Solid construction coating and preparation method thereof

A coating and solid technology, applied in the direction of polyurea/polyurethane coatings, coatings, etc., can solve the problems of slow drying speed of liquid or viscous liquid coatings, consuming manpower and material resources, and not suitable for thin coating, so as to reduce construction costs and reduce The effect of manpower and material resources and short drying time

Active Publication Date: 2016-08-17
李俊强
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When liquid or viscous paint is used in construction, construction personnel are required to have high coating technology, which consumes a lot of manpower and material resources; moreover, liquid or viscous paint is easy to splash during construction, especially in indoor construction. Protect furniture, electrical appliances and floors to avoid damage to indoor facilities; more importantly, liquid or viscous paints dry slowly
The powder coating requires special equipment when it is used in construction, it is not suitable for thin coating, only suitable for thick coating, and the baking temperature should be above 150 °C

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0029] The preparation method of the solid construction paint provided by the present embodiment may further comprise the steps:

[0030] Mix the excipient, humectant, and deionized water according to weight percentage, heat to a first predetermined temperature, and dissolve to obtain a first solution;

[0031] Adding a neutralizing agent to the first solution, raising the temperature to a second predetermined temperature, keeping the temperature for a predetermined time, so that the reaction is sufficient to obtain a second solution;

[0032] Add water-based paint to the second solution, and disperse evenly to obtain the third solution;

[0033] Pour the third solution into the mold, cool and shape to obtain the coating.

[0034] Preferably, the step is to mix the excipient, humectant, and deionized water by weight percentage, heat to a first predetermined temperature, and dissolve to obtain the first solution, and the first predetermined temperature is 60°C to 70°C;

[003...

preparation example 1

[0039] Mix 8% excipient by weight, 8% moisturizer by weight, and 21.28% deionized water by weight, heat to the first predetermined temperature of 60°C to 70°C, and dissolve; add 2% by weight % neutralizer, the temperature rises to 90°C-95°C, and the reaction is kept for 20-60 minutes to make the reaction fully; add 60.72% by weight of latex paint to obtain a uniformly dispersed solution; keep the temperature at 90°C-95°C , pour the solution into the mold, cool and shape to get solid interior wall latex paint. Herein, the weight percentage refers to the weight percentage of the raw material components and the solid coating, such as the weight percentage of stearic acid and the solid coating.

[0040] The latex paint can be any known latex paint in the art. But in this embodiment, the latex paint preferably includes the following components: 1.5 parts of propylene glycol, 0.2 parts of wetting agent, 1.5 parts of dispersant, 0.1 part of bactericide, 0.3 part of defoamer, 0.1 par...

preparation example 2

[0042] Mix 8% by weight of excipients and 8% by weight of humectants, heat to the first predetermined temperature of 60°C to 70°C, and dissolve; add 2% by weight of neutralizers, and raise the temperature to 90 ℃~95℃, keep warm for 20 minutes~60 minutes to make the reaction fully; add water-based industrial paint with a weight percentage of 82% to obtain a uniformly dispersed solution; keep the temperature at 90℃~95℃, pour the solution into the abrasive tool, Cool and form to obtain a solid water-based high-gloss white finish.

[0043] The water-based industrial paint can be any known water-based industrial paint in the art. But in this embodiment, the water-based industrial paint preferably includes the following components: 66 parts of water-based polyurethane dispersion, 0.6 part of 20% triethylamine, and 15.4 parts of titanium dioxide.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a solid construction coating and a preparation method thereof. The construction coating comprises: 50% to 82% by weight of water-based paint, 2% to 10% by weight of excipients, and 1% to 10% by weight of moisturizing agents , 1% to 5% by weight neutralizer, 0% to 40.5% by weight deionized water. The preparation method of the construction coating includes: mixing and dissolving excipients, humectants, and deionized water to obtain a first solution; adding a neutralizer, raising the temperature to make the reaction fully obtain a second solution; adding The water-based paint is uniformly dispersed to obtain a third solution; the third solution is poured into a mold for cooling and forming to obtain a paint. The paint provided by the invention is a solid paint, which will not cause paint splashes during construction and use, does not need to cover indoor facilities, saves construction time and reduces manpower and material resources, and has a short drying time. No professional equipment is required for construction and use, which reduces construction costs.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to solid construction coatings; in addition, the invention also relates to a preparation method of solid construction coatings. Background technique [0002] Coatings are materials that can be applied to the surface of an object to be coated and form a firmly adherent continuous film. It can be inorganic, such as copper plating, nickel plating, zinc plating, etc.; it can also be organic, such as most organic polymer materials. Organic coatings have become a major component of today's coatings market. In the related art, the form of the paint is liquid, viscous, or powder. When liquid or viscous paint is used in construction, construction personnel are required to have high coating technology, which consumes a lot of manpower and material resources; moreover, liquid or viscous paint is easy to splash during construction, especially in indoor construction. Protect furniture, elect...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D5/00C09D125/14C09D175/04C09D133/04C09D7/12
Inventor 李俊强
Owner 李俊强
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap