Preparation method of chinlon 6 cool jade fiber

A technology of jade fiber and nylon, applied in the field of preparation of nylon 6 cool jade fiber, can solve the problem of high production cost, and achieve the effects of lower contact temperature, strong cooling feeling and strong wear resistance.

Active Publication Date: 2014-04-30
FUJIAN JINJIANG TECH
View PDF7 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But there is no mention of compounding with other fiber materials, and the production cost is relatively high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Synchronously add nano-scale jade powder masterbatch and nylon 6 glossy slices to the screw through a separate metering system in proportion for spinning. The feeding speed of nano-scale jade powder masterbatch is 95g / min, and nylon 6 glossy chips The speed is 3165g / min: the temperature of each zone of the screw is: 235°C, 247°C, 255°C, 258°C, 260°C; the temperature of the spinning box: 258°C; the amount of oil: 1.2%; the speed of side blowing: 0.6m / min; drawing temperature: 78°C, drawing speed: 4360m / min; winding speed: 4350m / min.

[0017] The specifications of the prepared nylon 6 cool jade fiber silk are FDY70d / 48f, CV%=0.9, breaking strength=4.2CN / dt, breaking elongation=43%; boiling water shrinkage: 9%; full roll rate 80%; Dyeing degree: 4 grades. Body surface contact temperature drop: 2.0°C.

Embodiment 2

[0019] Synchronously add nano-scale jade powder masterbatch and nylon 6 bright slices to the screw through a separate metering system in proportion to spinning, wherein the feeding speed of nano-scale jade powder master batch is 200g / min, and nylon bright slices are fed The speed is 3000g / min: the temperature of each zone of the screw is: 238°C, 249°C, 257°C, 260°C, 262°C; the temperature of the spinning box: 261°C; the amount of oil: 1.2%; the speed of side blowing: 0.6m / min; drawing temperature: 78°C, drawing speed: 4360m / min; winding speed: 4350m / min.

[0020] The specifications of the prepared nylon 6 cool jade fiber silk are FDY70d / 48f, CV%=0.95, breaking strength=4.3CN / dt, breaking elongation=41%; boiling water shrinkage: 9%; full roll rate 85%; Dyeing degree: 4 grades. Body surface contact temperature drop: 1.5°C.

Embodiment 3

[0022] Synchronously add nano-scale jade powder masterbatch and nylon 6 glossy slices to the screw through a separate metering system in proportion to spinning, wherein the feeding speed of nano-scale jade powder masterbatch is 100g / min, and the feeding speed of nylon bright slices The speed is 3150kg / min: the temperature of each zone of the screw is: 235°C, 249°C, 258°C, 260°C, 263°C; the temperature of the spinning box: 260°C; the amount of oil: 1.3%; the speed of side blowing: 0.6m / min; drawing temperature: 80°C, drawing speed: 4360m / min; winding speed: 4350m / min.

[0023] The specifications of the prepared nylon 6 cool jade fiber silk are FDY70d / 48f, CV%=0.9, breaking strength=4.3CN / dt, breaking elongation=46%; boiling water shrinkage: 9%; full roll rate 90%; Dyeing degree: 4 grades. Body surface contact temperature drop: 1.5°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a chinlon 6 cool jade fiber. The fiber is prepared by the steps of adopting an extraction technology and a nanotechnology, allowing jade and other beneficial mineral materials such as aluminum, silicon, titanium, zirconium and other elements to reach the sub-nanometer particle size, then fusing into a chinlon 6 melt, and carrying out spinning processing to obtain the fiber. The chinlon 6 cool jade fiber has the strength equivalent to a conventional chinlon 6 fiber, has strong wear resistance, has strong cool feel compared with an ordinary silk woven fabric, and is simple in spinning process and high in practicability.

Description

technical field [0001] The invention relates to a preparation method of nylon 6 cool jade fiber; specifically, it is a method for preparing functional nylon 6 fiber by blending and spinning nanometer jade powder refined by nano-extraction technology and nylon 6 melt through screw rods. Background technique [0002] At present, jade fiber is basically polyester cool jade fiber. Shanghai Defulun Chemical Fiber Co., Ltd. uses inorganic nano super cool polyester masterbatch and polyester chips to mix, and produces super cool cool feeling through polyester fiber production process. Healthy polyester fiber. Compared with ordinary polyester fiber, this fiber can improve the cool feeling by more than 20%, and endow the product with excellent UV protection, moisture absorption and perspiration, antibacterial and health care functions. In addition, according to De Fulun, waste plastic bottle flakes and other raw materials are used to process cooling fibers. The products are both cool...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D01F6/90D01F1/10
Inventor 张瑞瑞霍显海易春旺
Owner FUJIAN JINJIANG TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More