Lanthanum-lead-strontium ferrite

A technology of ferrite and iron oxide, applied in the field of lanthanum-lead-strontium ferrite, which can solve the problems that ferrite cannot meet

Inactive Publication Date: 2014-03-05
NINGBO STAR MATERIALS HI TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

A single ferrite cannot meet the needs of various environments

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Lanthanum-lead-strontium ferrite

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] A lanthanum-lead-strontium ferrite, characterized in that: the mass ratio of its components is: lanthanum oxide 5%, lead oxide 7%, strontium oxide 4%, boron oxide 1%, nickel oxide 3%, oxide Zinc 9%, silicon oxide 2%, calcium oxide 0.7%, the balance is iron oxide.

Embodiment 2

[0014] A lanthanum-lead-strontium ferrite, characterized in that: the mass ratio of its components is: lanthanum oxide 10%, lead oxide 3%, strontium oxide 2%, boron oxide 2%, nickel oxide 4%, oxide Zinc 7%, silicon oxide 3%, calcium oxide 0.2%, the balance is iron oxide.

Embodiment 3

[0016] A lanthanum-lead-strontium ferrite, characterized in that: the mass ratio of its components is: lanthanum oxide 7%, lead oxide 5%, strontium oxide 3%, boron oxide 1.5%, nickel oxide 2%, oxide 4% zinc, 3% silicon oxide, 0.5% calcium oxide, and the balance is iron oxide.

[0017] The electromagnetic performance of the gadolinium barium ferrite described in embodiment 1-3 is as shown in table 1:

[0018]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a lanthanum-lead-strontium ferrite which is characterized in that the lanthanum-lead-strontium ferrite comprises, by mass, 5-10% of lanthanum oxide, 3-7% of lead oxide, 2-4% of strontium oxide, 1-2% of boric oxide, 2-6% of nickel oxide, 4-10% of zinc oxide, 2-3% of silicon oxide, 0.2-0.7% of calcium oxide, and the balance ferric oxide. The lanthanum-lead-strontium ferrite has wonderful saturation magnetization.

Description

technical field [0001] The invention belongs to the field of magnetic materials, in particular to a lanthanum-lead-strontium ferrite. Background technique [0002] Ferrite is a ferromagnetic metal oxide, which is sintered from iron oxide and other ingredients. In terms of electrical properties, the resistivity of ferrite is much larger than that of metal and alloy magnetic materials, and it also has higher dielectric properties. The magnetic properties of ferrite are also shown to have higher magnetic permeability at high frequencies. Therefore, ferrite has become a widely used non-metallic magnetic material in the field of high frequency and weak current. Due to the low magnetic energy stored in the unit volume of ferrite, the saturation magnetization is also low, usually only 1 / 3 to 1 / 5 of pure iron, which limits its use in low-frequency strong electricity and large fields that require higher magnetic energy density. applications in the power field. [0003] Ferrite na...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): H01F1/34
Inventor 苏广春关井和陈益明
Owner NINGBO STAR MATERIALS HI TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com