Polyether sulfone fiber compound rope and preparation method thereof

A polyethersulfone fiber and core-spun rope technology, applied in the field of ropes, can solve the problems of low heat resistance, physical and mechanical properties, low insulation performance, and unsuitability for high humidity, and achieve reasonable processing technology, compact weaving, and excellent heat resistance performance effect

Inactive Publication Date: 2014-02-12
TAIAN ROPE NET PLASTIC
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The core-spun rope is widely used due to its good properties of the inner and outer materials. Therefore, the core-spun rope is an important daily necessities. In the existing core-spun rope, although it has other high performance, However, the heat resistance, physical and mechanical properties, and insulation properties are not high, so it is not suitable for high humidity and high temperature environments

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyether sulfone fiber compound rope and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0015] The preparation method of polyethersulfone fiber core-spun rope comprises the following steps:

[0016] (1) Material selection: polyethersulfone fiber filaments are selected, and their specifications are 210D-1050D; the processing technology of the polyethersulfone fiber filaments is as follows: the polyethersulfone resin is dried by blowing, put into a twin-screw extruder Heating and melting at a temperature of 300-400°C, and then melting and extruding the filament through a spinning assembly with a temperature resistance temperature of at least 500°C. The extrusion temperature is 310-390°C to obtain surface-treated polyethersulfone fiber filaments, so that The fiber has excellent heat resistance, physical and mechanical properties, and insulation properties;

[0017] (2) Doubling: 3-6 polyethersulfone fiber filaments are combined into one strand for doubling;

[0018] (3) Twisting: After paralleling, the polyethersulfone fiber filaments are twisted into strands throu...

Embodiment 1

[0022] 1. Select raw materials: The selected raw materials are surface-treated polyethersulfone fiber filaments, and their specifications are 210D;

[0023] 2. Paralleling: 3 polyethersulfone fiber filaments are combined into one strand for paralleling;

[0024] 3. Twisting: After paralleling, the polyethersulfone fiber filaments are twisted through a twisting machine, and the transmission belt of the twisting machine is tight and tight. Each filament must be controlled by a tension regulator, and its speed and twist are measured regularly. Depending on the size of the rope strands;

[0025] 4. Pre-weaving: The strands twisted by the twisting machine are pre-woven on the automatic pre-looming machine into a bobbin that meets the spindle size of the high-speed weaving machine for weaving;

[0026] 5. Rope formation: Put the pre-woven bobbin on the spindle, and drive the spindle to rotate at high speed by starting the motor of the high-speed braiding machine. The rope sheath 1 ...

Embodiment 2

[0028] 1. Select raw materials: The selected raw materials are surface-treated polyethersulfone fiber filaments, and their specifications are 420D;

[0029] 2. Parallel line: 5 polyethersulfone fibers are combined into one strand for parallel line;

[0030] 3. Twisting: After paralleling, the polyethersulfone fiber filaments are twisted through a twisting machine, and the transmission belt of the twisting machine is tight and tight. Each filament must be controlled by a tension regulator, and its speed and twist are measured regularly. Depending on the size of the rope strands;

[0031] 4. Pre-weaving: The strands twisted by the twisting machine are pre-woven on the automatic pre-looming machine into a bobbin that meets the spindle size of the high-speed weaving machine for weaving;

[0032] 5. Rope formation: Put the pre-woven bobbin on the spindle, and drive the spindle to rotate at high speed by starting the motor of the high-speed braiding machine. The rope sheath 1 is se...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a polyether sulfone fiber compound rope and a preparation method thereof. The polyether sulfone fiber compound rope comprises a rope cover and a rope core, wherein the rope cover is formed by knitting part of polyether sulfone fiber strands in an S twisting direction and another part in a Z twisting direction; the rope cover is an outer sleeve body knitted from a plurality of polyether sulfone fiber strands which are formed by twisting a plurality of polyether sulfone fiber filaments subjected to surface treatment; the rope core is arranged in the rope cover and structured as an integrated body of the polyether sulfone fiber filaments. The polyether sulfone fiber compound rope is compact in knitting, reasonable in process, outstanding in heat resistance, physical and mechanical performances and insulation performance, and suitable for being applied to the site with high humidity and high temperature.

Description

technical field [0001] The invention belongs to the technical field of ropes, in particular to a polyethersulfone fiber core-spun rope and a preparation method thereof. Background technique [0002] The core-spun rope is widely used due to its good properties of the inner and outer materials. Therefore, the core-spun rope is an important daily necessities. In the existing core-spun rope, although it has other high performance, However, the heat resistance, physical and mechanical properties, and insulation properties are not high, and it is not suitable for high humidity and high temperature environments. Contents of the invention [0003] The object of the present invention is to provide a polyethersulfone fiber cored rope with excellent heat resistance and insulation performance and a preparation method thereof. [0004] In order to achieve the above object, the technical solution adopted by the present invention is: a polyethersulfone fiber core-spun rope, which includ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D04C1/12D04C1/02
Inventor 沈明刘瑞强张功明田涛侯虎刘翠华
Owner TAIAN ROPE NET PLASTIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com