Grafting modification method for solution-polymerized styrene-butadiene rubber with low gel rate

A technology of solution-polymerized styrene-butadiene rubber and styrene-butadiene rubber, which is applied in the field of graft modification of solution-polymerized styrene-butadiene rubber with low gel ratio, and can solve the problems of increasing gel ratio of SBR and affecting rubber properties, etc.

Active Publication Date: 2014-01-15
BEIJING INSTITUTE OF PETROCHEMICAL TECHNOLOGY +1
View PDF4 Cites 44 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, during the grafting process, due to the opening of some double bonds in SBR and cross-linking, the gel rate of SBR increases, which affects the performance of the rubber.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] In a 2L stainless steel polymerization kettle with a jacket and mechanical stirring, add 1.5L cyclohexane-hexane mixed glue solution of polystyrene butadiene rubber, 11.25g initiator dibenzoyl peroxide BPO and 45g monomer maleic acid anhydride, the concentration of the glue solution is 15gSSBR / 100mL solvent, and high-purity N 2 Gas, mechanical stirring, 180 rpm, 60 ° C for 3 hours.

[0015] After the reaction is completed, the grafted polymer is precipitated with absolute ethanol, and the grafted polymer is first dried in a vacuum oven for 6 hours, and then the grafted polymer is extracted with absolute ethanol for 12 hours. Then the grafted polymer was dried in a drying oven to constant weight. Its grafting rate is 1.57% measured by chemical titration, and the gel rate is 1.82% with the method described above.

Embodiment 2

[0017] In a 2L stainless steel polymerization kettle with a jacket and mechanical stirring, add 1.5L cyclohexane-hexane mixed glue solution of polystyrene butadiene rubber, 14g initiator dibenzoyl peroxide BPO and 56.4g monomer maleic acid anhydride, the concentration of the glue solution is 15gSSBR / 100mL solvent, and high-purity N 2 Gas, mechanical stirring, 180 rpm, 70°C for 2 hours.

[0018] After the reaction is completed, the grafted polymer is precipitated with absolute ethanol, and the grafted polymer is first dried in a vacuum oven for 6 hours, and then the grafted polymer is extracted with absolute ethanol for 12 hours. Then the grafted polymer was dried in a drying oven to constant weight. Its graft rate is 1.87% measured by chemical titration, and the gel rate is 1.15% with the method described above.

Embodiment 3

[0020] In a 2L stainless steel polymerization kettle with a jacket and mechanical stirring, add 1.5L cyclohexane-hexane mixed glue solution of polystyrene butadiene rubber, 7.95g initiator lauryl peroxide and 40g monomer acrylamide, Glue concentration is 15gSSBR / 100mL solvent, high-purity N 2 Gas, mechanical stirring, 180 rpm, 60 ° C for 4 hours.

[0021] After the reaction is completed, the grafted polymer is precipitated with absolute ethanol, and the grafted polymer is first dried in a vacuum oven for 6 hours, and then the grafted polymer is extracted with absolute ethanol for 12 hours. Then the grafted polymer was dried in a drying oven to constant weight. Its graft rate is 1.66% with chemical titration method, and the gel rate with the method described above is 1.34%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of polar solution-polymerized styrene-butadiene rubber with low gel rate. The method involves grafting polar monomers on solution-polymerized styrene-butadiene rubber by means of free radical solution method, so as to change the polarity and further improve the interface bonding force of styrene-butadiene rubber and carbon black or white carbon black, so that the wet-skid resistance, wear resistance and dynamic mechanical property of vulcanized rubber are improved and the rolling resistance is reduced. The polar monomers used comprise maleic anhydride, acrylic acid, acrylamide, N-vinyl pyrrolidone and the like. The grafting rate of modified styrene-butadiene rubber is 1-5% and the gel rate is 1-3%; and the rubber polarity changes obviously.

Description

technical field [0001] The invention relates to a graft modification method of styrene-butadiene rubber, which is applied in the tire industry and provides raw materials for us to develop "green tires". Background technique [0002] At present, due to the shortage of resources, the destruction of the environment, and the pressure of the economy, there is an urgent need for an environmentally friendly, economical, and safe "green tire". Among many tread rubbers, solution polystyrene-butadiene rubber SSBR has become the research object of major domestic and foreign enterprises because of its excellent wet skid resistance, low rolling resistance, wear resistance, handling and safety. However, as a non-polar rubber, it has poor compatibility with carbon black, especially white carbon black, so that the uniformity and stability of carbon black and white carbon black dispersed therein are low, which is not conducive to improving the rubber properties. Anti-wet properties and redu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08F279/02
Inventor 戴玉华杨金娟陈力军
Owner BEIJING INSTITUTE OF PETROCHEMICAL TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com