Containers that prevent solutes in salt and alkali solutions and molten salt and alkali from creeping out

A molten state, alkaline solution technology, applied in the field of containers where salt and alkali crawl out, can solve problems affecting normal production, salt stains, alkali stains are difficult to clean, concentration reduction, etc., to achieve large-scale production and excellent chemical stability , the effect of simple operation

Active Publication Date: 2016-03-23
SHANGHAI INST OF TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For salt, alkali solution and molten salt and alkali, in an open system, if left for a period of time, the crystals will climb out along the container wall, and climb outside the container mouth to form salt and alkali stains, making the concentration of the prepared solution Reduce or cause the loss of salt and alkali in molten state, and it is difficult to clean up salt and alkali stains, which not only affects the normal production of experiments and factories, but also wastes resources

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A container for preventing solutes in salt and alkali solutions and molten salt and alkali from creeping out, including the container, and sintering on the inner wall of the container mouth from the edge of the container mouth down to 0.5-1.5cm from the edge of the container mouth Has a non-adhesive film;

[0031] The non-adhesive film is polytetrafluoroethylene with a thickness of 0.05-0.075mm;

[0032] The container is an open glass container, i.e. a glass beaker.

[0033] A kind of above-mentioned preparation method of the container that prevents the solute in the salt and alkali solution and the salt in the molten state and the alkali to climb out, specifically comprises the following steps:

[0034] (1) Take a glass beaker and wash it with deionized water to get a clean glass beaker;

[0035] (2) On the inner wall of the mouth of a clean glass beaker, apply a layer of polytetrafluoroethylene emulsion dispersion liquid from the edge of the container mouth down to ...

Embodiment 2

[0040] A container for preventing solutes in salt and alkali solutions and molten salt and alkali from creeping out, including the container, and sintering on the inner wall of the container mouth from the edge of the container mouth down to 0.5-1.5cm from the edge of the container mouth Has a non-adhesive film;

[0041] The non-adhesive film is polytetrafluoroethylene with a thickness of 0.05-0.075mm;

[0042] The container is an open ceramic container, that is, a crucible.

[0043] A kind of above-mentioned preparation method of the container that prevents the solute in the salt and alkali solution and the salt in the molten state and the alkali to climb out, specifically comprises the following steps:

[0044] (1) Take the crucible, and get a clean crucible after being treated with deionized water;

[0045] (2) On the inner wall of the clean crucible mouth, from the edge of the container mouth down to 0.5-1.5cm away from the edge of the container mouth, apply a layer of p...

Embodiment 3

[0050] A container for preventing solutes in salt and alkali solutions and molten salt and alkali from creeping out, including the container, and sintering on the inner wall of the container mouth from the edge of the container mouth down to 0.5-1.5cm from the edge of the container mouth Has a non-adhesive film;

[0051] The non-adhesive film is polyvinylidene fluoride with a thickness of 0.05-0.075mm;

[0052] The container is an open metal container, that is, a stainless steel container.

[0053] A kind of above-mentioned preparation method of the container that prevents the solute in the salt and alkali solution and the salt in the molten state and the alkali to climb out, specifically comprises the following steps:

[0054] (1) Take a stainless steel container and clean it with deionized water;

[0055] (2) On the inner wall of a clean stainless steel container mouth, spray a layer of polyvinylidene fluoride swelling solution from the edge of the container mouth down to ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
sintering temperatureaaaaaaaaaa
sintering temperatureaaaaaaaaaa
Login to View More

Abstract

The invention discloses a container and a preparation method for preventing solutes in salt and alkali solutions and molten salts and alkalis from creeping out. On the inner wall of the container mouth, there is a non-adhesive film sintered from the edge of the container mouth down to 0.5-1.5cm from the edge of the container mouth. The non-adhesive film is polytetrafluoroethylene or polyvinylidene with a thickness of 0.05-0.075mm. Vinyl fluoride. The container for preventing the solute in the salt and alkali solution and the salt and alkali in the molten state from climbing out can effectively prevent the phenomenon of climbing salt and alkali, and does not affect the use of salt and alkali. Moreover, the preparation method is simple, the cost is low, and it is convenient for large-scale production.

Description

technical field [0001] The invention belongs to the field of energy saving and consumption reduction, in particular to a container from which the solute in the salt and alkali solution and the salt and alkali in the molten state creep out. Background technique [0002] The phenomenon that salt and alkali climb out along with the container wall is classified as "alkali climbing" phenomenon. For salt, alkali solution and molten salt and alkali, in an open system, if left for a period of time, the crystals will climb out along the container wall, and climb outside the container mouth, forming salt and alkali stains, making the concentration of the prepared solution Reduce or cause the loss of salt and alkali in the molten state, and the salt stains and alkali stains are difficult to clean up, which not only affects the normal production of experiments and factories, but also wastes resources. This method is simple and convenient, and can effectively improve the phenomenon of "...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B1/02B32B27/30B32B33/00B32B1/00
Inventor 张全生王淼党国举王昭勍李海燕闵凡奇李硕李细方张伟黄海军
Owner SHANGHAI INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com