Beryllium silicate glass containing NPO2 and radioactive waste liquid treatment method

A beryllium silicate and glass technology, applied in the field of beryllium silicate glass, can solve the problems of affecting the expected life of the material, easy to catch fire, low mechanical strength, etc., to enhance stability and corrosion resistance, enhance mechanical strength, enhance Effects of stability and corrosion resistance

Active Publication Date: 2014-04-16
LIYANG TECH DEV CENT
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, bituminous treatment has several major disadvantages: reduced stability, easy fire, limited range of use, low mechanical strength
However, cement curing has two significant disadvantages: the volume of the waste material doubles after coating; it affects the life expectancy of the obtained material
However, the stability, mechanical strength and corrosion resistance of borosilicate glass still cannot meet the needs of people to seal moderately radioactive waste liquid.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] The beryllium silicate glass of the present invention comprises the following components represented by mass percent:

[0038] a)SiO2 2 :45

[0039] b) BeO: 16

[0040] c)Na 2 O: 11

[0041] d)Al 2 o 3 :5

[0042] e) oxides of at least one transition element: 5;

[0043] f) at least one rare earth element oxide: 5;

[0044] g) NpO 2 :5;

[0045] h) HfO 2 :8.

Embodiment 2

[0047] The beryllium silicate glass of the present invention comprises the following components represented by mass percent:

[0048] a)SiO2 2 :46

[0049] b) BeO: 16

[0050] c)Na 2 O: 11

[0051] d)Al 2 o 3 :5

[0052] e) oxides of at least one transition element, preferably Fe 2 o 3 、Cr 2 o 3 , MnO 2 , TcO 2 , RuO 2 : 4.5;

[0053] f) At least one rare earth element oxide: 5.5;

[0054] g) NpO 2 :5;

[0055] h) HfO 2 :7.

Embodiment 3

[0057] The beryllium silicate glass of the present invention comprises the following components represented by mass percent:

[0058] a)SiO2 2 :45

[0059] b) BeO: 19

[0060] c)Na 2 O: 11

[0061] d)Al 2 o 3 :5

[0062] e) oxides of at least one transition element, preferably Fe 2o 3 、Cr 2 o 3 , MnO 2 , TcO 2 , RuO 2 : 4.5;

[0063] f) At least one rare earth element oxide: 4.5;

[0064] g) NpO 2 :4;

[0065] h) HfO 2 :7.

[0066] The invention also discloses a method for treating moderately radioactive radioactive waste liquid, wherein the waste liquid selectively added with roasting aids is roasted to obtain roasted products, and then vitrification aids are added to the roasting In the product, the calcined product and the vitrification aid are melted in a water-cooled crucible to obtain a glass frit, and then the glass frit is cooled, thereby obtaining the above-mentioned beryllium silicate glass.

[0067] Wherein the roasting aid is selected from alumi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses beryllium silicate glass. The beryllium silicate glass comprises, by mass, SiO2 42-49 %, BeO 15-20%, Na2O 11-14%, Al2O3 5-10%, at least one transition element oxide 3-6.5%, at least one rare earth element oxide 3-6.5%, NpO2 3-6.5%, and HfO2 5-8%. The beryllium silicate glass has high stability, good mechanical strength and very high chemical corrosion resistance and can be well sealed, preserved and isolate waste liquid under the condition that the volume is decreased.

Description

technical field [0001] The invention relates to a beryllium silicate glass used for sealing, preserving and isolating radioactive waste liquid in nuclear reactor devices. Background technique [0002] Moderately radioactive radioactive waste water is produced in nuclear fuel regeneration equipment such as nuclear reactors, and is currently mainly treated by asphalting or cement solidification. However, the use of asphalt treatment has several major disadvantages: reduced stability, easy fire, limited range of use, and low mechanical strength. The cost of cement treatment is moderate, the application is simple, the mechanical strength is good, and the stability is long-lasting. But cement curing has two significant disadvantages: the volume of the waste material doubles after coating; and it affects the life expectancy of the obtained material. [0003] In addition, people are now also studying the use of glass to seal radioactive waste liquid. Because of its amorphous stat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G21F9/20G21F9/16
Inventor 梅欣
Owner LIYANG TECH DEV CENT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com