Environmental-protection coating and preparation method
An environmentally friendly paint and paint technology, applied in the direction of coating, etc., can solve the problems of moldy spots on the wall, no clear instructions, paint falling off, etc., and achieve good anti-static effect, improved leveling performance, and fresh smell Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0024] Add 270kg of water, 2kg of alkaloid composition, 2kg of D-504 wetting agent, 5kg of dispersant, and 3kg of defoamer into the reactor, and disperse for 20-40 minutes at a speed of 700-900 rpm; Then add 220kg of titanium dioxide, 60kg of talcum powder, 50kg of decolorized seaweed mud powder, 50kg of beef bone powder, 50kg of shell powder, and 40kg of medical stone powder, and stir for 20-30 minutes at a speed of 500-1200 rpm , through sand milling until the fineness of the material is below 50um; then add 230kg of pure acrylic acid emulsion, 25kg of vegetable gum composition, 20kg of glycerin, 3kg of 95% ethanol, 2kg of defoamer, and 4kg of Sophora japonica extract to the reactor, Stir for 20-30 minutes at a rotation speed of 400-800 rpm; finally adjust the viscosity with 10kg of vegetable gum composition and 80kg of water so that the viscosity at room temperature is (90-110) KU, passing through 200 mesh After sieving, it is a qualified product, which is packaged and pres...
Embodiment 2
[0029] Add 150.8kg of water, 1.2kg of alkaloid composition, 3kg of D-504 wetting agent, 4.23kg of dispersant, and 2kg of defoamer into the reactor, and disperse 20- 40 minutes; then add 250kg of titanium dioxide, 80kg of talc powder, 30.2kg of decolorized seaweed mud powder, 70kg of bovine bone powder, 30kg of shell powder, and 50kg of medical stone powder, and stir at a speed of 500-1200 rpm After 20-30 minutes, sand mill until the fineness of the material is below 50um; then add 250kg of pure acrylic acid emulsion, 10.2kg of vegetable gum composition, 15kg of glycerin, 2kg of 95% ethanol, 2kg of defoamer, and 3kg of Sophora japonica extract to In the reaction kettle, stir for 20-30 minutes at a speed of 400-800 rpm; finally adjust the viscosity with 10.2kg of vegetable gum composition and 50kg of water so that the viscosity at normal temperature is (90-110 ) KU, after passing through a 200-mesh sieve, it is a qualified product, which is packaged and preserved.
[0030] Prep...
Embodiment 3
[0034] Add 200kg of water, 3kg of alkaloid composition, 1kg of D-504 wetting agent, 6kg of dispersant, and 3kg of defoamer into the reactor, and disperse for 20-40 minutes at a speed of 700-900 rpm; Then add 200kg of titanium dioxide, 40kg of talcum powder, 70kg of decolorized seaweed mud powder, 30.1kg of beef bone powder, 70kg of shell powder, and 30kg of medical stone powder, and stir for 20-30 minutes at a speed of 500-1200 rpm. Minutes, sand milling until the fineness of the material is below 50um; then add 200kg of pure acrylic emulsion, 30kg of vegetable gum composition, 30kg of glycerin, 4kg of 95% ethanol, 3kg of defoaming agent, and 2kg of Sophora japonica extract to the reactor, Stir for 20-30 minutes at a rotational speed of 400-800 rpm; finally adjust the viscosity with 20.1kg of vegetable gum composition and 100kg of water so that the viscosity at normal temperature is (90-110) KU, over 200-mesh sieve is a qualified product, which is packaged and preserved.
[0...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com