PVC extrusion column and molding technology thereof

A molding process and column technology, applied in the field of PVC extrusion column and its molding process, can solve the problems of easy falling off of the coating, non-wear resistance, unsuitable for social development, etc., and achieve the effect of solving serious environmental pollution

Inactive Publication Date: 2014-09-03
CHUZHOU UNIV
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, due to the low surface hardness and non-wear resistance of spray-coated column profiles, the coating is easy to fall off during long-term use, which is not suitable for the needs of social development.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PVC extrusion column and molding technology thereof
  • PVC extrusion column and molding technology thereof
  • PVC extrusion column and molding technology thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] PVC extrusion column raw materials:

[0014]

[0015]

[0016] PVC extrusion column molding process steps:

[0017] (1) Material mixing: weigh according to the above-mentioned components and their contents, add them to the mixer in batches and mix at high temperature, stop stirring when the temperature reaches 125°C, and then put them into a cooling bucket for stirring. Stop stirring when the temperature drops to 40°C, and put the mixed material into the storage barrel;

[0018] (2) Molding process: use a plastic extruder, the barrel temperature is controlled at 165-180°C, the mold temperature is controlled at 175-190°C, the PVC column profile is vacuum shaped and cooled after extrusion, and then cut according to the predetermined length, that is PVC extruded columns are available.

Embodiment 2

[0020] PVC extrusion column raw materials:

[0021]

[0022] PVC extrusion column molding process steps:

[0023] (1) Material mixing: weigh according to the above-mentioned components and their contents, add them to the mixer in batches and mix at high temperature, stop stirring when the temperature reaches 130°C, and then put them into a cooling bucket for stirring. Stop stirring when the temperature drops to 40°C, and put the mixed material into the storage barrel;

[0024] (2) Molding process: use a plastic extruder, the barrel temperature is controlled at 165-180°C, the mold temperature is controlled at 175-190°C, the PVC column profile is vacuum shaped and cooled after extrusion, and then cut according to the predetermined length, that is PVC extruded columns are available.

Embodiment 3

[0026] PVC extrusion column raw materials:

[0027]

[0028]

[0029] PVC extrusion column molding process steps:

[0030] (1) Material mixing: weigh according to the above-mentioned components and their contents, add them to the mixer in batches and mix at high temperature, stop stirring when the temperature reaches 128°C, and then put them into a cooling bucket for stirring. Stop stirring when the temperature drops to 40°C, and put the mixed material into the storage barrel;

[0031] (2) Molding process: use a plastic extruder, the barrel temperature is controlled at 165-180°C, the mold temperature is controlled at 175-190°C, the PVC column profile is vacuum shaped and cooled after extrusion, and then cut according to the predetermined length, that is PVC extruded columns are available.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a PVC extrusion column and a molding technology thereof. The PVC extrusion column comprises the following raw materials in parts by mass: 100 parts of polyvinyl chloride (PVC) resin, 70-110 parts of calcium carbonate (CaCO3), 7-14 parts of a PVC anti-impact processing modifier (ACM), 0.2-0.5 part of polyethylene (PE) wax, 1-3 parts of calcium stearate (Ca(Sa)2), 0.5-1 part of zinc stearate (Zn(St)2), 0.02-0.1 part of organic tin and 0.04-0.08 part of a toner. According to the provided PVC extrusion column and the molding technology thereof, the column extruding molding technology relatively well solves the problems that a sprayed column is server in environment pollution, low in finished-product qualified rate, complex in preparation technology and the like. Additionally, Ca(St)2, Zn(St)2 and organic tin are taken as PVC heat stabilizers, low-price PVC resin and CaCO3 are taken as the main raw materials, and the column extruding molding technology is employed, so that the PVC extrusion column profiles are prepared.

Description

technical field [0001] The invention relates to the field of polymer materials, in particular to a PVC extruded column and a molding process thereof. Background technique [0002] Spray-coated column means that after the column profile is obtained through the extrusion molding process, the surface is sprayed to change its original surface color, roughness, etc. It is called spraying column profile. At present, due to the low surface hardness and non-wear resistance of spray-coated column profiles, the coating is easy to fall off during long-term use, which is not suitable for the needs of social development. Contents of the invention [0003] The purpose of the present invention is to solve the above-mentioned defects in the prior art, and provide a PVC extruded column with low production cost, good mechanical properties and usable performance and its molding process. [0004] A PVC extruded column, its raw materials are calculated in parts by mass, including: [0005] ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08K13/02C08K3/26C08K5/098C08K5/57B29C47/92B29C48/92
CPCB29C47/0004B29C47/0066B29C47/92B29C48/0022B29C48/022B29C48/92B29C2948/92704B29C2948/92895
Inventor 葛秀涛涂前峰王攀鲁兰兰曹旭锋刘自庆黄善辂
Owner CHUZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products