40 parts of polylactic acid and 60 parts of glass fiber, and its density is 1.54g / cm 3 , the single layer thickness of the prepreg tape is 0.4mm;

[0059] Take 17 layers of fabrics for laying, of which 1, 3, 5, 7, 9, 11, 13, 15, and 17 layers are all in the direction of 0 degrees, 2, 4, 6, 8, 10, 12, 14, 16 The laying direction is 90 degrees, and the total thickness is 6.8mm, as shown in Figure 2(a) and 2(b);

[0060] (2) Take the polyurethane material film, the content is 7 parts, the shape is...

Embodiment 3

[0065] The skateboard surface is composed of a prepreg layer and a polyurethane layer. The prepreg layer is formed by laying 100 parts of glass fiber reinforced thermoplastic resin composite material unidirectional prepreg tape. The polyurethane layer is 8 parts of sheet thermoplastic polyurethane. Its preparation method comprises the following steps:

[0066] (1) Take glass fiber reinforced thermoplastic resin composite unidirectional prepreg tape, as shown in Figure 1, in which polyethylene is 45 parts, glass fiber is 55 parts, and its density is 1.41g / cm 3 , the single layer thickness of the prepreg tape is 0.3mm;

[0067] Take 19 layers of fabrics for laying, of which 1, 3, 5, 7, 9, 11, 13, 15, 17, and 19 layers are all in the direction of 0 degrees, 2, 4, 6, 8, 10, 12, 14, 16, 18 are laid in a 90-degree direction with a total thickness of 5.7mm, as shown in Figures 2(a) and 2(b);

[0068] (2) Take the polyurethane material film, its content is 8 parts, its shape is a se...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Densityaaaaaaaaaa
Densityaaaaaaaaaa
Densityaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of processing technology of composite materials and relates to a sliding plate surface and a manufacturing method thereof. The sliding plate surface is composed of a prepreg strip layer and a polyurethane layer. The prepreg strip layer is formed by 100 parts of a glass fiber reinforced thermoplastic resin composite material single-direction prepreg strip in a laminated manner. The polyurethane layer is formed by 5-10 parts of sheet-shaped thermoplastic polyurethane. A sliding plate material manufactured by means of the method in the invention is improved in a water-resistant performance and is not easy to warp and peel after being contacted with water. The manufacturing method is completely free of glue and a glue-coating process is reduced so that pollution during a processing process is reduced. In addition, the sliding plate surface, which is manufactured from the glass fiber reinforced thermoplastic composite material is thinner and is higher in strength.

Description

technical field [0001] The invention belongs to the technical field of composite material processing, and relates to a skateboard surface and a preparation method thereof. Background technique [0002] Commercially available skateboards are mainly made of wooden materials. The advantages of Canadian maple wood mainly lie in the hard texture of the material, compact wood, good polishing, and moderate strength. The skateboard surface processed with this wood has good elasticity and high strength. However, skaters require lighter, thinner, and stronger boards, and if improvements are still made on the basis of existing materials, it will lead to weakening of the strength and elasticity of skateboards, so many merchants turn their attention to alternatives to wood. on the material. [0003] At present, many brands produce fiber optic decks. The so-called fiber optic decks are reinforced with glass fibers. The main purpose is to improve the strength and elasticity of skateboard ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B32B27/08B32B27/32B32B27/34B32B27/36B32B27/40B32B17/04C08L23/06C08L23/12C08L23/08C08L77/00C08L59/00C08L67/04C08L67/02C08L69/00C08K7/14
Inventor 杨桂生刘密密
Owner SHANGHAI GENIUS ADVANCED MATERIAL (GRP) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com