Method for preparing coal mine filling paste by utilizing waste concrete

A technology for discarding concrete and coal mines, applied in the field of cemented filling materials, can solve the problems of destroying the ecological environment and occupying land, saving energy, reducing filling costs, and reducing bleeding

Active Publication Date: 2014-08-13
TAIYUAN UNIV OF TECH
View PDF5 Cites 27 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide a method for preparing coal mine filling paste with waste concrete as raw material, which can completely recycle the waste concrete without calcination, thus solving the problems of land occupation and ecological environment damage, and at the same time, providing a new environment for coal mines. Filling mining provides sufficient cheap raw materials, reduces filling costs, and lays the foundation for the full implementation of filling mining technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] (1) Collect the abandoned building concrete test blocks in the laboratory, sort and remove metal, wood, plastic and waste concrete contaminated by radioactive and heavy metal harmful substances, and then use the jaw crusher to crush the raw materials to make the crushed particles The diameter is mainly distributed below 15mm, and its raw materials are 100kg waste concrete and 50kg coal gangue, and the weight ratio of the two is 1:0.5;

[0041] (2) Sieve the crushed waste concrete and gangue particles with vibrating sieves with meshes of 1mm, 5mm and 15mm to obtain powders less than 1mm, fine aggregates of 1-5mm, and coarse aggregates of 5-15mm. The 15mm particles are sent back for re-crushing;

[0042] (3) Add fly ash and quicklime and gypsum solids mixed at a ratio of 1:0.5 to the powder obtained in step (2) with a particle size of less than 1mm, stir evenly and send it to a ball mill for ball milling, and ball mill for 15 minutes to obtain a ratio Surface area ≥ 300m...

Embodiment 2

[0046](1) Collect the abandoned building concrete test blocks in the laboratory, sort and remove metal, wood, plastic and waste concrete contaminated by radioactive and heavy metal harmful substances, and then use the jaw crusher to crush the raw materials to make the crushed particles The diameter is mainly distributed below 15mm, and its raw materials are 100kg waste concrete and 25kg coal gangue, and the weight ratio of the two is 1:0.25;

[0047] (2) Sieve the crushed waste concrete and gangue particles with vibrating sieves with meshes of 1mm, 5mm and 15mm to obtain powders less than 1mm, fine aggregates of 1-5mm, and coarse aggregates of 5-15mm. The 15mm particles are sent back for re-crushing;

[0048] (3) Add fly ash and quicklime and gypsum solids mixed at a ratio of 1:0.1 to the powder obtained in step (2) with a particle size of less than 1 mm, stir evenly, and then send it to a ball mill for ball milling for 15 minutes to obtain a ratio Surface area ≥ 300m 2 / kg ...

Embodiment 3

[0052] (1) Collect the abandoned building concrete test blocks in the laboratory, sort and remove metal, wood, plastic and waste concrete contaminated by radioactive and heavy metal harmful substances, and then use the jaw crusher to crush the raw materials to make the crushed particles The diameter is mainly distributed below 15mm, and its raw materials are 100kg waste concrete and 100kg coal gangue, and the weight ratio of the two is 1:1;

[0053] (2) Sieve the crushed waste concrete and gangue particles with vibrating sieves with meshes of 1mm, 5mm and 15mm to obtain powders less than 1mm, fine aggregates of 1-5mm, and coarse aggregates of 5-15mm. The 15mm particles are sent back for re-crushing;

[0054] (3) Add fly ash and quicklime and gypsum solids mixed at a ratio of 1:1 to the powder obtained in step (2) with a particle size of less than 1mm, stir evenly and send it to a ball mill for ball milling, and ball mill for 15 minutes to obtain a ratio Surface area ≥ 300m 2...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing a coal mine filling paste by utilizing waste concrete, and belongs to the technical field of cementation filling materials. The method comprises the steps: crushing the waste concrete and coal gangue, sieving, and allowing to become a powder having the particle size smaller than 1 mm, a fine aggregate with the particle size of 1-5 mm and a coarse aggregate with the particle size of 5-15 mm; then adding an admixture, raw lime and a gypsum solid into the powder with the particle size of less than 1 mm, stirring uniformly, then carrying out ball milling, and thus obtaining an ultrafine powder with the specific surface area of greater than or equal to 300 m<2> / kg; and finally, mixing and stirring cement, the fine aggregate, the coarse aggregate, the ultrafine powder, a conditioning agent and water to obtain the coal mine filling paste. The waste concrete is fully recycled under a condition without calcination, and thus the problems of land occupation and ecological environment destruction are solved, besides, more adequate cheap raw materials are provided for coal mine filling and mining, the filling cost is reduced, and a foundation is laid for full implementation of a filling and mining technology.

Description

technical field [0001] The invention relates to a method for preparing coal mine filling paste by using waste concrete, and belongs to the technical field of cemented filling materials. Background technique [0002] my country is a big country of coal production and consumption. The annual coal production and consumption amount to 100 million tons. Coal accounts for more than 70% of my country's total energy structure. However, my country’s only unified coal mines produce about 13.79 billion tons of coal in the "three lower" mines (buildings, railways, and water bodies), of which 9.468 billion tons of coal are pressed under buildings, accounting for about 69% of the total coal pressure. Seriously restricted the production and development of some mining areas. In addition, a large amount of coal gangue will be produced in the process of coal mine production, which is the largest type of industrial solid waste discharged and stockpiled. The stacking of gangue dumps has occupi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B18/30
CPCY02W30/91
Inventor 冯国瑞贾学强郭育霞戚庭野李典冯佳瑞李振
Owner TAIYUAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com