A printing method for gold thread polyester fabric

A technology of polyester fabric and printing method, which is applied in the field of textile printing and dyeing, can solve the problems of gold thread staining and fading, achieve the effects of reducing the degree of staining, improving anti-contamination, and solving fading

Active Publication Date: 2016-01-20
浙江嘉欣兴昌印染有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] What the present invention aims to solve is the problem of staining and fading of gold threads in the current polyester printing process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] Fabric pretreatment process: add 2.5g / L sodium carbonate, 2.5g / L refining agent, 0.2g / L degreasing agent and 0.5g / L chelating agent, and refine in an air-flow dyeing machine at 110°C for 90 minutes.

[0011] Printing process: use 3% water-dispersible polymer polyester compound, 2% disperse dye GS scarlet, water, 0.5% resist salt, appropriate amount of tamarind glue and 1% citric acid to form a gel solution to print the fabric.

[0012] Steaming process: steaming at a temperature of 170° C. for 5 minutes.

Embodiment 2

[0014] Fabric pretreatment process: add 2.5g / L sodium carbonate, 2.5g / L refining agent, 0.2g / L degreasing agent and 0.5g / L chelating agent, and refine in an air-flow dyeing machine at 110°C for 90 minutes.

[0015] Printing process: use 3% water-dispersible polymer polyester compound, 2% disperse dye S-RE dark blue, water, 0.5% resist salt, appropriate amount of sodium alginate paste and 1% citric acid to form a gel solution to process the fabric. printing.

[0016] Steaming process: steaming at a temperature of 170° C. for 5 minutes.

Embodiment 3

[0018] Fabric pretreatment process: add 2.5g / L sodium carbonate, 2.5g / L refining agent, 0.2g / L degreasing agent and 0.5g / L chelating agent, and refine in an air-flow dyeing machine at 110°C for 90 minutes.

[0019] Printing process: select 3% water dispersible polymer polyester compound, 2% disperse dye SG yellow, water, 0.5% resist salt, appropriate amount of tamarind glue and 1% citric acid to form a gel solution to print the fabric.

[0020] Steaming process: steaming at a temperature of 170° C. for 5 minutes.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a printing method for polyester fabrics with gold threads. The method comprises pretreatment, printing and steaming processes of fabrics; 2.0~2.5g / L sodium carbonate, 2.0~2.0g / L sodium carbonate, 2.0~ 2.5g / L refining agent, 0.16~0.2g / L degreasing agent and 0.4~0.5g / L chelating agent, refined in an airflow dyeing machine at 110°C for 90 minutes; water-dispersible polymers were selected in the printing process Polyester compound, dye, water, resist salt, printing paste and citric acid are combined to form a gel solution to print the fabric; the temperature of the steaming process is 170° C. and the time is 5 minutes. The printing method provided by the invention improves the color yield of the dye, improves the anti-contamination and anti-oxidation properties of the gold thread in the polyester printing process, and solves the fading problem of the gold thread in the polyester fabric printing process.

Description

technical field [0001] The invention relates to the field of textile printing and dyeing, in particular to a printing method for gold thread polyester fabric. Background technique [0002] On polyester printed fabrics, printing and dyeing workers use bronzing, gold powder or pearl powder printing methods to make up for the defect that gold threads cannot be used on polyester printed fabrics. Some scholars have also studied the manufacturing process of gold wires, using different chemical fiber films as base fabrics for vacuum aluminum plating, and coating colored transparent coatings on the outside, such as nylon NYLON, cupro ammonia fiber CUPRO, viscose RAYON, etc. However, this base fabric is very different from polyester fiber in terms of refining, coloring, alkali and chemical resistance, and can only be used in special polyester products. Ordinary gold thread will shrink, turn over, fade and other problems during the refining process of polyester fabrics. During the p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06P1/16D06P1/52D06P1/48D06P1/653D06P3/54D06M11/76D06B5/00D06M101/32
Inventor 刘宏东沈红卫胡传国侯爱芹
Owner 浙江嘉欣兴昌印染有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com