Marine water-based damping coating and preparation method thereof

A damping coating, water-based technology, applied in the coating and other directions, can solve the problems of poor flame retardancy and long drying time, and achieve the effects of good flame retardancy, good construction performance and strong adhesion

Inactive Publication Date: 2014-07-02
SHANGHAI UNIV
View PDF4 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The water-based damping coating has a high composite loss factor and excellent damping performance in low temperature environments, but has the disadvantages of poor flame retardancy and long drying time
Marine damping materials not only require good damping performance, but also require high flame retardancy, good workability and fast drying speed, so the existing environmentally friendly damping coatings cannot meet the requirements of marine materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] The water-based marine damping paint in the normal temperature domain of this embodiment, the proportioning of the main components by weight ratio is: 50 parts of water-based mixed emulsion; 10 parts of 40-purpose mica powder; 15 parts of 100-purpose mica powder; 20 parts of 200-purpose mica powder; 25 parts 2 parts of Aluminum Hydroxide; 2 parts of Taxanol film-forming aid, the Taxanol film-forming aid used in the present invention comes from Eastman Corporation of the United States.

[0037] The method for preparing the normal temperature waterborne marine damping coating of the present embodiment may further comprise the steps:

[0038] (1) At normal temperature, 35 parts of water-based styrene-acrylic emulsion with a glass transition temperature of 10°C and 15 parts of water-based styrene-acrylic emulsion with a glass transition temperature of 40°C were uniformly mixed, and the water-based mixed emulsion was obtained after stirring and mixing uniformly;

[0039] (2)...

Embodiment 2

[0043]The water-based marine damping coating in the normal temperature region of this embodiment, the proportioning of the main components by weight is: 55 parts of water-based mixed emulsion; 15 parts of 100-mesh mica powder; 30 parts of 200-mesh mica powder; 20 parts of aluminum hydroxide; 10 parts Magnesium hydroxide; 3.5 parts of Taxanol film-forming aids, the Taxanol film-forming aids used in the present invention come from American Eastman Corporation.

[0044] The method for preparing the normal temperature waterborne marine damping coating of the present embodiment may further comprise the steps:

[0045] (1) At normal temperature, mix 35 parts of water-based styrene-acrylic emulsion with a glass transition temperature of 10°C and 20 parts of water-based styrene-acrylic emulsion with a glass transition temperature of 40°C, and stir and mix uniformly to obtain an aqueous mixed emulsion;

[0046] (2) Add mica powder, aluminum hydroxide, and magnesium hydroxide into the a...

Embodiment 3

[0050] The water-based marine damping coating in the normal temperature region of this embodiment, the proportioning of the main components by weight is 40 parts of water-based mixed emulsion; 5 parts of 40-purpose mica powder; 10 parts of 100-purpose mica powder; 25 parts of 200-purpose mica powder; 10 parts Aluminum hydroxide; 10 parts of antimony trioxide; 1.8 parts of Taxanol film-forming aid, the Taxanol film-forming aid used in the present invention comes from Eastman Company of the United States.

[0051] The method for preparing the normal temperature waterborne marine damping coating of the present embodiment may further comprise the steps:

[0052] (1) At normal temperature, mix 30 parts of water-based styrene-acrylic emulsion with a glass transition temperature of 5° C. and 10 parts of water-based styrene-acrylic emulsion with a glass transition temperature of 45° C., stir and mix to obtain a water-based mixed emulsion;

[0053] (2) Add mica powder, aluminum hydroxi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
tack-free timeaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a marine water-based damping coating and a preparation method thereof. A water-based styrene-acrylic emulsion with an interpenetrating polymer network structure is used as a film forming matter, mica powder with a laminated structure is used as a filler and coating additives are added. The marine water-based damping coating comprises the following main components in parts by weight: 40-65 parts of water-based mixed emulsion, 35-60 parts of filler and 20-40 parts of flame retardants. The marine water-based damping coating is prepared by mixing water-based emulsions, adding the filler and the additives and mixing the coating. The marine water-based damping coating disclosed by the invention has construction performances, high complex loss factor, strong adhesion to steel plates and good flame retardance, can be quickly dried under normal temperature, can ensure the steel plates not to rust after being applied and is environmentally friendly.

Description

technical field [0001] The invention relates to a water-based marine damping paint and a preparation method thereof. Background technique [0002] With the development of science and technology, the problem of noise pollution from berthing has attracted widespread attention, and a series of laws, regulations, and rules have been promulgated at home and abroad to increase the intensity of the regulation of noise pollution. The control of noise is mainly achieved through the control of noise sources, transmission channels and the protection of receivers. Among them, in terms of controlling noise sources and transmission channels, damping coatings have been widely promoted and applied due to their convenient construction, low cost, and good damping performance, especially environmentally friendly damping coatings. [0003] Environmentally friendly damping coatings have both the energy loss characteristics of some viscous liquids in a certain state and the energy storage charac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D125/14C09D7/12C09D5/00
Inventor 俞成丙陈赛赛杨丹殷雯青李秦龙胡季华
Owner SHANGHAI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com