A technology based on soybean oil and epoxy, which is applied in inks, applications, household appliances, etc., can solve the problems of slow progress, low viscosity, poor adhesion, etc., and achieve the effect of stable system performance, clear imprint, and good adhesion

Inactive Publication Date: 2016-08-17
瑞柯斯海口技术推广服务合伙企业有限合伙
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Although soybean ink has become the mainstream of offset printing inks in the world, the research and development of soybean ink is very difficult
At present, the production technology of soybean ink is relatively mature in developed countries such as the United States, Japan, and Germany, and its application fields are quite extensive. However, the domestic progress is quite slow, and there are few studies on the production process of soybean ink, and all soybean ink used needs to be imported.
[0005] At present, domestic research hotspots are mainly focused on polymerized soybean oil, but the performance of polymerized soybean oil prepared by existing methods is poor, especially the viscosity is low, and the adhesion is poor, so it is basically not practical

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of epoxy polymerized soybean oil for printing ink
  • A kind of preparation method of epoxy polymerized soybean oil for printing ink
  • A kind of preparation method of epoxy polymerized soybean oil for printing ink

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A kind of epoxy polymerized soybean oil for printing ink is prepared according to the following steps:

[0023] (1) Put a certain amount of soybean oil in the reaction kettle, start stirring, and then slowly heat to 250°C, keep it warm for 30 minutes, then add a certain amount of anthraquinone, keep it warm for 2 hours, and then lower it to room temperature to obtain the polymerization crude soybean oil;

[0024] (2) Slowly raise the temperature of the polymerized soybean oil crude material at room temperature to 60°C under constant stirring, add a certain amount of ditungsten trioxide, and start to drop the hydrogen peroxide solution with a mass fraction of 30%, and control the dropwise addition The time is 1 hour, then keep warm for 5 hours, then cool to room temperature, and let it stand for 24 hours, then centrifuge at a speed of 2000r / min for 20 minutes, then collect the upper layer liquid and filter it, and the filtrate is epoxy-polymerized soybean oil product 1. ...

Embodiment 2

[0027] A kind of epoxy polymerized soybean oil for printing ink is prepared according to the following steps:

[0028] (1) Put a certain amount of soybean oil in the reaction kettle, start stirring, then slowly heat to 230°C, keep it warm for 30 minutes, then add a certain amount of pentahydroxy iron, keep warm for 2 hours, and then lower it to room temperature to obtain Polymerized soybean oil crude material;

[0029] (2) Slowly raise the temperature of the polymerized soybean oil coarse material at room temperature to 50°C under constant stirring, add a certain amount of lithium oxide, and start to drop a hydrogen peroxide solution with a mass fraction of 30%, and control the dropping time to 1h, then keep warm for 4h, then cool to room temperature, and let it stand for 24h, then centrifuge at 2500r / min for 20min, then collect the upper layer liquid and filter, the filtrate is the epoxy-polymerized soybean oil product 2.

[0030] Among them, the mass ratio of iron pentahydr...

Embodiment 3

[0032] A kind of epoxy polymerized soybean oil for printing ink is prepared according to the following steps:

[0033] (1) Put a certain amount of soybean oil in the reaction kettle, start stirring, and then slowly heat to 200°C, keep it warm for 20 minutes, then add a certain amount of anthraquinone, keep it warm for 1 hour, and then lower it to room temperature to obtain the polymer crude soybean oil;

[0034] (2) Slowly raise the temperature of the polymerized soybean oil coarse material at room temperature to 40°C under constant stirring, add a certain amount of ditungsten trioxide, and start to drop the hydrogen peroxide solution with a mass fraction of 30%, and control the dropwise addition The time is 0.5h, then keep warm for 4h, then cool to room temperature, and let it stand for 20h, then centrifuge at 1000r / min for 15min, then collect the upper layer liquid and filter, and the filtrate is the epoxy-polymerized soybean oil product 3.

[0035] Wherein, the mass ratio ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of epoxy polymerized soybean oil for ink. The preparation method comprises the following steps of: firstly preparing thermally polymerized soybean oil by carrying out thermal polymerization on soybean oil under the condition of certain thermal polymerization reaction process parameters; then carrying out epoxidation on the thermally polymerized soybean oil by utilizing a high-efficiency catalyst to prepare the epoxy polymerized soybean oil. The epoxy polymerized soybean oil disclosed by the invention has the advantages of high viscosity, low acid number and good adhesive property, and meets the requirement of a soybean ink connecting material. Soybean ink prepared by taking the epoxy polymerized soybean oil as the soybean ink connecting material is high in volatilizing speed and high in adhesive force on various offset litho printing substrates and can substitute a large quantity of soybean oil ink products on the market.

Description

[technical field] [0001] The invention relates to a preparation method of epoxy-polymerized soybean oil for printing ink. [Background technique] [0002] Traditional printing inks are generally composed of binders, pigments and fillers, mineral oils, additives and other components, of which petroleum-based mineral oils (such as benzene, toluene, xylene, etc.) are used in an amount of 20-60%. A large amount of toxic and harmful VOC (Volatile Organic Chemical) will be produced in the process of manufacturing and ink printing, which will bring serious hidden dangers to the health of production operators and the natural ecological environment. According to statistics, the annual VOC emissions caused by various inks in the world have reached hundreds of thousands of tons, which can not only lead to a more serious greenhouse effect than carbon dioxide, but also form harmful oxides and photochemical smog under the action of sunlight, thus Seriously pollute the air environment. Es...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C11C3/00C09D11/107
Inventor 林跃华聂建华杨小艳刘兴高陈志国林秋云龙清平邱国平
Owner 瑞柯斯海口技术推广服务合伙企业有限合伙
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap