Rubber glove with skin moisturizing function

A rubber glove, functional technology, applied in the field of surgical gloves, can solve the problems of no skin care, no moisturizing, dry skin, etc., to achieve the effect of avoiding allergies, avoiding dry skin, and enhancing safety performance

Inactive Publication Date: 2014-08-13
GUILIN HBM HEALTHCARES
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the various gloves currently used basically only have a protective effect and do not have the effect of maintaining the skin. Moreover, the materials of some gloves, such as nitrile and PVC, are quite different from the human skin environment. Long-term exposure to such materials , can cause mild skin allergies and even inflammation
At present, rubber gloves only play a simple role of isolation and protection for human hands, but do not have the function of moisturizing, so that users are prone to dry skin and chapped skin during use, especially in autumn and winter.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rubber glove with skin moisturizing function
  • Rubber glove with skin moisturizing function
  • Rubber glove with skin moisturizing function

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A kind of rubber glove with moisturizing function, wherein, described rubber latex is made up of following composition, by weight:

[0028]

[0029] The emollient active ingredient consists of pomegranate seed extract and centella asiatica extract in a weight ratio of 1:2.

[0030] Its preparation method is as follows:

[0031] A. Prepare the rubber latex for impregnation, fully mix natural rubber, emulsified liquid paraffin, colloidal sulfur, zinc oxide, accelerator ZDBC, accelerator ZMBT, and skin-moisturizing active ingredients, and adjust the solid content to 25-32%;

[0032] B, after the mold is dried, impregnate the coagulant first, and the coagulant is calcium nitrate or calcium chloride solution of 15% by weight;

[0033] C. Dry the mold, then dip the mold into the rubber latex prepared above, then crimp, then immerse in warm water at 45°C for 2 minutes, take it out, and dry it at a high temperature of 140°C for 20 minutes;

[0034] D, cool down, take off t...

Embodiment 2

[0036] A kind of rubber glove with moisturizing function, wherein, described rubber latex is made up of following composition, by weight:

[0037]

[0038]

[0039] The emollient active ingredient is composed of pomegranate seed extract and centella asiatica extract in a weight ratio of 3:4.

[0040] Its preparation method is as follows:

[0041] A, prepare the rubber latex that dipping is used, with natural rubber, emulsified liquid paraffin, colloidal sulfur, zinc oxide, promotor ZDBC, promotor ZMBT, emollient active ingredient, fully mix, regulate solid content to be 32%;

[0042] B, after the mold is dried, impregnate the coagulant first, and the coagulant is calcium nitrate or calcium chloride solution of 8% by weight;

[0043] C. Dry the mold, then dip the mold into the rubber latex prepared above, then crimp, then immerse in warm water at 45°C for 2 minutes, take it out, and dry it at high temperature at 120°C for 40 minutes;

[0044] D, cool down, take off the ...

Embodiment 3

[0046] A kind of rubber glove with moisturizing function, wherein, described rubber latex is made up of following composition, preferably, by weight:

[0047]

[0048] The emollient active ingredient is composed of pomegranate seed extract and centella asiatica extract in a weight ratio of 2:3.

[0049] Its preparation method is as follows:

[0050] A, prepare the rubber latex that dipping is used, with natural rubber, emulsified liquid paraffin, colloidal sulfur, zinc oxide, promotor ZDBC, promotor ZMBT, emollient active ingredient, fully mix, and adjust solid content to be 28%;

[0051] B. After the mold is dried, first impregnate the coagulant, which is 10% by weight of calcium nitrate or calcium chloride solution;

[0052] C. Dry the mold, then dip the mold into the rubber latex prepared above, then crimp, then immerse in warm water at 45°C for 2 minutes, take it out, and dry it at a high temperature of 130°C for 30 minutes;

[0053] D, cool down, take off the gloves ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongationaaaaaaaaaa
elongationaaaaaaaaaa
Login to view more

Abstract

The invention discloses a rubber glove with skin moisturizing function, which comprises a rubber latex and a skin moisturizing active component. The rubber glove is characterized in that the rubber latex is composed of the following components in parts by weight: 70-80 parts of natural rubber, 20-30 parts of nitrile-butadiene rubber, 5-8 parts of emulsified liquid paraffin, 0.6-1.2 parts of colloid sulfur, 0.4-1.0 part of zinc oxide, 0.2-0.4 part of accelerator ZDBC, 0.3-0.5 part of accelerator ZMBT and 0.7-1.5 parts of skin moisturizing active component. The skin moisturizing active component is composed of a pomegranate seed extract and a centella extract in a weight ratio of (1-3):(2-4). The skin moisturizing active component is added into the matrix of the operating glove, so that the skin moisturizing active component can moisturize the skin and enhance the safety performance when in use.

Description

technical field [0001] The invention relates to surgical gloves, in particular to a rubber glove with moisturizing function. Background technique [0002] Gloves have been widely used in people's production and life because of their barrier protection and can well protect the safety of users. According to its different uses, it can be divided into medical gloves, industrial gloves and household gloves; according to the different materials used in manufacturing, it can be divided into natural rubber gloves, nitrile gloves, PVC gloves and so on. [0003] However, among the disposable surgical gloves currently used in hospitals, the vast majority are still natural rubber gloves. There are two main reasons for this: 1. The tensile properties and elasticity of nitrile rubber gloves are worse than those of natural rubber latex; the national standard GB7543-2006 "Disposable Sterilized Rubber Surgical Gloves" also stipulates the stretching properties of gloves. Performance require...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08L9/02C08L91/06C08K13/02C08K3/06C08K3/22A61B19/04
Inventor 胡智强
Owner GUILIN HBM HEALTHCARES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap