A kind of hydrostone ceramic ball and preparation method thereof

A technology of water protolith and ceramic balls, applied in the field of shuiyuanshi ceramic balls and their preparation, to achieve the effects of reducing blood lipids, replenishing energy, and eliminating peculiar smells

Active Publication Date: 2015-08-19
徐州雅居乐环保科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there is no report about the hydrostone ceramic ball in the market

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A ceramic ball of water element stone, made of the following weight (kg) raw materials: water element stone 80, green life stone 45, garnet 20, carbon stone fiber 10, rectorite 24, diatomite 18, illite 14-22, ochre 12, goose tube stone 10, nano silver carbon molecular sieve 7, blue stone 15, natural manganese sand 25, titanium dioxide 5.

[0018] The preparation method of water element stone ceramic ball includes the following steps:

[0019] (1) Mix green lifestone, garnet, diatomaceous earth and illite evenly, calcined at 720°C for 3h, take it out and cool to below 50°C at 2°C, smash after cooling, pass through a 100 mesh sieve, dry, and set aside ;

[0020] (2) Mix water element stone, rectorite and natural manganese sand evenly, crush, pass through a 300-mesh sieve, add hydrogen peroxide to make a slurry with a concentration of 45, grind it at high speed until the slurry particle size reaches 15μm, and spray dry it into a powder ,stand-by;

[0021] (3)...

Embodiment 2

[0024] A ceramic ball of water element stone, made of the following weight (kg) raw materials: water element stone 90, green life stone 55, garnet 30, carbon fiber 12, rectorite 32, diatomite 22, illite 18, ochre 16, goose tube stone 12, nano silver carbon molecular sieve 11, bluestone 18, natural manganese sand 35, titanium dioxide 8.

[0025] The preparation method of water element stone ceramic ball includes the following steps:

[0026] (1) Mix green lifestone, garnet, diatomaceous earth, and illite evenly, calcined at 740°C for 2.5h, take it out and cool to below 50°C at 3°C, pulverize after cooling, pass through a 150-mesh sieve, and dry. use;

[0027] (2) Mix the water element stone, rectorite and natural manganese sand evenly, crush them, pass through a 350-mesh sieve, add hydrogen peroxide to make a slurry with a concentration of 50%, grind it at high speed to a slurry particle size of 20μm, and spray dry it into a slurry Powder, ready to use;

[0028] (...

Embodiment 3

[0031] A kind of water element stone ceramic ball, made from the following weight (kg) raw materials: water element stone 100, green life stone 65, garnet 40, carbon fiber 15, rectorite 36, diatomite 26, illite 22. Ochre 18, Goose Tube Stone 15, Nano Silver Carbon Molecular Sieve 14, Bluestone 20, Natural Manganese Sand 45, Titanium Dioxide 10.

[0032] The preparation method of water element stone ceramic ball includes the following steps:

[0033] (1) Mix green lifestone, garnet, diatomaceous earth, and illite uniformly, calcinate at 760°C for 2h, take it out and cool to below 50°C at 5°C, pulverize after cooling, pass through a 150 mesh sieve, dry, and set aside ;

[0034] (2) Mix water element stone, rectorite and natural manganese sand evenly, crush, pass through a 400-mesh sieve, add hydrogen peroxide to make a slurry with a concentration of 55%, grind it at high speed to a slurry particle size of 25μm, and spray dry it into Powder, ready to use;

[0035] (...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a water element stone ceramic ball and preparing method thereof. The water element stone ceramic ball is prepared from the following raw materials in parts by weight: 80-100 parts of water element stones, 45-65 parts of green stones, 20-40 parts of garnet, 10-15 parts of carbon stone fiber, 24-36 parts of rectorite, 18-26 parts of diatomite, 14-22 parts of illite, 12-18 parts of ocher, 10-15 parts of Balanophyllia sp, 7-14 parts of nano silver carbon molecular sieves, 15-20 parts of green frontiers stones, 25-45 parts of natural manganese sands and 5-10 parts of titanium dioxide. After being processed by the water element stone ceramic ball, drinking water is weakly alkaline in water quality with small molecules and negative potential, rich in oxygen, minerals and trace elements needed by the body, and beneficial to human health; the water element stone ceramic ball has the functions of killing bacteria and viruses in the drinking water, eliminating odors and adsorbing harmful substances of chlorine dioxide, heavy metals and the like, so as to ensure the good quality of the drinking water.

Description

Technical field [0001] The invention relates to a water element stone ceramic ball and a preparation method thereof, and belongs to the field of ceramic materials. Background technique [0002] Water element stone, geological type belongs to iron dolomite, also known as wood grain stone, is a precious natural ore rich in many rare elements, formed in the geological age of the mid-Cambrian about 570 million years ago, in shallow sea A precious mineral resource formed by chemical deposition. The unique natural circulating magnetic field of Shuiyuan Stone can change the structure of water molecules, which can instantly improve the water quality of ordinary drinking water and turn ordinary drinking water into active water beneficial to human health. Therefore, the development of a ceramic ball of water element is of great significance for water treatment. However, there is no report on the ceramic ball of water element on the market. Summary of the invention [0003] The purpose of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/00C04B35/622
Inventor 任新年任浩楠黄冉
Owner 徐州雅居乐环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com