630 MPa-grade high-strength hot-rolled reinforced bar and production process thereof

A kind of steel bar and high strength technology, applied in the field of 630MPa high-strength hot-rolled steel bar and its production process, it can solve the problems of difficulty in guaranteeing the yield platform, low yield strength of hot-rolled steel bar, etc., to avoid excessive corrosion rate and hardness, and uniform elongation. , The effect of strong anti-hysteresis fracture

Active Publication Date: 2015-06-24
江苏森林建筑新材料股份有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The yield strength of existing hot-rolled steel bars is relatively low. It is very difficult to make the yield strength of hot-rolled steel bars reach such a high strength as 630Mpa and above, and the strength is so high that it is difficult to guarantee the yield platform. Strength may be expressed as a 0.2% strain versus strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] The 630MPa grade high-strength hot-rolled steel bar in this embodiment has the following chemical composition by weight: C: 0.38%, Cr: 1.1%, Mn: 0.75%, Mo: 0.25%, Si: 0.21%, S: 0.025%, P: 0.03%, N: 0.025%, the balance is Fe.

[0035] The production technology of the 630MPa level high-strength hot-rolled steel bar of the present embodiment is carried out according to the following steps:

[0036] (1) Send the smelted steel bar into the heating furnace and heat it to 1200°C, then quickly cool the steel bar to 610°C through the first online cooling process, and then quench it with water or quenching liquid in the quenching device for 12 seconds, and then pass through The tempering heating furnace is heated to 660°C for tempering, and then cooled to normal temperature through the second cooling process;

[0037] The first cooling process: use water cooling to water-cool the steel bars to 610°C at a cooling rate of 15°C / s;

[0038] The second cooling process: the combinati...

Embodiment 2

[0045] The 630MPa grade high-strength hot-rolled steel bar in this embodiment has the following chemical composition by weight: C: 0.41%, Cr: 0.8%, Mn: 1.0%, Mo: 0.15%, Si: 0.15%, S: 0.015%, P: 0.025%, N: 0.015%, and the balance is Fe.

[0046] The production technology of the 630MPa level high-strength hot-rolled steel bar of the present embodiment is carried out according to the following steps:

[0047] (1) Put the smelted steel bar into the heating furnace and heat it to 1100°C, then cool the steel bar quickly to 620°C through the first online cooling process, and then quench it with water or quenching liquid in the quenching device for 13 seconds, and then pass through The tempering heating furnace is heated to 600°C for tempering, and then cooled to normal temperature through the second cooling process;

[0048] The first cooling process: use water cooling to cool the steel bars to 620°C at a cooling rate of 16°C / s;

[0049] The second cooling process: the combination ...

Embodiment 3

[0056] The 630MPa grade high-strength hot-rolled steel bar in this embodiment has the following chemical composition by weight: C: 0.43%, Cr: 0.9%, Mn: 0.85%, Mo: 0.2%, Si: 0.3%, S: 0.013%, P: 0.015%, N: 0.012%, and the balance is Fe.

[0057] The production technology of the 630MPa level high-strength hot-rolled steel bar of the present embodiment is carried out according to the following steps:

[0058] (1) Put the smelted steel bar into the heating furnace and heat it to 1010°C, then quickly cool the steel bar to 630°C through the first online cooling process, and then quench it with water or quenching liquid in the quenching device for 14 seconds, and then pass through The tempering heating furnace is heated to 520°C for tempering, and then cooled to normal temperature through the second cooling process;

[0059] The first cooling process: use water cooling to water-cool the steel bars to 630°C at a cooling rate of 17°C / s;

[0060] The second cooling process: the combina...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
diameteraaaaaaaaaa
elastic modulusaaaaaaaaaa
Login to view more

Abstract

The invention relates to a steel bar and its production process, which is a 630MPa grade high-strength hot-rolled steel bar and its production process. The chemical composition in weight percentage is: C: 0.38-0.43%, Cr: 0.8-1.1%, Mn: 0.75- 1.0%, Mo: 0.15-0.25%, Si: 0.15-0.3%, S: <0.035%, P: <0.035%, N: <0.035%, and the balance is Fe. The steel bar yield strength of the present invention can reach 630Mpa, has the advantages of high strength, good ductility, strong hysteresis fracture resistance, steel saving, low relaxation, easy welding, good upsetting performance, etc., and can fully dissolve carbides and evenly diffuse, It avoids the precipitation of carbides between grains and causes excessive intergranular corrosion and pitting corrosion.

Description

technical field [0001] The invention relates to a steel bar and a production process thereof, in particular to a 630MPa high-strength hot-rolled steel bar and a production process thereof. Background technique [0002] Hot-rolled steel bars are finished steel bars that have been hot-rolled and naturally cooled. They are made of low-carbon steel and ordinary alloy steel at high temperatures. They are mainly used for reinforcement of reinforced concrete and prestressed concrete structures. They are used in civil engineering One of the most widely used steel varieties. Hot-rolled steel bars are graded according to the standard value of yield strength and are divided into four grades: [0003] HPB235 (Q235), the standard value of the yield strength of the steel bar is 235MPa, the diameter is 8-20mm, and the elastic modulus is 210GPa. [0004] HRB335 (20MnSi), the standard value of the yield strength of the steel bar is 335MPa, the diameter is 6-50mm, and the elastic modulus is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/22C21D8/08
Inventor 姚圣法吴海洋
Owner 江苏森林建筑新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap