Down coat fabric treatment method for preventing down feather from escaping from needle holes

A technology for down jacket fabrics and processing methods, applied in fiber processing, fiber types, textiles and papermaking, etc., can solve the problems of low weight gain and cold resistance, achieve high resilience and smoothness, excellent wearing comfort, and improved elasticity Effect

Active Publication Date: 2014-03-05
DANDONG UNIK TEXTILE
View PDF5 Cites 29 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a method for anti-pinhole drilling of down jacket fabrics, which solves the problem of down drilling in down jacket fabrics, especially the problem of down drilling at sewing pinholes, by finishing (coating) the fabrics. The good combination of glue can meet the anti-drilling effect, especially the anti-drilling effect at the sewing pinhole. At the same time, the optional coating glue can ensure the anti-drilling performance, cold resistance and permeability of the fabric with low weight gain. Wetness, washability, softness and other comprehensive indicators make the fabric more comfortable to wear under the premise of satisfying functionality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Down coat fabric treatment method for preventing down feather from escaping from needle holes

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] (1) Fabric selection: plain fabric woven from nylon FDY fully stretched yarn, yarn count 40D*40D, density 290T;

[0038] (2) Water-repellent finishing is carried out on the fabric, and the water-staining level is ≥3;

[0039] (3) Calender the fabric after water-repellent finishing with a calender, with a pressure of 11Mpa, a temperature of 110°C, and a speed of 30 m / min;

[0040] (4) Coating glue preparation, raw material weight ratio:

[0041] 100 parts of polyether polyurethane coating glue;

[0042] 30 parts of hydroxyl-terminated polydimethylsiloxane emulsion;

[0043] 1 part of isocyanate crosslinking agent;

[0044] 1.2 parts of cross-linking accelerator;

[0045] 3 parts of silica matting powder;

[0046] 15 parts of toluene;

[0047] Mix and stir the silica-based matting powder with toluene to fully dissolve, then mix and stir with polyether polyurethane coating glue evenly, then add hydroxyl-terminated polydimethylsiloxane emulsion, isocyanate cross-linki...

Embodiment 2

[0051](1) Fabric selection: plain weave fabric woven with nylon FDY fully stretched yarn, yarn count 20D*20D, density 370T;

[0052] (2) Water-repellent finishing is carried out on the fabric, and the water-staining level is ≥3;

[0053] (3) Calender the fabric after water-repellent finishing with a calender, with a pressure of 9Mpa, a temperature of 100°C, and a speed of 35 m / min

[0054] (4) Coating glue preparation, raw material weight ratio:

[0055] 100 parts of polyether polyurethane coating glue;

[0056] 25 parts of hydroxyl-terminated polydimethylsiloxane emulsion;

[0057] 1.2 parts of isocyanate crosslinking agent;

[0058] 1.5 parts of cross-linking accelerator;

[0059] 3 parts of silica matting powder;

[0060] 15 parts of toluene;

[0061] Mix and stir the silica-based matting powder with toluene to fully dissolve, then mix and stir with polyether polyurethane coating glue evenly, then add hydroxyl-terminated polydimethylsiloxane emulsion, isocyanate cross...

Embodiment 3

[0065] (1) Fabric selection: plain weave fabric woven with nylon FDY fully stretched yarn, yarn count 30D*30D, density 300T;

[0066] (2) Water-repellent finishing is carried out on the fabric, and the water-staining level is ≥3;

[0067] (3) Calender the fabric after water-repellent finishing with a calender, with a pressure of 10Mpa, a temperature of 100°C, and a speed of 35 m / min;

[0068] (4) Coating glue preparation, raw material weight ratio:

[0069] 100 parts of polyether polyurethane coating glue;

[0070] 20 parts of hydroxyl-terminated polydimethylsiloxane emulsion;

[0071] 1.5 parts of isocyanate crosslinking agent;

[0072] 1.8 parts of cross-linking accelerator;

[0073] 4 parts of silica matting powder;

[0074] Butanone 15 parts;

[0075] Mix and stir the silica-based matting powder with toluene to fully dissolve, then mix and stir with polyether polyurethane coating glue evenly, then add hydroxyl-terminated polydimethylsiloxane emulsion, isocyanate cros...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a down coat fabric treatment method for preventing down feather from escaping from needle holes. The down coat fabric treatment method is mainly technically characterized in that 100 parts by weight of a polyether polyurethane coating adhesive, 20-30 parts of a hydroxy terminated polydimethylsiloxane emulsion, 1-1.5 parts of an isocyanate cross-linking agent, 1.2-1.8 parts by weight of a cross-linking promoter, 3-5 parts of silicon dioxide extinction powder and 15 parts of butanone or toluene are mixed to prepare a coating adhesive, which is applied to a fabric by a floating knife coating machine, and the dry weight increase reaches 4-6 g / m<2>. The effect of preventing down feather from escaping from sewing needle holes is good, and the cold resistance, moisture permeability, washing fastness and flexibility of a fabric are ensured.

Description

Technical field [0001] The present invention involves the finishing technology after the textile fabric, which is specifically involved. Background technique [0002] The phenomenon of down jackets drilling has always plagued the down fabric manufacturers and clothing processing enterprises, and it also brings many inconvenience to consumers.Industry workers have also been committed to the research and development of anti -drilling fabric products and anti -diamond velvet clothing processing technology. [0003] The anti -diamond -proof effect of down jackets is mainly achieved from several aspects. One is to increase the weaving density of the fabric, the other is to organize it through the mirror surface, and the third is to coat with polyurethane or organic silicon coating adhesive, or use organizational collation.Polish treatment.To improve the anti -diamond velvet effect of the fabric.For example, the patented CN 102433743 B's "processing method of anti -diamond velvet fabri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/568D06M15/647D06M11/79D06M101/34
Inventor 张迎春李金华李晓霞孟雅贤张悦
Owner DANDONG UNIK TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com