Using method for heat preserving and thermal insulating elastic joint mixture

A technology of thermal insulation and caulking agent, which is applied in the direction of construction and building structure, can solve the problems of construction trouble, human and environmental damage, affecting the quality of walls or ground, etc., and achieves the effect of easy operation and small deformation.

Inactive Publication Date: 2014-05-07
NANJING HENGAN RESIN CHEM
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the caulking agents currently available on the market use toxic and harmful raw materials, which are very harmful to the human body and the environment, and can only maintain the wall or ground for 8-9 months without cracking or damage after use, and it is very difficult to construct. Trouble, once the ratio is wrong, it will seriously affect the quality of the wall or ground

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Embodiment 1: a kind of method for using thermal insulation elastic joint filler, the method comprises the following steps:

[0017] 1) First weigh according to the parts by weight of the following raw materials: 10 parts of polypropylene short fiber, 10 parts of phenolic resin, 60 parts of quartz powder, 5 parts of tackifier, 1 part of surfactant, 15 parts of polystyrene, silane 3 parts of joint agent, 12 parts of white cement; wherein, the tackifier is a mixture of calcium sulfate and zinc oxide with a weight ratio of 3:2;

[0018] 2) Under stirring conditions, put polypropylene short fiber, phenolic resin, quartz powder, white cement, surfactant, silane coupling agent, and polystyrene in a stirrer and stir for 20 minutes, and then add tackifier for stirring 10min, promptly obtain described thermal insulation elastic sealant;

[0019] 3) Then mix the caulking agent obtained in step 2) with water to make a viscous material, fill the viscous material between the tiles,...

Embodiment 2

[0020] Embodiment 2: a method for using a thermal insulation elastic sealant, the method comprises the following steps:

[0021] 1) First weigh according to the parts by weight of the following raw materials: 15 parts of polypropylene short fiber, 30 parts of phenolic resin, 80 parts of quartz powder, 8 parts of tackifier, 3 parts of surfactant, 25 parts of polystyrene, silane 7 parts of joint agent, 18 parts of white cement; wherein, the tackifier is a mixture of calcium sulfate and zinc oxide with a weight ratio of 3:2;

[0022] 2) Under stirring conditions, put polypropylene short fiber, phenolic resin, quartz powder, white cement, surfactant, silane coupling agent, and polystyrene in a stirrer and stir for 30 minutes, and then add tackifier for stirring 15min, promptly obtain described thermal insulation elastic sealant;

[0023] 3) Then mix the caulking agent obtained in step 2) with water to make a viscous material, fill the viscous material between the tiles, and spray...

Embodiment 3

[0024] Embodiment 3: a method for using a heat-insulating elastic sealant, the method comprises the following steps:

[0025] 1) First weigh according to the parts by weight of the following raw materials: 12 parts of polypropylene short fiber, 22 parts of phenolic resin, 70 parts of quartz powder, 6 parts of tackifier, 2 parts of surfactant, 20 parts of polystyrene, silane 5 parts of joint agent, 15 parts of white cement; wherein, the tackifier is a mixture of calcium sulfate and zinc oxide with a weight ratio of 3:2;

[0026] 2) Under stirring conditions, put polypropylene short fiber, phenolic resin, quartz powder, white cement, surfactant, silane coupling agent, and polystyrene in a stirrer and stir for 25 minutes, and then add tackifier for stirring 12min, promptly obtain described thermal insulation elastic sealant;

[0027] 3) Then mix the caulking agent obtained in step 2) with water to make a viscous material, fill the viscous material between the tiles, and spray wa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a using method for heat preserving and thermal insulating elastic joint mixture. The using method for the heat preserving and thermal insulating elastic joint mixture comprises weighting the follow raw materials which comprise 10 to 15 parts of polypropylene short fibers, 10 to 30 parts of phenolic resin, 60 to 80 parts of quartz powder, 5 to 8 parts of tackifier, 1 to 3 parts of surface active agent, 15 to 25 parts of polrvinyl benzene, 3 to 7 parts of silane coupling agent and 12 to 18 parts of white cement; stirring the polypropylene short fibers, the phenolic resin, the quartz powder, the surface active agent, the polrvinyl benzene, the silane coupling agent and the white cement in a stirrer for 20 to 30 minutes, adding the tackifier and stirring for 10 to 15 minutes and obtaining the heat preserving and thermal insulating elastic joint mixture; mixing the joint mixture and water, mixing into sticky material to be filled between ceramic tiles and spraying water for one time after the sticky material is dried. According to the using method for the heat preserving and thermal insulating elastic joint mixture, operation is simple and convenient, the joint mixture can be mixed when being used, water spraying can consolidate the joint mixture when the joint mixture is used, and the wall surface generates no cracks caused by ceramic file replacement.

Description

[0001] technical field [0002] The invention relates to a method for using a thermal insulation elastic joint filler. Background technique [0003] Sealant is a chemical widely used in the construction industry. Usually, it has strong adhesion, small shrinkage, strong color fixation, flexibility to prevent cracks, good decorative texture, pressure resistance, wear resistance, and mold resistance. specialty. [0004] However, the caulking agents currently available on the market use toxic and harmful raw materials, which are very harmful to the human body and the environment, and can only maintain the wall or ground for 8-9 months without cracking or damage after use, and it is very difficult to construct. Trouble, once the ratio is wrong, it will seriously affect the quality of the wall or ground. Contents of the invention [0005] Purpose of the invention: In order to overcome the deficiencies of the prior art, the purpose of the present invention is to provide a metho...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): E04B1/682C04B28/04
Inventor 马步强
Owner NANJING HENGAN RESIN CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap