A kind of mullite liner outer layer for automobile exhaust catalyst and preparation method

A technology of automobile exhaust and mullite, which is applied in the field of refractory and heat insulation materials

Active Publication Date: 2016-02-10
湖州南浔旧馆頔南工程建设有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This patent involves the production and manufacture of mullite fiber, which requires

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0029] A kind of preparation method of the mullite liner outer layer that automobile exhaust catalyst is used as above, this preparation method comprises the steps:

[0030] a) Weigh each raw material according to the proportion, mix it evenly, and obtain the slurry through mixing;

[0031] b) Then, it is formed by suction filtration, and dried at a temperature of 190-210°C for 10 hours to obtain the finished product.

[0032] The performance indicators of the finished product are as follows: linear shrinkage rate -6 / ℃, thermal conductivity from 0.10-0.23w / mk, tensile strength ≥0.35MPa, bulk density from 200-260kg / m 3 , refractoriness > 1800, maximum service temperature > 1500°C, fiber length maintained at 5-9um.

Embodiment 1

[0034] Example 1: Put 100 parts of mullite fiber and 0.5 parts of silane coupling agent KH550 in an industrial mixer, add 120 parts of water, add 5 parts of 5wt% glycerin, and stir the mixture slowly at 100 rpm After 2 hours in the upper layer, add an appropriate amount of boiling water, adjust the water temperature to 40°C, then add 10 parts of epoxy resin, add ammonia water, adjust the pH value to 5, and stir at a medium speed of 500 rpm for 4 hours. Then add tap water to rinse until neutral, filter, and dry in an oven at 80°C. The detection and analysis results before and after modification show that: 72.43wt%Al in the modified mullite fiber 2 o 3 , 25.96%wtSiO 2 , oily substance 1.52wt%; fiber length 8-10um.

[0035] The formula of the outer layer of the liner is 60wt% of modified mullite fiber, 20wt% of calcined alumina powder, 10wt% of silica sol, 1.2wt% of sodium hypochlorite, 7.3wt% of starch, and 1.5wt% of methylcellulose. Mix evenly and knead to obtain a slurry, ...

Embodiment 2

[0036] Example 2: Put 100 parts of mullite fiber and 1 part of silane coupling agent KH560 in an industrial mixer, add 120 parts of water, add 10 parts of 5wt% glycerin, and stir the mixture at a slow speed at 100 rpm After 2 hours in the upper layer, add an appropriate amount of boiling water, adjust the water temperature to 60°C, then add 10 parts of epoxy resin, add ammonia water, adjust the pH value to 6, and stir at a medium speed of 500 rpm for 4 hours. Then add tap water to rinse until neutral, filter, and dry in an oven at 90°C. The detection and analysis results before and after modification show that: 70.12wt%Al in the modified mullite fiber 2 o 3 , 24.14wt% SiO 2 , oily substance 5.74wt%; fiber length 8-12um.

[0037] The formula of the outer layer of the liner is 85% of modified mullite fiber, 5% of calcined alumina micropowder, 3% of silica sol, 3.8% of sodium hypochlorite, 2.7% of starch, and 0.5% of methyl cellulose. Mix evenly and knead to obtain a slurry, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thermal conductivityaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Densityaaaaaaaaaa
Login to view more

Abstract

A mullite liner outer layer for an auto-exhaust catalyst and a preparation method thereof are provided. The mullite liner outer layer is composed of the following components by weight percentage: 60-85% of a modified mullite fiber, 5-10% of a calcined alumina micro-powder, 3-10% of silica sol, 1.2-3.8% of sodium hypochlorite, 2.7-7.3% of starch, and 0.5-1.5% of an additive, wherein the sum of the contents of the components is 100%. The modified mullite fiber comprises the chemical components by weight: not less than 70% of Al2O3, not more than 25% of SiO2, and more than 1.5% of an oily substance, wherein the sum of the contents of the chemical components is 100 wt%. The preparation method comprises the steps: a) weighing the raw materials according to the proportion, mixing evenly, and thus obtaining a slurry through mixing; and b) then carrying out suction filtration molding, and drying at a temperature of 190-210 DEG C for 10 h to obtain the finished product. With utilization of the modified mullite fiber as the main raw material and under a condition of overcoming pulverization, an excellent refractory property of the product is ensured.

Description

technical field [0001] The invention relates to a mullite liner outer layer for automobile exhaust catalysts and a preparation method thereof, belonging to the technical field of fire-resistant and heat-insulating materials. Background technique [0002] With the booming production and sales in China's auto market, there is huge pressure on environmental protection and strong demand for exhaust gas treatment catalysts. Automobile exhaust has become a major mobile pollution source in human society, endangering people's health. Automobile exhaust three-way catalytic converter and EFI closed-loop control are one of the effective measures to solve automobile exhaust pollution. Generally, the three-way catalytic converter for automobile exhaust gas is composed of three-way catalyst, liner, shell and other parts, among which the three-way catalyst plays the role of catalytic purification. With the further improvement of emission standards, the catalyst needs to increase the numb...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/24C04B14/38
Inventor 伊国民
Owner 湖州南浔旧馆頔南工程建设有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap