Flame-retardant knitted fabric

A technology for knitted fabrics and fabrics, applied in the direction of fabrics, textiles, textiles and papermaking, can solve the problems of unsatisfactory flame retardant effect and uncomfortable hand feeling, and achieve the effect of firm adhesion, comfortable hand feeling and quality reduction

Inactive Publication Date: 2014-09-17
JIANGSU JINHONG KNITTING
View PDF8 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The flame retardant effect of the current knitted fabric is not very ideal, and the fabric with better flame retardant performance is not very comfortable to the touch.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] A flame-retardant knitted fabric, the warp of the fabric is DTY 150D / 48F, and the weft is ATY 320D / 96F;

[0014] The fabric is soaked in an impregnation solution containing 40% composite flame retardant at 75°C for 6 hours, and then kept at 160°C for 7 hours after taking it out;

[0015] The composite flame retardant is prepared by the following method: 3 parts of carboxymethyl cellulose, 5 parts of vinyl trimethoxysilane, 9 parts of tetrakis hydroxymethyl phosphine chloride, 2 parts of phosphite, 4 parts of ethyl trimethoxy Ethoxysilane is mixed, and then 8 parts of cyclic phosphonate and 7 parts of molybdenum trioxide are slowly added at the same time, and the feeding is completed within 10 minutes, and the mixing is continued for 15 minutes to obtain a composite flame retardant.

Embodiment 2

[0017] A flame-retardant knitted fabric, the warp of the fabric is DTY 150D / 48F, and the weft is ATY 320D / 96F;

[0018] The fabric is immersed in an impregnating solution containing 35-40% composite flame retardant at 70-75°C for 5-6 hours, and after taking it out, it is kept at a constant temperature of 155-160°C for 5-7 hours;

[0019] The composite flame retardant is prepared by the following method: 2 parts of carboxymethyl cellulose, 4 parts of vinyl trimethoxysilane, 8 parts of tetrakis hydroxymethyl phosphine chloride, 1 part of phosphite, 3 parts of ethyl trimethoxysilane Ethoxysilane is mixed, and then 7 parts of cyclic phosphonate and 6 parts of molybdenum trioxide are slowly added at the same time, and the feeding is completed within 8 minutes, and the mixing is continued for 10 minutes to obtain a composite flame retardant.

Embodiment 3

[0021] A flame-retardant knitted fabric, the warp of the fabric is DTY 150D / 48F, and the weft is ATY 320D / 96F;

[0022] The fabric is immersed in an impregnating solution containing 37% composite flame retardant at 73°C for 5.5 hours, and after taking it out, keep the temperature at 158°C for 6 hours;

[0023] The composite flame retardant is prepared by the following method: 2.3 parts of carboxymethyl cellulose, 4.5 parts of vinyl trimethoxysilane, 8.9 parts of tetrakis hydroxymethyl phosphine chloride, 1.2 parts of phosphite, 3.4 parts of ethyl trimethoxysilane Ethoxysilane was mixed, and then 7.8 parts of cyclic phosphonate and 6.7 parts of molybdenum trioxide were slowly added at the same time, and the feeding was completed within 9 minutes, and the mixing was continued for 14 minutes to obtain a composite flame retardant.

[0024] The flame retardant slice test report of the flame retardant knitted fabric of the present invention is shown in Table 1.

[0025] Table 1 Fla...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a flame-retardant knitted fabric. The warp of the fabric is DTY150D / 48F, and the weft of the fabric is ATY320D / 96F; the fabric is soaked in steeping liquid containing 35%-40% composite finishing agent at the temperature ranging from 70 DEG C to 75 DEG C for five hours to six hours and then is placed at the constant temperature ranging from 155 DEG C to 160 DEG C for five hours to seven hours after being taken out. The composite finishing agent is prepared with the following methods that 2 parts to 3 parts of carboxymethyl cellulose, 4 parts to 5 parts of vinyl trimethoxy silane, 8 parts to 9 parts of tetrakis hydroxymethyl phosphonium chloride, 1 part to 2 parts of phosphorous ester and three parts to four parts of triethoxy ethyl silane are mixed, then, 7 parts to 8 parts of cyclic phosphonate ester and 6 parts to 7 parts of molybdenum trioxide are synchronously and slowly added, material feeding is completed within eight minutes to ten minutes, continuous mixing lasts for ten minutes to fifteen minutes, and the composite flame-retardant agent is prepared. The flame-retardant knitted fabric has excellent flame-retardant performance.

Description

technical field [0001] The invention relates to flame-retardant knitted fabrics. Background technique [0002] The flame retardant effect of the current knitted fabrics is not very ideal, and the fabrics with better flame retardant properties are not very comfortable to the touch. Contents of the invention [0003] The object of the present invention is to provide a flame-retardant knitted fabric, which is comfortable to the touch and has excellent flame-retardant properties. [0004] In order to achieve the above purpose, the technical solution of the present invention is to design a flame-retardant knitted fabric, the warp of the fabric is DTY 150D / 48F, and the weft is ATY 320D / 96F; [0005] The fabric is immersed in an impregnating solution containing 35-40% composite flame retardant at 70-75°C for 5-6 hours, and after taking it out, it is kept at a constant temperature of 155-160°C for 5-7 hours; [0006] The composite flame retardant is prepared by the following met...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D03D15/12D06M13/282D06M13/288D06M13/513D06M13/292D06M11/48D06M15/09D03D15/513
Inventor 张惠元
Owner JIANGSU JINHONG KNITTING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com