Modified polyvinyl chloride cable sheath material with low-temperature impact resistance

A polyvinyl chloride cable, impact modification technology, applied in the direction of insulated cables, cables, circuits, etc., can solve the problems of poor chemical stability, life and property safety, poor flame retardancy, etc., to achieve good mechanical properties and processing performance, the market Broad application prospects, chemical corrosion resistance effect

Inactive Publication Date: 2014-01-22
李小芬
View PDF5 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the development of the economy, the places where cables need to be used have become diversified, and there are more stringent and diverse requirements for the performance indicators of cable sheath materials, such as insulation, tensile strength, service temperature, flame retardant performance and other indicators There are strict requirements, and continuous improvement of the performance of sheath materials is an urgent need for economic and social development. Traditional sheath materials often have poor flame retardancy, poor chemical stability, high temperature deformation, poor mechanical properties, and short service life. And other problems, bring a lot of inconvenience to the actual use, and even threaten the safety of people's lives and property. Therefore, it is urgent to change the original sheath material formula and improve the material performance to meet the diverse needs of the cable market.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0009] This embodiment contains the following raw materials in parts by weight: SG-3 polyvinyl chloride 26, isotactic polypropylene 18, EVA 23, low-density polyethylene 5, zinc oxide 3, montmorillonite powder 8, sepiolite powder 14, diatomite 6. Sodium carbonate 2, propylene glycol sebacate polyester 18, isooctyl dithioglycolate, di-n-octyl tin 2, zinc oxide 5, carbon black 220 5, ethylene bisstearamide 11.5, tributyl citrate 116, auxiliary Agent 15.

[0010] The auxiliary agent contains the following raw materials in parts by weight: lapis lazuli 25, crosslinking agent TAC 5, trimethylolpropane triacrylate 3, accelerator TMTD 2, polyisobutylene 3, aluminate coupling agent DL-411 2. Ferrocene 3, lead dibasic phosphite 2, aluminum nitride powder 3, nano jade powder 3, methyl acrylate 3, Zanthoxylum bungeanum seed oil 2; the preparation method is to put lapis lazuli in a calciner at 570°C Calcined for 4 hours, cooled, crushed into 80 mesh, soaked in 15% hydrochloric acid soluti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
electrical resistivityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a cable material, specifically to a modified polyvinyl chloride cable sheath material with low-temperature impact resistance. The material comprises the following raw materials by weight: 23 to 26 parts of SG-3 polyvinyl chloride, 14 to 18 parts of isotactic polypropylene, 20 to 23 parts of EVA, 4 to 5 parts of low density polyethylene, 2 to 3 parts of zinc oxide, 6 to 8 parts of montmorillonite powder, 12 to 14 parts of meerschaum powder, 4 to 6 parts of diatomite, 1 to 2 parts of sodium carbonate, 15 to 18 parts of poly(propyleneglycol sebacate), 1 to 2 parts of di-n-octyltin bis(isooctyl mercaptoacetate), 3 to 5 parts of zinc oxide, 23 to 25 parts of carbon black 220, 1.2 to 1.5 parts of ethylene bisstearamide, 13 to 16 parts of tributyl citrate and 14 to 16 parts of an auxiliary agent. According to the invention, the advantages of the raw materials like SG-3 polyvinyl chloride, isotactic polypropylene and EVA are combined together, the prepared material has the advantages of flexibility, wear resistance, resistance to high temperature ageing, low-temperature impact resistance, resistance to chemical attack, safety and reliability in utilization, wide applicability to preparation of a variety of cable sheath insulating materials and wide market demands and prospects.

Description

technical field [0001] The invention relates to a cable material, in particular to a low-temperature impact-resistant modified polyvinyl chloride cable sheath material and a preparation method thereof. Background technique [0002] With the development of the economy, the places where cables need to be used have become diversified, and there are more stringent and diverse requirements for the performance indicators of cable sheath materials, such as insulation, tensile strength, service temperature, flame retardant performance and other indicators There are strict requirements, and continuous improvement of the performance of sheath materials is an urgent need for economic and social development. Traditional sheath materials often have poor flame retardancy, poor chemical stability, high temperature deformation, poor mechanical properties, and short service life. And other problems, bring a lot of inconvenience to the actual use, and even threaten people's life and property ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L23/12C08L23/08C08L23/06C08K13/06C08K9/00C08K9/04C08K3/34C08K3/22C08K3/26C08K5/11C08K5/103H01B7/28
Inventor 谢华
Owner 李小芬
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products